Hard alloy particle dispersion type wear resisting sintered ferro alloy and method of forming the same
Assignee: Riken Corp
•
Filing: 1989-04-14
•
Granted: 1992-01-14
•
Expires: 2009-04-14
Abstract
Abstract A material for valve seats comprising a wear resisting sintered ferro alloy formed by dispersing particles of a high speed steel in a matrix in which hard alloy particles are dispersed. Steps for forming include mixing particles of a matrix material, carbide material and a hard alloy, and blending the mixture with high speed steel particles, pressurizing and compacting the mixture after blending, then sintering them at 1000° to 1200° C. In the preferred method, at least one element of Fe, C, Ni, Co, Si or Mn is included as the matrix material, and at least one element of Fe, Cr, Mo or V as the carbide material and at least one element of Fe, Cr, Mo, Co, C or W as the hard alloy are prepared. Furthermore, the ferro alloy preferably includes the following amounts of the above mentioned elements, 0.5 to 2.0 wt % of C, 1 to 25 wt % of one or more of Cr, Mo, V, or W and 1 to 15 wt % of one or more of Co, Ni, Mn, or Si.
Inventors
- 👤 Akiyoshi Ishibashi
- 👤 Kazutoshi Takemura
- 👤 Makoto Abe
- 👤 Akira Fujiki
- 👤 Kimitsugu Kiso
- 👤 Takaaki Ito
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 09:19
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0257; C22C33/0264; C22C33/0207; F; F02; F02F; F02F7/00; F02F7/0085
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
63 words
A ferro alloy comprised of a base material forming a matrix, a hard alloy dispersed in said matrix in a form of a particle, wherein said hard alloy is present in a predetermined amount in relation to said base material, and a high speed steel also dispsersed in said matrix so as to fill gaps formed between said hard alloy and said matrix.
Claim 2
Dependent Claim
63 words
A ferro alloy comprised of a base material forming a matrix, a hard alloy dispersed in said matrix in a form of a particle, wherein said hard alloy is present in a predetermined amount in relation to said base material, and a high speed steel also dispsersed in said matrix so as to fill gaps formed between said hard alloy and said matrix.
Claim 3
Dependent Claim
153 words
The ferro alloy as in claim 1, wherein said ferro alloy comprises: a mixture of particles having a first component as a matrix material and a second component as a carbide material and a third component as a hard alloy, the first component having at least one element selected from the group consisting of Fe, C, Ni, Co, Si and Mn in the form of a particle, the second component having at least one element selected from the group consisting of Fe, Cr, Mo and V in the form of a particle and the third component having at least one element selected from the group consisting of Fe, Cr, Mo, Co, C and W in the form of a particle, a high speed steel particle blended with said mixture of particles before being pressurized and compacted to enhance the sealing between said hard alloy particle and said matrix and, a balance of Fe,
Claim 4
Dependent Claim
68 words
The ferro alloy as in claim 2, wherein said elements are present in amounts within the following ranges: 0.5 to 2.0 wt% of C, 1 to 25% for the total amount of the elements selected from the group consisting of Cr, Mo, V and W, and 1 to 15 wt% for the total amount of the elements selected from the group consisting of Co, Ni, Mn and Si.
Claim 5
Dependent Claim
19 words
The ferro alloy as in claim 2, wherein said mixture of particles is sintered at 1000° to 1200° C.
Claim 6
Dependent Claim
76 words
A valve seat formed by a wear resisting sintered ferro alloy, wherein said ferro alloy is comprised of a base material forming a matrix, a hard alloy dispsersed in said matrix in a form of a particle, wherein said hard alloy is present in a predetermined amount in relation to said base material, and a high speed steel also dispsersed in said matrix so as to fill gaps formed between said hard alloy and said matrix.
Claim 7
Dependent Claim
76 words
A valve seat formed by a wear resisting sintered ferro alloy, wherein said ferro alloy is comprised of a base material forming a matrix, a hard alloy dispsersed in said matrix in a form of a particle, wherein said hard alloy is present in a predetermined amount in relation to said base material, and a high speed steel also dispsersed in said matrix so as to fill gaps formed between said hard alloy and said matrix.
Claim 8
Dependent Claim
153 words
The valve seat as in claim 5, wherein said ferro alloy comprises: a mixture of particles having a first component as a matrix material and a second component as a carbide material and a third component as a hard alloy, the first component having at least one element selected from the group consisting of Fe, C, Ni, Co, Si and Mn in the form of a particle, the second component having at least one element selected from the group consisting of Fe, Cr, Mo and V in the form of a particle and the third component having at least one element selected from the group consisting of Fe, Cr, Mo, Co, C and W in the form of a particle, a high speed steel particle blended with said mixture of particles before being pressurized and compacted to enhance the binding between said hard alloy particle and said matrix and a balance of Fe.
Claim 9
Dependent Claim
69 words
The valve seat as in claim 5, wherein said elements are present in amounts within the following ranges: 0.5 to 2.0 wt% of C, 1 to 25 wt% for the total amount of the elements selected from the group consisting of Cr, Mo, V and W, and 1 to 15 wt% for the total amount of the elements selected from the group consisting of Co, Ni, Mn and Si.
