US5070119A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Flexible intumescent coating composition
Assignee: PPG Industries Ohio Inc
•
Filing: 1991-03-11
•
Granted: 1991-12-03
•
Expires: 2011-03-11
Abstract
Abstract Disclosed is an intumescent curable composition which contains as a resinous binder a flexible polyepoxide resin. The polyepoxide is cured with an appropriate curing agent adapted for the particular resin. An additive component is present which contains a mixture of materials which provide a source of (i) zinc, (ii) boron, (iii) phosphorus, and (iv) an expansion gas upon thermal decomposition. The composition is capable of forming a carbonaceous char upon exposure to heat or flame, with the proviso that the cured, unburned composition has sufficient flexibility that it passes at least 10 continuous cycles of a cold cycle test without cracking. The cold cycle test involves the following steps; the composition is applied at a thickness of 0.5 inch (12.7 millimeters) to a 10 inch (0.254 meter) section of a 4W13 I-beam having two thermocouples attached to the surface, allowed to cure at ambient temperature for 16 hours, force cured for 5 days at about 60° C. an subjected to the cold cycle test. For one cycle, the beam is placed in a freezer operating at a temperature between about 0° F. (-18° C.) and about -10° F. (-23° C.) for sufficient time for the steel to reach a temperature between about 0° F. (-18° C.) and about (-10° F.) -23° C. as determined by the two thermocouples attached to the surface of the beam beneath the coating, removed from the freezer and a 50 square inch area 0.0323 square meter) of the surface warmed as shown in FIGS. 1 and 2 by passing a heat gun (Model No. HG 50146, Alpha Division of Loral Corp, 14 amp; minimum temperature at tip 500° F. (260° C.) a distance of 0.5 inch (12.7 millimeter) from the surface, uniformly over the surface until the surface temperature reaches 110° F. (43° C.) within a 3 minute period, as determined by a thermocouple moved about the surface and allowed to stand for at least 2 hours at ambient temperature.
Inventors
- 👤 Richard M. Nugent, Jr.
- 👤 Thomas A. Ward
- 👤 Paul D. Greigger
- 👤 Jerome A. Seiner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 03:00
CPC Classifications
C; C09; C09K; C09K21/00; C09K21/06; C09K21/12; C08; C08K; C08K13/00; C08K13/02; C09D; C09D5/00; C09D5/18; C09D5/185; C09K21/02; C09K21/04; Y; Y10; Y10S; Y10S521/00; Y10S521/907
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
293 words
An intumescent curable composition comprising: (a) a polyepoxide resin, (b) a curing agent adapted to cure the polyepoxide resin, (c) an additive component comprising a mixture of materials adapted to provide a source of (i) zinc (ii) boron, (iii) phosphorus and (iv) an expansion gas upon thermal decomposition, said composition being capable of forming a carbonaceous char upon exposure to heat or flame, with the proviso that the cured, unburned composition has sufficient flexibility that it passes at least 10 continuous cycles of a cold cycle test without cracking when the composition is applied at a thickness of 0.5 inch (12.7 millimeters) to a 10 inch (0.254 meter) section of a 4W13 I-beam having two thermocouples attached to the surface, allowed to cure at ambient temperature for 16 hours, force cured for 5 days at about 60° C. and subjected to the cold cycle test wherein for one cycle the beam is placed in a freezer operating at a temperature between about 0° F. (-18° C.) and about -10° F. (-23° C.) for sufficient time for the steel to reach a temperature between about 0° F. (-18° C.) and about (-10° F.) - 23° C. as determined by the two thermocouples attached to the surface of the beam beneath the coating, removed from the freezer and a 50 square inch area (0.0323 square meter) of the surface warmed by passing a heat gun, 14 amps, minimum temperature at tip 500° F. (260° C.) at a distance of 0.5 inch (12.7 millimeter) from the surface, uniformly over the surface until the surface temperature reaches 110° F. (43° C.) within a 3 minute period, as determined by a thermocouple moved about the surface, and allowed to stand for at least 2 hours at ambient temperature.
