US5080933A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Selective deposition of polycrystalline silicon
Assignee: NXP USA Inc
•
Filing: 1990-09-04
•
Granted: 1992-01-14
•
Expires: 2010-09-04
Abstract
Abstract A method for selectively depositing polysilicon on a semiconductor surface (13) is accomplished by preparing the surface (13) in a manner to provide a contamination free surface. The contamination free semiconductor surface is placed into a chemical vapor deposition reactor. The semiconductor surface (13) is exposed to a single crystal inhibitor gas to prevent formation of single crystal silicon on surface (13). Semiconductor surface (13) is then exposed to a silicon containing gas with a hydrogen source to form the polysilicon.
Inventors
- 👤 Melissa E. Grupen-Shemansky
- 👤 Hang M. Liaw
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 09:38
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/02; C23C16/0227; C23C16/0236; C23C16/0209; C23C16/04
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
54 words
A method for selectively producing polysilicon on a semiconductor wafer comprising: placing a semiconductor wafer into a chemical vapor deposition reactor; exposing the semiconductor wafer to a single crystal growth inhibiting gas to inhibit single crystal growth; exposing the semiconductor wafer to a silicon containing gas and a hydrogen source, thereby producing the polysilicon.
Claim 2
Independent Claim
54 words
A method for selectively producing polysilicon on a semiconductor wafer comprising: placing a semiconductor wafer into a chemical vapor deposition reactor; exposing the semiconductor wafer to a single crystal growth inhibiting gas to inhibit single crystal growth; exposing the semiconductor wafer to a silicon containing gas and a hydrogen source, thereby producing the polysilicon.
Claim 3
Dependent Claim
15 words
The method of claim 1 further including using nitrogen for single crystal growth inhibiting gas.
Claim 4
Dependent Claim
47 words
The method of claim 1 further including maintaining the reactor temperature in a range of approximately 600 to 1000 degrees centigrade for the single crystal growth inhibiting gas and in a range of approximately 500 to 1000 degrees centigrade for the silicon containing gas and hydrogen source.
Claim 5
Dependent Claim
45 words
The method of claim 3 further including maintaining the reactor pressure in a range of approximately 10 millitorr to atmospheric for the single crystal growth inhibiting gas and in a range of approximately 10 millitorr to atmospheric for the silicon containing gas and hydrogen source.
Claim 6
Dependent Claim
38 words
The method of claim 4 further including adjusting the chemical vapor deposition reactor pressure to substantially 740 torr for the single crystal growth inhibiting gas and to substantially 740 torr for the silicon containing gas and hydrogen source.
Claim 7
Dependent Claim
40 words
The method of claim 3 further including adjusting the chemical vapor deposition reactor temperature to substantially 800 degrees centigrade for the single crystal growth inhibiting gas and to substantially 700 degrees centigrade for the silicon containing gas and hydrogen source.
Claim 8
Dependent Claim
26 words
The method of claim 1 further including providing the silicon containing gas is one gas from a group comprising silicon tetrachloride, trichlorosilane, dichlorosilane, chlorosilane, and silane.
Claim 9
Independent Claim
60 words
A method for selectively depositing polysilicon on a semiconductor wafer comprising: placing the semiconductor wafer into a chemical vapor deposition reactor; exposing the semiconductor wafer to a hydrogen environment; exposing the semiconductor wafer to a single crystal growth inhibiting gas to inhibit single crystal growth; subjecting the semiconductor wafer to a silicon containing gas and hydrogen, thereby selectively depositing polysilicon.
Claim 10
Independent Claim
60 words
A method for selectively depositing polysilicon on a semiconductor wafer comprising: placing the semiconductor wafer into a chemical vapor deposition reactor; exposing the semiconductor wafer to a hydrogen environment; exposing the semiconductor wafer to a single crystal growth inhibiting gas to inhibit single crystal growth; subjecting the semiconductor wafer to a silicon containing gas and hydrogen, thereby selectively depositing polysilicon.
Claim 11
Dependent Claim
23 words
The method of claim 8 further including selecting a silicon containing gas from a group comprising silicon tetrachloride, trichlorosilane, dichlorosilane, chlorosilane, and silane.
Claim 12
Dependent Claim
69 words
The method of claim 8 further including maintaining the reactor temperature in a range of approximately 600 to 1000 degrees centigrade for exposing the semiconductor wafer to hydrogen, in a range of the approximately 600 to 1000 degrees centigrade for the single crystal growth inhibiting gas, and in a range of approximately 500 to 1000 degrees centigrade for exposing a semiconductor wafer to a silicon containing gas and hydrogen.
Claim 13
Dependent Claim
22 words
The method of claim 10 further including maintaining the chemical vapor deposition reactor pressure at a range of 10 millitorr to atmospheric.
