High density leucite based ceramics from zeolite
Assignee: Honeywell UOP LLC
•
Filing: 1990-07-25
•
Granted: 1991-12-10
•
Expires: 2010-07-25
Abstract
Abstract This invention relates to processes for preparing ceramic articles. One process involves taking a potassium exchanged zeolite, the zeolite characterized in that it has a SiO 2 /Al 2 O 3 ratio of 3.5 to about 7.5, and calcining it at a temperature of about 900° to about 1100° C. for a time sufficient to collapse the zeolite framework and provide an amorphous powder. Next, the amorphous powder is formed into a shaped article and the article is sintered at a temperature of about 1150° to about 1400° C. for a time of about 0.5 to about 12 hours to give a ceramic article whose principal crystalline phase is tetragonal leucite, is substantially crack free, and has less than 5% porosity. When the zeolite is exchanged with cesium, one obtains a ceramic article whose principal crystalline phase is pollucite, when a rubidium exchanged zeolite is used one obtains a ceramic article whose principal crystalline phase is rubidium leucite, and when a potassium/cesium exchanged zeolite is used one obtains a ceramic article having as its principal crystalline phase a leucite/pollucite solid solution. The addition of pollucite to the leucite article provides a ceramic article whose thermal expansion coefficient can be varied from about 2×10 -6 to about 27×10 -60 C -1 as measured over the range 50°-700° C. This invention also relates to this leucite/pollucite ceramic article.
Inventors
- 👤 Robert L. Bedard
- 👤 Edith M. Flanigen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 19:02
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/16; C04B35/18; C04B35/19
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
111 words
A process for producing a substantially crack free ceramic article having less than 5% porosity and whose principal crystalline phase is tetragonal leucite comprising calcining a powder of a potassium exchanged zeolite, the zeolite having a SiO 2 /Al 2 O 3 ratio of about 3.5 to about 7.5, at a temperature of about 900° to about 1100° C. for a time effective to collapse the zeolite framework and provide an amorphous powder, forming the amorphous powder into a shaped article and sintering the shaped article at a temperature of about 1150° to about 1400° C., for a time of about 0.5 to about 12 hours, thereby forming said ceramic article.
Claim 2
Dependent Claim
111 words
A process for producing a substantially crack free ceramic article having less than 5% porosity and whose principal crystalline phase is tetragonal leucite comprising calcining a powder of a potassium exchanged zeolite, the zeolite having a SiO 2 /Al 2 O 3 ratio of about 3.5 to about 7.5, at a temperature of about 900° to about 1100° C. for a time effective to collapse the zeolite framework and provide an amorphous powder, forming the amorphous powder into a shaped article and sintering the shaped article at a temperature of about 1150° to about 1400° C., for a time of about 0.5 to about 12 hours, thereby forming said ceramic article.
Claim 3
Dependent Claim
22 words
The process of claim 1 where the sintering is carried out at a temperature of about 1200° C. to about 1300° C.
Claim 4
Dependent Claim
26 words
The process of claim 1 where the zeolite is selected from the group consisting of zeolite Y, zeolite B, zeolite L, zeolite W and zeolite omega.
Claim 5
Dependent Claim
11 words
The process of claim 3 where the zeolite is zeolite Y.
Claim 6
Dependent Claim
27 words
The process of claim 1 where the amount of potassium in the potassium exchanged zeolite is at least 50% of the ion exchange capacity of the zeolite.
Claim 7
Dependent Claim
27 words
The process of claim 1 where the amount of potassium in the potassium exchanged zeolite is at least 90% of the ion exchange capacity of the zeolite.
Claim 8
Dependent Claim
175 words
A process for producing a substantially crack free ceramic article having less than 5% porosity and whose principal crystalline phase is a leucite/pollucite solid solution, comprising calcining a powder of a potassium and cesium coexchanged zeolite at a temperature of about 900° to about 1100° C. for a time effective to collapse the zeolite framework and provide an amorphous powder, the zeolite having a SiO 2 /Al 2 O 3 ratio of about 3.5 to about 7.5, a potassium content of greater than zero but less than 100% of the ion exchange capacity of the zeolite, a cesium content of greater than zero but less than 100% of the ion exchange capacity of the zeolite and the sum of the potassium and cesium content is at least 50% of the total ion exchange capacity of the zeolite; forming the amorphous powder into a shaped article and sintering the shaped article at a temperature of about 1150° to about 1400° C., for a time of about 0.5 to about 12 hours, thereby forming said ceramic article.