Claim 2
Dependent Claim
293 words
An intumescent curable composition comprising: (a) a polyepoxide resin, (b) a curing agent adapted to cure the polyepoxide resin, (c) an additive component comprising a mixture of materials adapted to provide a source of (i) zinc (ii) boron, (iii) phosphorus and (iv) an expansion gas upon thermal decomposition, said composition being capable of forming a carbonaceous char upon exposure to heat or flame, with the proviso that the cured, unburned composition has sufficient flexibility that it passes at least 10 continuous cycles of a cold cycle test without cracking when the composition is applied at a thickness of 0.5 inch (12.7 millimeters) to a 10 inch (0.254 meter) section of a 4W13 I-beam having two thermocouples attached to the surface, allowed to cure at ambient temperature for 16 hours, force cured for 5 days at about 60° C. and subjected to the cold cycle test wherein for one cycle the beam is placed in a freezer operating at a temperature between about 0° F. (-18° C.) and about -10° F. (-23° C.) for sufficient time for the steel to reach a temperature between about 0° F. (-18° C.) and about (-10° F.) - 23° C. as determined by the two thermocouples attached to the surface of the beam beneath the coating, removed from the freezer and a 50 square inch area (0.0323 square meter) of the surface warmed by passing a heat gun, 14 amps, minimum temperature at tip 500° F. (260° C.) at a distance of 0.5 inch (12.7 millimeter) from the surface, uniformly over the surface until the surface temperature reaches 110° F. (43° C.) within a 3 minute period, as determined by a thermocouple moved about the surface, and allowed to stand for at least 2 hours at ambient temperature.
Claim 3
Dependent Claim
294 words
An intumescent curable composition comprising: (a) a flexible polyepoxide resin; (b) a curing agent adapted to cure the polyepoxide resin, (c) an additive component comprising a mixture of materials adapted to provide a source of (i) zinc, (ii) boron, (iii) phosphorus and (iv) an expansion gas upon thermal decomposition, said composition being capable of forming a carbonaceous char upon exposure to heat or flame, with the proviso that the cured, unburned composition has sufficient flexibility that it passes at least 10 continuous cycles of a cold cycle test without cracking when the composition is applied at a thickness of 0.5 inch (12.7 millimeters) to a 10 inch (0.254 meter) section of a 4W13 I-beam having two thermocouples attached to the surface, allowed to cure at ambient temperature for 16 hours, force cured for 5 days at about 60° C. and subjected to the cold cycle test wherein for one cycle the beam is placed in a freezer operating at a temperature between about 0° F. (-18° C.) and about -10° F. (-23° C.) for sufficient time for the steel to reach a temperature between about 0° F. (-18° C.) and about (-10° F.) - 23° C. as determined by the two thermocouples attached to the surface of the beam beneath the coating, removed from the freezer and a 50 square inch area (0.0323 square meter) of the surface warmed by passing a heat gun, 14 amps minimum temperature at tip 500° F. (260° C.) at a distance of 0.5 inch (12.7 millimeter) from the surface, uniformly over the surface until the surface temperature reaches 110° F. (43° C.) within a 3 minute period, as determined by a thermocouple moved about the surface, and allowed to stand for at least 2 hours at ambient temperature.
Claim 4
Dependent Claim
294 words
An intumescent curable composition comprising: (a) a flexible polyepoxide resin; (b) a curing agent adapted to cure the polyepoxide resin, (c) an additive component comprising a mixture of materials adapted to provide a source of (i) zinc, (ii) boron, (iii) phosphorus and (iv) an expansion gas upon thermal decomposition, said composition being capable of forming a carbonaceous char upon exposure to heat or flame, with the proviso that the cured, unburned composition has sufficient flexibility that it passes at least 10 continuous cycles of a cold cycle test without cracking when the composition is applied at a thickness of 0.5 inch (12.7 millimeters) to a 10 inch (0.254 meter) section of a 4W13 I-beam having two thermocouples attached to the surface, allowed to cure at ambient temperature for 16 hours, force cured for 5 days at about 60° C. and subjected to the cold cycle test wherein for one cycle the beam is placed in a freezer operating at a temperature between about 0° F. (-18° C.) and about -10° F. (-23° C.) for sufficient time for the steel to reach a temperature between about 0° F. (-18° C.) and about (-10° F.) - 23° C. as determined by the two thermocouples attached to the surface of the beam beneath the coating, removed from the freezer and a 50 square inch area (0.0323 square meter) of the surface warmed by passing a heat gun, 14 amps minimum temperature at tip 500° F. (260° C.) at a distance of 0.5 inch (12.7 millimeter) from the surface, uniformly over the surface until the surface temperature reaches 110° F. (43° C.) within a 3 minute period, as determined by a thermocouple moved about the surface, and allowed to stand for at least 2 hours at ambient temperature.
