Abstract A highly oriented rare earth based permanent magnet satisfies the relationship a≧b>c where a is the longer side or major axis of the magnet, b is the shorter or minor axis of the magnet, and c is the thickness of the magnet, and that has a flat shape which is magnetized in the direction of thickness c, with the direction of magnetization being inclined at an angle of no more than 3 degrees with respect to the line normal to the plane defined by a and b. The magnet is produced by loading an alloy powder as the starting material into a mold having a cavity that satisfies the relationship A≧B>C where A is the longer side or major axis of the cavity, B is the shorter side or minor axis of the cavity, and C is the depth of the cavity; exerting a compressive force of at least 0.4 tons/cm 2 in a direction substantially perpendicular to the plane defined by A and C while applying a magnetic field in a direction substantially perpendicular to the plane defined by A and B, thereby effecting in-field molding so as to obtain a preform; and performing cold isostatic pressing at a pressure higher than that employed in the preforming step.
A process for producing a highly oriented rare earth base permanent magnet which satisfies a dimensional relationship a≧b>c, where a is the longer side or major axis of the magnet, b is the shorter side or minor axis of the magnet, and c is the thickness of the magnet, and which has a direction of magnetization inclined at an angle not exceeding 3 degrees with respect to the line normal to the plane defined by a and b, said process comprising the steps of: providing a mold comprising magnetic material mold members and nonmagnetic material mold members, said magnetic material mold members and said nonmagnetic material mold members being arranged to form a cavity in said mold, said nonmagnetic material mold members projecting inwardly; loading an alloy powder as the starting material into said mold having said cavity that satisfies a relationship A ≧B>C, where A is the longer side or major axis of the cavity, B is the shorter side or minor axis of the cavity, and C is the depth of the cavity, and said cavity being formed in a substantially uniform parallel magnetic field; exerting a compressive force of at least 0.4 tons/cm 2 in a direction substantially perpendicular to the plane defined by A and C while applying a magnetic field in a direction substantially perpendicular to the plane defined by A and B, thereby effecting in-field molding so as to obtain a preform having the direction of magnetization inclined at an angle, said angle being no more than 3 degrees with respect to the line normal to the plane defined by A and B; and performing cold isostatic pressing at a pressure higher than that employed in the preforming step.
Claim 2
Dependent Claim
285 words
A process for producing a highly oriented rare earth base permanent magnet which satisfies a dimensional relationship a≧b>c, where a is the longer side or major axis of the magnet, b is the shorter side or minor axis of the magnet, and c is the thickness of the magnet, and which has a direction of magnetization inclined at an angle not exceeding 3 degrees with respect to the line normal to the plane defined by a and b, said process comprising the steps of: providing a mold comprising magnetic material mold members and nonmagnetic material mold members, said magnetic material mold members and said nonmagnetic material mold members being arranged to form a cavity in said mold, said nonmagnetic material mold members projecting inwardly; loading an alloy powder as the starting material into said mold having said cavity that satisfies a relationship A ≧B>C, where A is the longer side or major axis of the cavity, B is the shorter side or minor axis of the cavity, and C is the depth of the cavity, and said cavity being formed in a substantially uniform parallel magnetic field; exerting a compressive force of at least 0.4 tons/cm 2 in a direction substantially perpendicular to the plane defined by A and C while applying a magnetic field in a direction substantially perpendicular to the plane defined by A and B, thereby effecting in-field molding so as to obtain a preform having the direction of magnetization inclined at an angle, said angle being no more than 3 degrees with respect to the line normal to the plane defined by A and B; and performing cold isostatic pressing at a pressure higher than that employed in the preforming step.
Claim 3
Dependent Claim
19 words
A process according to claim 1, wherein said compressive force is in the range of 0.4-4 tons/cm 2 .