US5079274A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for preparing absorptive porous resin beads
Assignee: Dow Chemical Co
•
Filing: 1990-03-14
•
Granted: 1992-01-07
•
Expires: 2010-03-14
Abstract
Abstract Organic materials, for example halocarbons, hydrocarbons or halogenated hydrocarbons are recovered from fluid streams, such as air or water, by passing these streams over post-cross-linked asdorptive porous resin beads. These beads have been prepared by (a) haloalkylating cross-linked copolymer beads of i) styrene or an alkylstyrene and ii) divinylbenzene and/or trivinylbenzene, (b) purifying the haloalkylated copolymer beads, (c) swelling the haloalkylated copolymer beads in an inert organic liquid and post-cross-linking the swollen beads in the presence of a Friedel-Crafts catalyst. The cross-linked copolymer beads which are used in the haloalkylation step are microporous copolymer beads of i) 99.8 to 98.2 weight percent of styrene or an alkylstyrene and ii) 0.2 to 1.8 weight percent of divinylbenzene and/or trivinylbenzene, based on the total weight of i) and ii).
Inventors
- 👤 Hans P. Schneider
- 👤 Yvonne M. Gorlach-Doht
- 👤 Marius A. M. Kumin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 07:55
CPC Classifications
C; C08; C08F; C08F212/00; C08F212/02; C08F212/04; C08F212/14; B; B01; B01J; B01J20/00; B01J20/22; B01J20/26; C08F8/00; C08F8/18; C08F8/24
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
87 words
A process for preparing adsorptive porous resins beads comprising: (a) haloalkylating cross-linked microporous beads of a copolymer containing i) from 99.8 to 98.2 weight percent of styrene or alkylstyrene and ii) from 0.2 to 1.8 weight percent of divinylbenzene or trivinylbenzene or both, based on the total weight of i) and ii), (b) purifying the haloalkylated copolymer beads, and (c) swelling and post-cross-linking the haloalkylated copolymer beads by reaction of haloalkyl groups with aromatic rings in an inert organic liquid in the presence of a Friedel-Crafts catalyst.
Claim 2
Dependent Claim
87 words
A process for preparing adsorptive porous resins beads comprising: (a) haloalkylating cross-linked microporous beads of a copolymer containing i) from 99.8 to 98.2 weight percent of styrene or alkylstyrene and ii) from 0.2 to 1.8 weight percent of divinylbenzene or trivinylbenzene or both, based on the total weight of i) and ii), (b) purifying the haloalkylated copolymer beads, and (c) swelling and post-cross-linking the haloalkylated copolymer beads by reaction of haloalkyl groups with aromatic rings in an inert organic liquid in the presence of a Friedel-Crafts catalyst.
Claim 3
Dependent Claim
44 words
The process of claim 1 wherein cross-linked microporous beads of a copolymer, containing i) from about 99.7 to about 98.5 weight percent of styrene or alkylstyrene and ii) from about 0.33 to about 1.5 weight percent of divinylbenzene or trivinylbenzene or both, are haloalkylated.
Claim 4
Dependent Claim
44 words
The process of claim 1 wherein cross-linked microporous beads of a copolymer, containing i) from about 99.5 to about 99.0 weight percent of styrene or alkylstyrene and ii) from about 0.5 to about 1.0 weight percent of divinylbenzene or trivinylbenzene or both. are haloalkylated.
Claim 5
Dependent Claim
17 words
The process of claim 1 wherein cross-linked microporous beads of i) styrene and ii) divinylbenzene are haloalkylated.
Claim 6
Dependent Claim
17 words
The process of claim 3 wherein cross-linked microporous beads of i) styrene and ii) divinylbenzene are haloalkylated.
Claim 7
Dependent Claim
24 words
The process of claim 1 wherein the adsorptive porous resin beads have an average pore diameter of about 0.5 nm to about 2.5 nm.
