Assignee: Applied Process Inc
•
Filing: 1989-12-04
•
Granted: 1991-11-12
•
Expires: 2009-12-04
Abstract
Abstract A method for producing a selectively surface hardened cast iron part includes uniformly heating the surface of the part by immersion into a molten metallic bath until a desired thickness of surface austenite is produced, and thereafter quenching the heated cast iron part in a liquid quenching bath which is maintained at a temperature of between about 450° to about 800° F. for about 10 minutes to about 4 hours. The resultant selectively surface hardened cast iron part is surface hardened with the bulk of the body of the part remaining untempered. An apparatus for performing this process includes a molten metal bath chamber for containing the molten metal and a molten salt bath quenching chamber for quenching the cast iron parts with a conveyor means extending between the molten metal bath and the molten salt bath chambers. A second conveyor means removes the parts from the molten salt bath chamber.
Inventors
- 👤 Bela V. Kovacs
- 👤 John R. Keough
- 👤 Douglas M. Pramstaller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 09:39
CPC Classifications
C; C21; C21D; C21D5/00; C21D1/00; C21D1/34; C21D1/44; Y; Y10; Y10S; Y10S420/00; Y10S420/902
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
143 words
A method for producing a selectively surface hardened cast iron part, comprising: uniformly heating the surface of the cast iron part, without heating the interior of the cast iron part, by immersing the part in a molten matallic bath maintained at a temperature of from about 1500 to about 1800 degrees Fahrenheit for about 10 second to about 5 minutes to form a desired thickness of surface austenite, wherein only the surface of the cast iron part is prepared for hardening; quenching the surface heated cast iron part in a liquid quenching bath maintained at a temperature of between about 450 to about 800 degrees Fahrenheit for about 10 minutes to about 4 hours; and cooling the cast iron part before bainite is formed. such that the interior bulk of the part remains substantially unheated and unhardened, and only the surface is hardened.
Claim 2
Independent Claim
143 words
A method for producing a selectively surface hardened cast iron part, comprising: uniformly heating the surface of the cast iron part, without heating the interior of the cast iron part, by immersing the part in a molten matallic bath maintained at a temperature of from about 1500 to about 1800 degrees Fahrenheit for about 10 second to about 5 minutes to form a desired thickness of surface austenite, wherein only the surface of the cast iron part is prepared for hardening; quenching the surface heated cast iron part in a liquid quenching bath maintained at a temperature of between about 450 to about 800 degrees Fahrenheit for about 10 minutes to about 4 hours; and cooling the cast iron part before bainite is formed. such that the interior bulk of the part remains substantially unheated and unhardened, and only the surface is hardened.
Claim 3
Dependent Claim
51 words
The method of claim 1, wherein said step of uniformly heating the surface of the cast iron part is accomplished by uniformly heating the surface of a finish-machined iron part made of a cast iron selected from the group consisting of compacted graphite iron, gray iron, malleable iron, and ductile iron.
Claim 4
Dependent Claim
23 words
The method of claim 1, further comprising an additional step of agitating the cast iron part after immersion in the molten metallic bath.
Claim 5
Dependent Claim
27 words
The method of claim 1, further comprising an additional step of agitating the molten metal around the part after immersing the part in a molten metallic bath.
Claim 6
Dependent Claim
46 words
The method of claim 1, wherein said step of heating the cast iron part by immersing the part in a molten metallic bath is accomplished by immersing the part in a metallic bath including a molten metal selected from the group consisting of lead and tin.
Claim 7
Dependent Claim
38 words
The method of claim 1, wherein said step of uniformly heating the cast ]-ron part until a desired thickness of surface austenite is produced includes producing a thickness of austenite from about 1/32 inch to about 1/4 inch.
Claim 8
Dependent Claim
43 words
The method of claim 1, wherein said step of quenching the heated cast iron part in a liquid quenching bath is accomplished by quenching in a quenching bath including a quenching fluid selected from the group consisting of molten salt and hot oil.
Claim 9
Dependent Claim
39 words
The method of claim 1, wherein said quenching in a liquid quenching bath is accomplished by quenching in a molten salt bath including a molten salt selected from the group consisting of potassium nitrate, sodium nitrite, and mixtures thereof.
Claim 10
Independent Claim
149 words
A method for producing a finish-machined, selectively surface hardened cast iron part, comprising: uniformly heating the surface of a finish-machined cast iron part, without heating the interior of the cast iron part, by immersing in a molten lead bath maintained at a temperature from about 1500-1800 degrees Fahrenheit for about 30 to about 120 seconds, wherein only the surface of the cast iron part is prepared for hardening while maintaining an inert atmosphere above the molten lead bath; quenching the surface heated cast iron part in a molten salt bath of about 50% potassium nitrate and about 50% sodium nitrite maintained at a temperature of from about 450 to about 750 degrees Fahrenheit for about 1/2 to about 4 hours; and cooling the cast iron part before bainite is formed, such that the interior bulk of the part remains substantially unheated and unhardened, and only the surface is hardened.