Claim 14
Dependent Claim
53 words
The method of claim 10 further including adjusting the chemical vapor deposition reactor pressure to substantially 50 torr for exposing the semiconductor wafer to hydrogen, to substantially 740 torr for the single crystal growth inhibiting gas, and to substantially 740 torr for exposing the semiconductor wafer to the silicon containing gas and hydrogen.
Claim 15
Dependent Claim
16 words
The method of claim 10 further including a high growth rate sequence for selectively depositing polysilicon.
Claim 16
Dependent Claim
24 words
The method of claim 13 further including maintaining the chemical vapor deposition reactor in a temperature range of approximately 600 to 1150 degrees centigrade.
Claim 17
Dependent Claim
56 words
The method of claim 8 further including adjusting the chemical vapor deposition reactor temperature to substantially 975 degrees centigrade for exposing the semiconductor wafer to hydrogen, to substantiality 800 degrees centigrade for the single crystal growth inhibiting gas, and to substantially 700 degrees centigrade for exposing a semiconductor wafer to a silicon containing gas and hydrogen.
Claim 18
Independent Claim
146 words
A method for selectively depositing polycrystalline silicon comprising the steps of: placing a semiconductor wafer to a hydrogen environment for a prebake treatment; exposing the semiconductor wafer into a single crystal growth inhibitor gas to inhibit single crystal growth; exposing the semiconductor wafer to a silicon containing gas and a hydrogen gas source while maintaining the chemical vapor deposition reactor pressure in a range of 10 millitorr to atmospheric and temperature in a range of 500 degrees centigrade to 1000 degrees centigrade for the formation of at least a monolayer of selective polysilicon; and changing the reactor pressure to a range of 10 millitorr to atmospheric and changing the temperature to a range of 700 degrees centigrade to 1150 degrees centigrade while maintaining the exposure to the silicon containing gas and the hydrogen gas source thereby providing for rapid growth of selective polysilicon on the monolayer.
Claim 19
Independent Claim
146 words
A method for selectively depositing polycrystalline silicon comprising the steps of: placing a semiconductor wafer to a hydrogen environment for a prebake treatment; exposing the semiconductor wafer into a single crystal growth inhibitor gas to inhibit single crystal growth; exposing the semiconductor wafer to a silicon containing gas and a hydrogen gas source while maintaining the chemical vapor deposition reactor pressure in a range of 10 millitorr to atmospheric and temperature in a range of 500 degrees centigrade to 1000 degrees centigrade for the formation of at least a monolayer of selective polysilicon; and changing the reactor pressure to a range of 10 millitorr to atmospheric and changing the temperature to a range of 700 degrees centigrade to 1150 degrees centigrade while maintaining the exposure to the silicon containing gas and the hydrogen gas source thereby providing for rapid growth of selective polysilicon on the monolayer.
Claim 20
Dependent Claim
72 words
The method of claim 16 further including adjusting the chemical vapor deposition reactor temperature to substantially 975 degrees centigrade for the hydrogen prebake treatment, changing the reactor temperature to substantially 800 degrees centigrade for the single crystal inhibitor gas, changing the reactor temperature to substantially 700 degrees centigrade for the formation of the selective polysilicon monolayer, and changing the temperature to substantially 845 degrees centigrade for the rapid growth of selective polysilicon.
Claim 21
Dependent Claim
68 words
The method of claim 16 further including maintaining the chemical vapor deposition reactor pressure to substantially 50 torr for the prebake treatment, changing the reactor pressure to substantially 740 torr for the single crystal inhibitor gas, changing the reactor pressure to substantiality 740 torr for the formation of the selective polysilicon monolayer, and changing the reactor pressure to substantially 740 torr for the rapid growth of selective polysilicon.
Claim 22
Independent Claim
55 words
A method for selectively depositing doped polysilicon on a semiconductor wafer comprising: placing the semiconductor wafer into a chemical vapor deposition reactor; exposing the semiconductor wafer to a single crystal growth inhibitor gas to inhibit single crystal growth; exposing the semiconductor wafer to a silicon gas, hydrogen gas source and dopant source, thereby creating polysilicon.
Claim 23
Independent Claim
55 words
A method for selectively depositing doped polysilicon on a semiconductor wafer comprising: placing the semiconductor wafer into a chemical vapor deposition reactor; exposing the semiconductor wafer to a single crystal growth inhibitor gas to inhibit single crystal growth; exposing the semiconductor wafer to a silicon gas, hydrogen gas source and dopant source, thereby creating polysilicon.
Claim 24
Dependent Claim
19 words
The method of claim 19 further including providing the dopant gas from a group comprising arsine, phosphine, and diborane.
Claim 25
Dependent Claim
26 words
The method of claim 20 further including cleaning the semiconductor wafer by a hydrogen prebake prior to exposing the wafer to the single crystal inhibitor gas.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-01-13 | 1995-07-15 | 1996-01-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-01-13 | 1999-07-15 | 2000-01-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-01-13 | 2003-07-15 | 2004-01-14 | $7700.00 | Window Closed / Lapsed |