Claim 5
Dependent Claim
285 words
An intumescent curable composition comprising: (a) a polyepoxide resin, (b) a flexible curing agent adapted to cure the polyepoxide, (c) an additive component, comprising a mixture of (i) zinc, (ii) boron, (iii) phosphorus and (iv) an expansion gas upon thermal decomposition, said composition being capable of forming a carbonaceous char upon exposure to heat or flame, with the proviso that the cured, unburned composition has sufficient flexibility that it passes at least 10 continuous cycles of a cold cycle test without cracking when the composition is applied at a thickness of 0.5 inch (12.7 millimeters) to a 10 inch (0.254 meter) section of a 4W13 I-beam having two thermocouples attached to the surface, allowed to cure at ambient temperature for 16 hours, force cured for 5 days at about 60° C. and subjected to the cold cycle test wherein for one cycle the beam is placed in a freezer operating at a temperature between about 0° F. (-18° C.) and about -10° F. (-23° C.) for sufficient time for the steel to reach a temperature between about 0° F. (-18° C.) and about (-10° F.) -23° C. as determined by the two thermocouples attached to the surface of the beam beneath the coating, removed from the freezer and a 50 square inch area (0.0323 square meter) of the surface warmed by passing a heat gun, 14 amps minimum temperature at tip 500° F. (260° C.) at a distance of 0.5 inch (12.7 millimeter) from the surface, uniformly over the surface until the surface temperature reaches 110° F. (43° C.) within a 3 minute period, as determined by a thermocouple moved about the surface, and allowed to stand for at least 2 hours at ambient temperature.
Claim 6
Dependent Claim
285 words
An intumescent curable composition comprising: (a) a polyepoxide resin, (b) a flexible curing agent adapted to cure the polyepoxide, (c) an additive component, comprising a mixture of (i) zinc, (ii) boron, (iii) phosphorus and (iv) an expansion gas upon thermal decomposition, said composition being capable of forming a carbonaceous char upon exposure to heat or flame, with the proviso that the cured, unburned composition has sufficient flexibility that it passes at least 10 continuous cycles of a cold cycle test without cracking when the composition is applied at a thickness of 0.5 inch (12.7 millimeters) to a 10 inch (0.254 meter) section of a 4W13 I-beam having two thermocouples attached to the surface, allowed to cure at ambient temperature for 16 hours, force cured for 5 days at about 60° C. and subjected to the cold cycle test wherein for one cycle the beam is placed in a freezer operating at a temperature between about 0° F. (-18° C.) and about -10° F. (-23° C.) for sufficient time for the steel to reach a temperature between about 0° F. (-18° C.) and about (-10° F.) -23° C. as determined by the two thermocouples attached to the surface of the beam beneath the coating, removed from the freezer and a 50 square inch area (0.0323 square meter) of the surface warmed by passing a heat gun, 14 amps minimum temperature at tip 500° F. (260° C.) at a distance of 0.5 inch (12.7 millimeter) from the surface, uniformly over the surface until the surface temperature reaches 110° F. (43° C.) within a 3 minute period, as determined by a thermocouple moved about the surface, and allowed to stand for at least 2 hours at ambient temperature.
Claim 7
Dependent Claim
304 words
An intumescent curable composition comprising: (a) an epoxy functional adduct of a flexible acid functional polyester with a polyepoxide, (b) a curing agent adapted to cure the epoxy functional adduct; and (c) an additive component comprising a mixture of materials adapted to provide a source of (i) zinc, (ii) boron, (iii) phosphorus and (iv) an expansion gas upon thermal decomposition, said composition being capable of forming a carbonaceous char upon exposure to heat or flame, with the proviso that the cured, unburned composition has sufficient flexibility that it passes at least 10 continuous cycles of a cold cycle test without cracking when the composition is applied at a thickness of 0.5 inch (12.7 millimeters) to a 10 inch (0.254 meter) section of a 4W13 I-beam having two thermocouples attached to the surface, allowed to cure at ambient temperature for 16 hours, force cured for 5 days at about 60° C. and subjected to the cold cycle test wherein for one cycle the beam is placed in a freezer operating at a temperature between about 0° F. (-18° C.) and about -10° F. (-23° C.) for sufficient time for the steel to reach a temperature between about 0° F. (-18° C.) and about (-10° F.) -23° C. as determined by the two thermocouples attached to the surface of the beam beneath the coating, removed from the freezer and a 50 square inch area (0.0323 square meter) of the surface warmed by passing a heat gun, 14 amps minimum temperature at tip 500° F. (260° C.) at a distance of 0.5 inch (12.7 millimeter) from the surface, uniformly over the surface until the surface temperature reaches 110° F. (43° C.) within a 3 minute period, as determined by a thermocouple moved about the surface, and allowed to stand for at least 2 hours at ambient temperature.