Claim 11
Independent Claim
149 words
A method for producing a finish-machined, selectively surface hardened cast iron part, comprising: uniformly heating the surface of a finish-machined cast iron part, without heating the interior of the cast iron part, by immersing in a molten lead bath maintained at a temperature from about 1500-1800 degrees Fahrenheit for about 30 to about 120 seconds, wherein only the surface of the cast iron part is prepared for hardening while maintaining an inert atmosphere above the molten lead bath; quenching the surface heated cast iron part in a molten salt bath of about 50% potassium nitrate and about 50% sodium nitrite maintained at a temperature of from about 450 to about 750 degrees Fahrenheit for about 1/2 to about 4 hours; and cooling the cast iron part before bainite is formed, such that the interior bulk of the part remains substantially unheated and unhardened, and only the surface is hardened.
Claim 12
Dependent Claim
22 words
The method of claim 9, further comprising a step of agitating the cast iron part after immersion in the molten lead bath.
Claim 13
Dependent Claim
19 words
The method of claim 9, further comprising a step of agitating the molten lead around the part after immersion.
Claim 14
Dependent Claim
36 words
The method of claim 9, wherein the step of maintaining an inert atmosphere is accomplished by maintaining an atmosphere of gas selected from the group consisting of nitrogen, argon and helium over the molten lead bath.
Claim 15
Dependent Claim
49 words
The method of claim 9, wherein said step of uniformly heating the surface of the cast iron part is accomplished by uniformly heating the surface of an iron part made of an iron selected from the group consisting of compacted graphite iron, gray iron, malleable iron, and ductile iron.
Claim 16
Dependent Claim
170 words
A selectively surface hardened cast iron part, comprising: a cast iron core formed by casting and finish machining into a desired shape; a selectively hardened surface surrounding the cast iron core, said surface being formed by rapidly heating the surface of the cast iron part by immersing in a molten metallic bath maintained at a temperature of from about 1500 to about 1800 degrees Fahrenheit for about 5 minutes or less, to form a desired thickness of surface austenite, wherein only the surface of the cast iron part is prepared for hardening; thereafter quenching by immersing the surface heated cast iron part in a quenching bath maintained at a bainite reaction temperature of between about 450 to about 800 degrees Fahrenheit for about 10 minutes to about 4 hours to produce the desired hardness and physical properties in the surface layer; and cooling the cast iron part before bainite is formed, such that the interior bulk of the part remains substantially unheated and unhardened, and only the surface is hardened.
Claim 17
Dependent Claim
170 words
A selectively surface hardened cast iron part, comprising: a cast iron core formed by casting and finish machining into a desired shape; a selectively hardened surface surrounding the cast iron core, said surface being formed by rapidly heating the surface of the cast iron part by immersing in a molten metallic bath maintained at a temperature of from about 1500 to about 1800 degrees Fahrenheit for about 5 minutes or less, to form a desired thickness of surface austenite, wherein only the surface of the cast iron part is prepared for hardening; thereafter quenching by immersing the surface heated cast iron part in a quenching bath maintained at a bainite reaction temperature of between about 450 to about 800 degrees Fahrenheit for about 10 minutes to about 4 hours to produce the desired hardness and physical properties in the surface layer; and cooling the cast iron part before bainite is formed, such that the interior bulk of the part remains substantially unheated and unhardened, and only the surface is hardened.
Claim 18
Dependent Claim
36 words
The selectively surface hardened cast iron part of claim 14, wherein said cast iron core is formed of an iron selected from a group consisting of compacted graphite iron, gray iron, malleable iron and ductile iron.
Claim 19
Dependent Claim
37 words
The selectively surface hardened cast iron part of claim 14, wherein said cast iron part is formed by a method of casting selected from the group consisting of sand casting, permanent mold casting, and ceramic mold casting.
Claim 20
Dependent Claim
38 words
The selectively surface hardened cast iron part of claim 14, wherein said desired thickness of surface austenite is formed by immersing the cast iron part in the molten metallic bath for about 10 seconds to about 5 minutes.
Claim 21
Dependent Claim
34 words
The selectively surface hardened cast iron part of claim 17, wherein said desired thickness of surface austenite is formed by immersing the cast iron part in the molten metallic bath for about 45 seconds.
Claim 22
Dependent Claim
30 words
The selectively surface hardened cast iron part of claim 14, wherein said part is formed by immersing in a metal bath selected from the group consisting of lead and- tin.
Claim 23
Dependent Claim
46 words
The selectively surface hardened cast iron part of claim 14, wherein said molten metallic bath maintained at a temperature of from about 1500 to about 1800 degrees Fahrenheit depends o the chemical composition and stoichiometry of the particular cast iron composition of the cast iron part.
Claim 24
Dependent Claim
29 words
The selectively surface hardened cast iron part of claim 14, wherein said desired thickness of surface austenite includes a thickness of from about 1/32 inch to about 1/4 inch.
Claim 25
Dependent Claim
32 words
The selectively surface hardened cast iron part of claim 14, wherein said part is quenched in a bath of a material selected from the group consisting of hot oil and molten salt.
Claim 26
Dependent Claim
39 words
The selectively surface hardened cast iron part of claim 22, wherein said quenching bath is made from a composition of between about 0 to 50 percent by volume potassium nitrate and 50 to 100 percent by volume sodium nitrite.
Claim 27
Dependent Claim
31 words
The selectively surface hardened cast iron part of claim 23, wherein said part is quenched in a quenching bath of about 50 percent potassium nitrate and about 50 percent sodium nitrite.
References Cited (Backward Citations)
US4596606A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-11-11 | 1995-05-13 | 1995-11-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-11-11 | 1999-05-13 | 1999-11-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-11-11 | 2003-05-13 | 2003-11-12 | $7700.00 | Window Closed / Lapsed |