Claim 8
Dependent Claim
24 words
The process of claim 5 wherein the adsorptive porous resin beads have an average pore diameter of about 0.5 nm to about 2.5 nm.
Claim 9
Dependent Claim
26 words
The process of claim 1 wherein the cross-linked microporous beads are haloalkylated in step a) with chloromethyl methyl ether in the presence of a Friedel-Crafts catalyst.
Claim 10
Dependent Claim
26 words
The process of claim 5 wherein the cross-linked microporous beads are haloalkylated in step a) with chloromethyl methyl ether in the presence of a Friedel-Crafts catalyst.
Claim 11
Dependent Claim
24 words
The process of claim 1 wherein the halogenated copolymer beads are purified in step b) by washing the beads in an oxygenated organic liquid.
Claim 12
Dependent Claim
24 words
The process of claim 9 wherein the halogenated copolymer beads are purified in step b) by washing the beads in an oxygenated organic liquid.
Claim 13
Dependent Claim
40 words
The process of claim 1 wherein the purified haloalkylated copolymer beads in step c) are swollen in a chlorinated hydrocarbon at a temperature of from about 60° C. to about 85° C. in the presence of an acidic metal halide.
Claim 14
Dependent Claim
40 words
The process of claim 11 wherein the purified haloalkylated copolymer beads in step c) are swollen in a chlorinated hydrocarbon at a temperature of from about 60° C. to about 85° C. in the presence of an acidic metal halide.
Claim 15
Dependent Claim
43 words
A method of recovering an organic material from a fluid stream by passing the fluid stream containing the organic material over adsorptive porous resin beads wherein the adsorptive porous resin beads have been prepared according to the process as claimed in claim 1.
Claim 16
Dependent Claim
16 words
The method of claim 14 wherein the organic material is selected from hydrocarbons and halogenated hydrocarbons.
Claim 17
Dependent Claim
15 words
The method of claim 14 wherein the fluid stream is an aqueous medium or air.
Claim 18
Dependent Claim
43 words
The method of claim 14 wherein air containing a halogenated hydrocarbon is passed over the adsorptive porous resin beads at a temperature of from about -25° C. to about +50° C. and a pressure of from about 0.5 bar to about 2 bar.
Claim 19
Dependent Claim
80 words
The method of claim 14 wherein air containing a halogenated hydrocarbon is passed over the adsorptive porous resin beads at a temperature of from about -25° C. to about +50° C. and a pressure of from about 0.5 bar to about 2 bar and the adsorbed halogenated hydrocarbon is desorbed from the adsorptive porous resin beads at a temperature of from about 50° C. to about 140° C. and a pressure of from about 10 mbar to about 300 mbar.
Claim 20
Dependent Claim
43 words
A method of recovering an organic material from a fluid stream by passing the fluid stream containing the organic material over adsorptive porous resin beads wherein the adsorptive porous resin beads have been prepared according to the process as claimed in claim 13.
Claim 21
Dependent Claim
80 words
The method of claim 19 wherein air containing a halogenated hydrocarbon is passed over the adsorptive porous resin beads at a temperature of from about -25° C. to about +50° C. and a pressure of from about 0.5 bar to about 2 bar and the adsorbed halogenated hydrocarbon is desorbed from the adsorptive porous resin beads at a temperature of from about 50° C. to about 140° C. and a pressure of from about 10 mbar to about 300 mbar.
References Cited (Backward Citations)
DE220964C
Cited
DE229992C
Cited
DE203556C
Cited
DE249190C
Cited
DE220965C
Cited
GB1176706A
Cited
US3686827A
Cited
US3822244A
Cited
US4191813A
Cited
US4192920A
Cited
US4263407A
Cited
US4358546A
Cited
GB2113226A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-01-06 | 1995-07-08 | 1996-01-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-01-06 | 1999-07-08 | 2000-01-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-01-06 | 2003-07-08 | 2004-01-07 | $7700.00 | Window Closed / Lapsed |