Claim 9
Dependent Claim
175 words
A process for producing a substantially crack free ceramic article having less than 5% porosity and whose principal crystalline phase is a leucite/pollucite solid solution, comprising calcining a powder of a potassium and cesium coexchanged zeolite at a temperature of about 900° to about 1100° C. for a time effective to collapse the zeolite framework and provide an amorphous powder, the zeolite having a SiO 2 /Al 2 O 3 ratio of about 3.5 to about 7.5, a potassium content of greater than zero but less than 100% of the ion exchange capacity of the zeolite, a cesium content of greater than zero but less than 100% of the ion exchange capacity of the zeolite and the sum of the potassium and cesium content is at least 50% of the total ion exchange capacity of the zeolite; forming the amorphous powder into a shaped article and sintering the shaped article at a temperature of about 1150° to about 1400° C., for a time of about 0.5 to about 12 hours, thereby forming said ceramic article.
Claim 10
Dependent Claim
21 words
The process of claim 7 where the sintering is carried out at a temperature of about 1200° to about 1300° C.
Claim 11
Dependent Claim
26 words
The process of claim 7 where the zeolite is selected from the group consisting of zeolite Y, zeolite B, zeolite L, zeolite W and zeolite omega.
Claim 12
Dependent Claim
11 words
The process of claim 9 where the zeolite is zeolite Y.
Claim 13
Dependent Claim
30 words
The process of claim 7 where the sum of the potassium and cesium concentration in the co-exchanged zeolite is at least 90% of the ion exchange capacity of the zeolite.
Claim 14
Dependent Claim
191 words
A process for producing a substantially crack free ceramic article having less than 5% porosity and whose principal crystalline phase is a leucite/pollucite solid solution, comprising calcining a powder which is a mixture of a potassium exchanged zeolite and a cesium exchanged zeolite at a temperature of about 900° C. to about 1100° C. for a time effective to collapse the zeolite framework and provide an amorphous powder, the zeolite having a SiO 2 /Al 2 O 3 ratio of about 3.5 to about 7.5, the potassium exchanged zeolite having a potassium content greater than zero but less than 100% of the ion exchange capacity of the zeolite, the cesium exchanged zeolite having a cesium content greater than zero but less than 100% of the ion exchange capacity of the zeolite and the sum of the potassium and cesium content is at least 50% of the total ion exchange capacity of the zeolites; forming the amorphous powder into a shaped article and sintering the shaped article at a temperature of about 1150° to about 1400° C., for a time of about 0.5 to about 12 hours, thereby forming said ceramic article.
Claim 15
Dependent Claim
191 words
A process for producing a substantially crack free ceramic article having less than 5% porosity and whose principal crystalline phase is a leucite/pollucite solid solution, comprising calcining a powder which is a mixture of a potassium exchanged zeolite and a cesium exchanged zeolite at a temperature of about 900° C. to about 1100° C. for a time effective to collapse the zeolite framework and provide an amorphous powder, the zeolite having a SiO 2 /Al 2 O 3 ratio of about 3.5 to about 7.5, the potassium exchanged zeolite having a potassium content greater than zero but less than 100% of the ion exchange capacity of the zeolite, the cesium exchanged zeolite having a cesium content greater than zero but less than 100% of the ion exchange capacity of the zeolite and the sum of the potassium and cesium content is at least 50% of the total ion exchange capacity of the zeolites; forming the amorphous powder into a shaped article and sintering the shaped article at a temperature of about 1150° to about 1400° C., for a time of about 0.5 to about 12 hours, thereby forming said ceramic article.
Claim 16
Dependent Claim
21 words
The process of claim 12 where the sintering is carried out at a temperature of about 1200° to about 1300° C.
Claim 17
Dependent Claim
26 words
The process of claim 12 where the zeolite is selected from the group consisting of zeolite Y, zeolite B, zeolite L, zeolite W and zeolite omega.
Claim 18
Dependent Claim
11 words
The process of claim 14 where the zeolite is zeolite Y.
Claim 19
Dependent Claim
27 words
The process of claim 12 where the sum of the potassium and cesium concentration is at least 90% of the total ion exchange capacity of the zeolites.
Claim 20
Dependent Claim
111 words
A process for producing a substantially crack free ceramic article having less than 5% porosity and whose principal crystalline phase is rubidium leucite, comprising calcining a powder of a rubidium exchanged zeolite, the zeolite having a SiO 2 /Al 2 O 3 ratio of about 3.5 to about 7.5, at a temperature of about 900° to about 1100° C. for a time effective to collapse the zeolite framework and provide an amorphous powder, forming the amorphous powder into a shaped article and sintering the shaped article at a temperature of about 1150° to about 1400° C., for a time of about 0.5 to about 12 hours, thereby forming said ceramic article.
Claim 21
Dependent Claim
111 words
A process for producing a substantially crack free ceramic article having less than 5% porosity and whose principal crystalline phase is rubidium leucite, comprising calcining a powder of a rubidium exchanged zeolite, the zeolite having a SiO 2 /Al 2 O 3 ratio of about 3.5 to about 7.5, at a temperature of about 900° to about 1100° C. for a time effective to collapse the zeolite framework and provide an amorphous powder, forming the amorphous powder into a shaped article and sintering the shaped article at a temperature of about 1150° to about 1400° C., for a time of about 0.5 to about 12 hours, thereby forming said ceramic article.
