High strength nickel base single crystal alloys having enhanced solid solution strength and methods for making same
Assignee: Honeywell International Inc
•
Filing: 1989-11-29
•
Granted: 1991-12-31
•
Expires: 2009-11-29
Abstract
Abstract Disclosed are novel nickel base single crystal alloy compositions consisting essentially of, by weight, about 4.0-10.0% chromium, 1.5-6.0% cobalt, 1.0-12.0% molybdenum, 3.0-10.0% tungsten, 2.5-7.0% titanium, 2.5-7.0% aluminum, 3.0-10.0% tantalum, about 0.02%-1.5% of hafnium and/or about 0.02%-1.0% silicon, from about 0.02%-1.0% each of yttrium and/or lanthanum, from about 0.3% to about 8.0% rhenium; from about 0.2% to about 4.0% vanadium and/or from about 0.2% to about 4.0% niobium; from about 0.02% to about 3% platinum; from about 0 to about 1.0% boron, the balance nickel, and the balance nickel. Methods of thermal treatment and coating of the novel alloys to enhance their mechanical properties are also disclosed, as are articles produced by such methods.
Inventors
- 👤 Subhash K. Naik
- 👤 Vinod K. Nangia
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 14:59
CPC Classifications
C; C30; C30B; C30B11/00; C22; C22C; C22C19/00; C22C19/03; C22C19/05; C22C19/051; C22C19/056; C30B29/00; C30B29/10; C30B29/52; C30B33/00; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12771; Y10T428/12861; Y10T428/12931; Y10T428/12944
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
138 words
A single crystal alloy composition having improved oxidation/corrosion resistance, high strength at elevated temperatures and improved solid solution strength consisting essentially of, by weight, about 4.0% to about 10.0% chromium; about 1.5% to about 6.0% cobalt; about 1.0% to about 12.0% molybdenum; about 3.0% to about 10.0% tungsten; about 2.5% to about 7.0% titanium; about 2.5% to about 7.0% aluminum; about 3.0% to about 10.0% tantalum; at least one element selected from the group consisting of from about 0.02% to about 1.5% of hafnium and from about 0.02% to about 1.0% of silicon; from about 0.02% to about 1% of at least one element selected from the group consisting of yttrium and lanthanum; from about 0.3% to about 8.0% rhenium; from about 0.2% to about 4.0% of at least one element selected from the group consisting of vanadium.
Claim 2
Dependent Claim
138 words
A single crystal alloy composition having improved oxidation/corrosion resistance, high strength at elevated temperatures and improved solid solution strength consisting essentially of, by weight, about 4.0% to about 10.0% chromium; about 1.5% to about 6.0% cobalt; about 1.0% to about 12.0% molybdenum; about 3.0% to about 10.0% tungsten; about 2.5% to about 7.0% titanium; about 2.5% to about 7.0% aluminum; about 3.0% to about 10.0% tantalum; at least one element selected from the group consisting of from about 0.02% to about 1.5% of hafnium and from about 0.02% to about 1.0% of silicon; from about 0.02% to about 1% of at least one element selected from the group consisting of yttrium and lanthanum; from about 0.3% to about 8.0% rhenium; from about 0.2% to about 4.0% of at least one element selected from the group consisting of vanadium.
Claim 3
Dependent Claim
140 words
The composition of claim 1 consisting essentially of, by weight, about 4.0% to about 7.9% chromium; about 2.5% to about 5.0% cobalt; about 2.0% to about 6.0% molybdenum; about 5.0% to about 9.0% tungsten; about 2.5% to about 6.0% titanium; about 3.0% to about 6.0% aluminum; about 4.0% to about 9.0% tantalum; at least one element selected from the group consisting of from about 0.05% to about 0.5% hafnium and from about 0.02% to about 0.3% silicon; about 0.05% to about 0.4% of at least one element selected from the group consisting of yttrium and lanthanum; from about 1.0% to about 6.0% rhenium; from about 0.2% to about 1.5% of at least one element selected from the group consisting of vanadium and niobium; from about 0.2% to about 1.5% platinum; from about 0 to 0.3% boron, and the balance nickel.