Claim 8
Dependent Claim
304 words
An intumescent curable composition comprising: (a) an epoxy functional adduct of a flexible acid functional polyester with a polyepoxide, (b) a curing agent adapted to cure the epoxy functional adduct; and (c) an additive component comprising a mixture of materials adapted to provide a source of (i) zinc, (ii) boron, (iii) phosphorus and (iv) an expansion gas upon thermal decomposition, said composition being capable of forming a carbonaceous char upon exposure to heat or flame, with the proviso that the cured, unburned composition has sufficient flexibility that it passes at least 10 continuous cycles of a cold cycle test without cracking when the composition is applied at a thickness of 0.5 inch (12.7 millimeters) to a 10 inch (0.254 meter) section of a 4W13 I-beam having two thermocouples attached to the surface, allowed to cure at ambient temperature for 16 hours, force cured for 5 days at about 60° C. and subjected to the cold cycle test wherein for one cycle the beam is placed in a freezer operating at a temperature between about 0° F. (-18° C.) and about -10° F. (-23° C.) for sufficient time for the steel to reach a temperature between about 0° F. (-18° C.) and about (-10° F.) -23° C. as determined by the two thermocouples attached to the surface of the beam beneath the coating, removed from the freezer and a 50 square inch area (0.0323 square meter) of the surface warmed by passing a heat gun, 14 amps minimum temperature at tip 500° F. (260° C.) at a distance of 0.5 inch (12.7 millimeter) from the surface, uniformly over the surface until the surface temperature reaches 110° F. (43° C.) within a 3 minute period, as determined by a thermocouple moved about the surface, and allowed to stand for at least 2 hours at ambient temperature.
Claim 9
Dependent Claim
16 words
The intumescent curable composition of claim 1 additionally comprising a flexibilizer reactive with the curing agent.
Claim 10
Dependent Claim
36 words
The intumescent curable composition of claim 4 wherein the curing agent is an amine functional Michael adduct prepared from a mono-m di- or polyamine or mixture thereof with a mono-, di- or polyacrylate or mixture thereof.
Claim 11
Dependent Claim
47 words
The intumescent curable composition of claim 4 wherein the polyester used to prepare the adduct is prepared from a polycarboxylic acid component comprising a polycarboxylic acid or mixture of acids having from 7 to 16 carbon atoms and a polyol component comprising a portion of diethylene glycol.
Claim 12
Dependent Claim
21 words
The intumescent curable composition of claim 7 wherein the polycarboxylic acid component comprises a mixture of dodecanedioic acid and azeleic acid.
Claim 13
Dependent Claim
16 words
The intumescent curable composition of claim 4 wherein the curing agent is an amine curing agent.
Claim 14
Dependent Claim
13 words
The intumescent curable composition of claim 9 wherein the amine is a polyamino-polyamide.
Claim 15
Dependent Claim
24 words
The intumescent curable composition of claim 4 wherein the source of zinc is selected from zinc oxide, zinc borate, zinc phosphate and zinc carbonate.
Claim 16
Dependent Claim
28 words
The intumescent curable composition of claim 4 wherein the source of boron is selected from boron oxide, sodium borate, potassium borate, ammonium pentaborate, ammonium borate and zinc borate.
Claim 17
Dependent Claim
28 words
The intumescent curable composition of claim 4 wherein the source of phosphorus is selected from tris-2-chloroethyl phosphate, phosphoric acid, mono- and di-ammonium phosphate, melamine pyrophosphate, and ammonium polyphosphate.
Claim 18
Dependent Claim
39 words
The intumescent curable composition of claim 4 wherein the zinc is present in an amount ranging from about 0.1 to about 25 percent by weight based on the total weight of the polyepoxide resin, curing agent and additive component.
Claim 19
Dependent Claim
39 words
The intumescent curable composition of claim 4 wherein the boron is present in an amount ranging from about 0.1 to about 10 percent by weight based on the total weight of the polyepoxide resin, curing agent and additive component.
Claim 20
Dependent Claim
37 words
The intumescent curable composition of claim 4 wherein the phosphorus is present in an amount ranging from about 0.05 to about 20 percent by weight based on total weight of polyepoxide resin, curing agent and additive component.
Claim 21
Dependent Claim
12 words
The intumescent curable composition of claim 1 additionally comprising a reinforcing filler.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-12-02 | 1995-06-03 | 1995-12-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-12-02 | 1999-06-03 | 1999-12-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-12-02 | 2003-06-03 | 2003-12-03 | $7700.00 | Window Closed / Lapsed |