Claim 22
Dependent Claim
22 words
The process of claim 17 where the sintering is carried out at a temperature of about 1200° C. to about 1300° C.
Claim 23
Dependent Claim
26 words
The process of claim 17 where the zeolite is selected from the group consisting of zeolite Y, zeolite B, zeolite L, zeolite W and zeolite omega.
Claim 24
Dependent Claim
11 words
The process of claim 19 where the zeolite is zeolite Y.
Claim 25
Dependent Claim
27 words
The process of claim 17 where the amount of rubidium in the rubidium exchanged zeolite is at least 50% of the ion exchange capacity of the zeolite.
Claim 26
Dependent Claim
27 words
The process of claim 17 where the amount of rubidium in the rubidium exchanged zeolite is at least 90% of the ion exchange capacity of the zeolite.
Claim 27
Dependent Claim
108 words
A process for producing a substantially crack free ceramic article having less than 5% porosity and whose principal crystalline phase is pollucite comprising calcining a powder of a cesium exchanged zeolite having a SiO 2 /Al 2 O 3 ratio of about 3.5 to about 7.5, at a temperature of about 900° to about 1100° C. for a time effective to collapse the zeolite framework and provide an amorphous powder, forming the amorphous powder into a shaped article and sintering the shaped article at a temperature of about 1150° to about 1400° C., for a time of about 0.5 to about 12 hours, thereby forming said ceramic article.
Claim 28
Dependent Claim
108 words
A process for producing a substantially crack free ceramic article having less than 5% porosity and whose principal crystalline phase is pollucite comprising calcining a powder of a cesium exchanged zeolite having a SiO 2 /Al 2 O 3 ratio of about 3.5 to about 7.5, at a temperature of about 900° to about 1100° C. for a time effective to collapse the zeolite framework and provide an amorphous powder, forming the amorphous powder into a shaped article and sintering the shaped article at a temperature of about 1150° to about 1400° C., for a time of about 0.5 to about 12 hours, thereby forming said ceramic article.
Claim 29
Dependent Claim
21 words
The process of claim 23 where the sintering is carried out at a temperature of about 1200° to about 1300° C.
Claim 30
Dependent Claim
26 words
The process of claim 23 where the zeolite is selected from the group consisting of zeolite Y, zeolite B, zeolite L, zeolite W and zeolite omega.
Claim 31
Dependent Claim
11 words
The process of claim 25 where the zeolite is zeolite Y.
Claim 32
Dependent Claim
25 words
The process of claim 23 where the concentration of cesium in the zeolite is at least 50% of the ion exchange capacity of the zeolite.
Claim 33
Dependent Claim
25 words
The process of claim 23 where the concentration of cesium in the zeolite is at least 90% of the ion exchange capacity of the zeolite.
Claim 34
Dependent Claim
106 words
A substantially crack free ceramic article having less than 5% porosity, having as its principal crystalline phase a leucite/pollucite solid solution and having an empirical formula expressed in terms of the metal oxides: xK.sub.2 O:yCs.sub.2 O:zSiO.sub.2 :Al.sub.2 O.sub.3 where x varies from about 0.01 to about 0.99, y varies from about 0.99 to about 0.01 and z varies from about 3.5 to about 7.5 except that when z is 7.5, y is greater than 0.19, the ceramic article characterized in that it has a coefficient of thermal expansion of about 2×10 -6 to about 27×10 -6 ° C. -1 over the range 50° to 700° C.
Claim 35
Dependent Claim
106 words
A substantially crack free ceramic article having less than 5% porosity, having as its principal crystalline phase a leucite/pollucite solid solution and having an empirical formula expressed in terms of the metal oxides: xK.sub.2 O:yCs.sub.2 O:zSiO.sub.2 :Al.sub.2 O.sub.3 where x varies from about 0.01 to about 0.99, y varies from about 0.99 to about 0.01 and z varies from about 3.5 to about 7.5 except that when z is 7.5, y is greater than 0.19, the ceramic article characterized in that it has a coefficient of thermal expansion of about 2×10 -6 to about 27×10 -6 ° C. -1 over the range 50° to 700° C.
References Cited (Backward Citations)
US4503023A
Cited
US4604366A
Cited
US4840779A
Cited
US4798536A
Cited
EP0298701A2
Cited
US4814303A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-12-09 | 1995-06-10 | 1995-12-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-12-09 | 1999-06-10 | 1999-12-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-12-09 | 2003-06-10 | 2003-12-10 | $7700.00 | Window Closed / Lapsed |