Claim 4
Dependent Claim
10 words
The composition of claim 1 containing both yttrium and lanthanum.
Claim 5
Dependent Claim
17 words
The composition of claim 3 comprising up to about 0.4% yttrium and up to about 0.4% lanthanum.
Claim 6
Dependent Claim
13 words
The composition of claim 1 comprising from about 1.0% to about 6.0% rhenium.
Claim 7
Dependent Claim
13 words
The composition of claim 1 comprising from about 0.2% to about 4.0% vanadium.
Claim 8
Dependent Claim
13 words
The composition of claim 1 comprising from about 0.2% to about 4.0% niobium.
Claim 9
Dependent Claim
13 words
The composition of claim 1 comprising from about 0.2% to about 1.5% platinum.
Claim 10
Dependent Claim
34 words
An article of manufacture comprising a substrate material fabricated from the composition of claim 1, the substrate being coated with a layer of an aluminide deposit to impart improved high temperature oxidation/corrosion resistance thereto.
Claim 11
Dependent Claim
31 words
The article of claim 9 wherein the aluminide deposit is prepared from a NiAl alloy which contains from about 25 to about 40 percent by weight aluminum, the balance being nickel.
Claim 12
Dependent Claim
120 words
An article of manufacture comprising a substrate material fabricated from the composition of claim 1, the substrate being coated with an overlay coating to impart improved high temperature oxidation/corrosion resistance thereto, the overlay coating composition having the general formula MCrAlY wherein M is a solid solution of metal selected from the group consisting of nickel, cobalt, and mixtures of nickel and cobalt with molybdenum wherein the metals represented by M comprise 30 to 75 percent by weight of the coating; chromium comprises about 10 to about 40 percent by weight of the coating; aluminum comprises about 5 to about 20 percent by weight of the coating and yttrium comprises about 0.1 to about 1.0 percent by weight of the coating.
Claim 13
Independent Claim
288 words
A method for producing a heat-treated single crystal alloy material having improved oxidation/corrosion resistance and improved solid solution strength comprising: (a) providing a composition consisting essentially of, by weight, about 4.0% to about 10.0% chromium; about 1.5% to about 6.0% cobalt; about 1.0% to about 12.0% molybdenum; about 3.0% to about 10.0% tungsten; about 2.5% to about 7.0% titanium; about 2.5% to about 7.0% aluminum; about 3.0% to about 10.0% tantalum; about 0.02% to about 1.0% of at least one element selected from the group consisting of hafnium and silicon; from 0.01 to 1% of at least one element selected from the group consisting of yttrium and lanthanum; from about 0.3% to about 8.0% rhenium; from about 0.2% to about 4.0% of at least one element selected from the group consisting of vanadium and niobium; from about 0.02% to about 3% plantinum; from about 0 to about 1.0% boron, the balance nickel. (b) melting and directionally solidifying the composition to produce a single crystal alloy material; (c) solution heat treating the material at a temperature of between about 2330° F. and about 2430° F. for about 2 to about 6 hours; (d) rapidly cooling the material at a rate greater than about 120° F. per minute from the solution temperature to about 1600° F.; and (e) subjecting the material to a double aging heat treatment by (i) heat treating the material at a temperature of between about 1975° F. and 2050° F. and holding the material at this temperature for about 2 to about 6 hours and then (ii) heat treating the material at a temperature of between about 1600° F. and 1800° F. and holding the material at this temperature for about 16 to about 22 hours.