Claim 10
Dependent Claim
22 words
The valve seat as in claim 5, wherein said mixture of particles is sintered at a temperature of 1000° to 1200° C.
Claim 11
Independent Claim
69 words
A method of forming a ferro alloy comprising the steps of: forming a matrix of a base material, dispersing a hard alloy in said matrix in a form of particles, wherein said hard alloy is present in a predetermined amount in relation to said base material, and dispersing a high speed steel also in said matrix so as to fill gaps formed between said hard alloy and said matrix.
Claim 12
Independent Claim
69 words
A method of forming a ferro alloy comprising the steps of: forming a matrix of a base material, dispersing a hard alloy in said matrix in a form of particles, wherein said hard alloy is present in a predetermined amount in relation to said base material, and dispersing a high speed steel also in said matrix so as to fill gaps formed between said hard alloy and said matrix.
Claim 13
Dependent Claim
159 words
The method of forming the ferro alloy as in claim 9, wherein said method comprises the steps of: mixing of particles having a first component as a matrix material and a second component as a carbide material and a third component as a hard alloy, the first component having at least one element selected from the group consisting of Fe, C, Ni, Co, Si and Mn in the form of a particle, the second component having at least one element selected from the group consisting of Fe, Cr, Mo and V in the form of a particle and the third component having at least one element selected from the group consisting of Fe, Cr, Mo, Co, C and W in the form of a particle, blending high speed steel particles with said mixture of particles before pressurizing and compacting to enhance the binding between said hard alloy particle and said matrix, wherein the balance of the alloy comprises Fe.
Claim 14
Dependent Claim
72 words
The method of forming the ferro alloy as in claim 10, wherein said elements are present in amounts within the following ranges: 0.5 to 2.0 wt% of C, 1 to 25 wt% for the total amount of the elements selected from the group consisting of Cr, Mo and W, and 1 to 15 wt% for the total amount of the elements selected from the group consisting of Co, Ni, Mn and Si.
Claim 15
Dependent Claim
26 words
The method of forming the ferro alloy as in claim 10, wherein said mixture of particles is sintered at a temperature of 1000° to 1200° C.
Claim 16
Independent Claim
77 words
A method of forming a valve seat comprised of a wear resisting sintered ferro alloy, comprising the steps of: forming a matrix of a base material, dispersing a hard alloy in said matrix in a form of particles, wherein said hard alloy is present in a predetermined amount in relation to said base material, and dispersing a high speed steel also in said matrix so as to fill gaps formed between said hard alloy and said matrix.
Claim 17
Independent Claim
77 words
A method of forming a valve seat comprised of a wear resisting sintered ferro alloy, comprising the steps of: forming a matrix of a base material, dispersing a hard alloy in said matrix in a form of particles, wherein said hard alloy is present in a predetermined amount in relation to said base material, and dispersing a high speed steel also in said matrix so as to fill gaps formed between said hard alloy and said matrix.
Claim 18
Dependent Claim
159 words
The method of forming a valve seat as in claim 13, wherein said method comprises the steps of: mixing of particles having a first component as a matrix material and a second component as a carbide material and a third component as a hard alloy, the first component having at least one element selected from the group consisting of Fe, C, Ni, Co, Si and Mn in the form of a particle, the second component having at least one element selected from the group consisting of Fe, Cr, Mo and V in the form of a particle and the third component having at least one element selected from the group consisting of Fe, Cr, Mo, Co, C and W in the form of a particle, blending high speed steel particles with said mixture of particles before pressurizing and compacting to enhance the binding between said hard alloy particle and said matrix, wherein the balance of the alloy comprises Fe.
Claim 19
Dependent Claim
72 words
The method of forming the valve seat as in claim 14, wherein said elements are present in amounts within the following ranges: 0.5 to 2.0 wt% of C, 1 to 25 wt% for the total amount of the elements selected from the group consisting of Cr, Mo and W, and 1 to 15 wt% for the total amount of the elements selected from the group consisting of Co, Ni, Mn and Si.
Claim 20
Dependent Claim
26 words
The method of forming the valve seat as in claim 14, wherein said mixture of particles is sintered at a temperature of 1000° to 1200° C.
Claim 21
Dependent Claim
19 words
The ferro alloy as in claim 1, wherein between 2 and 15 wt% of said hard alloy is present.
Claim 22
Dependent Claim
19 words
The ferro alloy as in claim 5, wherein between 2 and 15 wt% of said hard alloy is present.
Claim 23
Dependent Claim
22 words
The method of forming ferro alloy as in claim 9, wherein between 2 and 15 wt% of said hard alloy is present.
Claim 24
Dependent Claim
22 words
The method of forming a valve seat as in claim 13, wherein between 2 and 15% of said hard alloy is present
References Cited (Backward Citations)
US4204031A
Cited
US4552590A
Cited
JPS56158846A
Cited
US4505988A
Cited
GB2157711A
Cited
JPS6164855A
Cited
EP0202035A1
Cited
JPS62146246A
Cited
EP0266935A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-01-13 | 1995-07-15 | 1996-01-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-01-13 | 1999-07-15 | 2000-01-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-01-13 | 2003-07-15 | 2004-01-14 | $7700.00 | Window Closed / Lapsed |