Claim 14
Independent Claim
288 words
A method for producing a heat-treated single crystal alloy material having improved oxidation/corrosion resistance and improved solid solution strength comprising: (a) providing a composition consisting essentially of, by weight, about 4.0% to about 10.0% chromium; about 1.5% to about 6.0% cobalt; about 1.0% to about 12.0% molybdenum; about 3.0% to about 10.0% tungsten; about 2.5% to about 7.0% titanium; about 2.5% to about 7.0% aluminum; about 3.0% to about 10.0% tantalum; about 0.02% to about 1.0% of at least one element selected from the group consisting of hafnium and silicon; from 0.01 to 1% of at least one element selected from the group consisting of yttrium and lanthanum; from about 0.3% to about 8.0% rhenium; from about 0.2% to about 4.0% of at least one element selected from the group consisting of vanadium and niobium; from about 0.02% to about 3% plantinum; from about 0 to about 1.0% boron, the balance nickel. (b) melting and directionally solidifying the composition to produce a single crystal alloy material; (c) solution heat treating the material at a temperature of between about 2330° F. and about 2430° F. for about 2 to about 6 hours; (d) rapidly cooling the material at a rate greater than about 120° F. per minute from the solution temperature to about 1600° F.; and (e) subjecting the material to a double aging heat treatment by (i) heat treating the material at a temperature of between about 1975° F. and 2050° F. and holding the material at this temperature for about 2 to about 6 hours and then (ii) heat treating the material at a temperature of between about 1600° F. and 1800° F. and holding the material at this temperature for about 16 to about 22 hours.
Claim 15
Dependent Claim
23 words
The method of claim 12 wherein said solution heat treatment of step (c) is performed for about 3 hours in a vacuum atmosphere.
Claim 16
Dependent Claim
15 words
The method of claim 12 wherein said cooling of step (d) occurs by gas cooling.
Claim 17
Dependent Claim
23 words
The method of claim 12 wherein the first aging treatment of step (e) is performed at about 1975° F. for about 4 hours.
Claim 18
Dependent Claim
16 words
The method of claim 15 wherein said first aging treatment is performed in an argon atmosphere.
Claim 19
Dependent Claim
23 words
The method of claim 12 wherein the second aging treatment of step (e) is performed at about 1600° F. for about 20 hours.
Claim 20
Dependent Claim
18 words
The method of claim 17 wherein said second aging treatment is performed in an argon or air atmosphere.
Claim 21
Dependent Claim
21 words
The method of claim 12 wherein said solution heat treatment of step (c) comprises solution heat treating the material two times.
Claim 22
Dependent Claim
56 words
The method of claim 19 wherein the material is (i) first subject to a solution heat treatment at a temperature of about 2330° F. for about 3 hours, (ii) rapidly cooled and then (iii) subject to a second solution heat treatment at a temperature of about 2350° F. for about 3 hours prior to step (d).
Claim 23
Dependent Claim
37 words
The method of claim 20 wherein the step of rapidly cooling the material as defined in (ii) occurs at a rate greater than about 120° F. per minute from said first solution temperature to about 1600° F.
Claim 24
Dependent Claim
13 words
The method of claim 21 wherein said rapid cooling occurs by gas cooling.
Claim 25
Dependent Claim
42 words
The method of claim 20 wherein said double aging heat treatment comprises first heat treating the material at a temperature of about 1975° F. for about 4 hours followed by heat treating the material at about 1600° F. for about 20 hours.
Claim 26
Dependent Claim
116 words
The method of claim 12 wherein said composition consists essentially of, by weight, about 4.0% to about 7.9% chromium; about 2.5% to about 5.0% cobalt; about 2.0% to about 6.0% molybdenum; about 5.0% to about 9.0% tungsten; about 2.5% to about 6.0% titanium; about 3.0% to about 6.0% aluminum; about 4.0% to about 9.0% tantalum; at least one element selected from the group consisting of from about 0.05% to about 0.5% hafnium and from 0.02% to about 0.3% silicon; about 0.05 up to about 0.4% of at least one element selected from the group consisting of yttrium and niobium; from about 0.2% to about 1.5% platinum; from about 0 to 0.3% boron, and the balance nickel.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-12-30 | 1995-07-01 | 1995-12-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-12-30 | 1999-07-01 | 1999-12-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-12-30 | 2003-07-01 | 2003-12-31 | $7700.00 | Window Closed / Lapsed |