Abstract
Abstract A method is described for separating a mixture of flat metal alloy particles in which the particles of one alloy are generally smaller and less conductive than the particles of another alloy, e.g. a scrap mixture of aluminum-lithium alloy and other wrought aluminum alloys. In this method, the scrap mixture is thermally pretreated and then crushed into relatively flat particles, such that the aluminum-lithium alloy is fragmented into smaller particle sizes than the otehr wrought alloys. These particles are then physically separated based on differences in particle size, density and/or electric conductivity. For instance, the separation may be done by an eddy current separator or a dense media separator.
Inventors
- 👤 Robin D. Brassinga
- 👤 Wijnand L. Dalmijn
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 14:20
CPC Classifications
C; C22; C22B; C22B7/00; C22B7/005; B; B03; B03B; B03B1/00; B03B1/02; B03B5/00; B03B5/28; B03B5/30; B03B5/32; B03B5/34; B03B9/00; B03B9/06; B03B9/061; B03C; B03C1/00; B03C1/02; B03C1/23; Y; Y02; Y02P; Y02P10/00; Y02P10/20; Y02W; Y02W30/00; Y02W30/50; Y02W30/52
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
211 words
A method of separating a mixture of aluminum-lithium alloy and other wrought aluminum alloys comprising the steps of: (a) crushing the mixture into the form of substantially flat particles in which the particles of aluminum-lithium alloy have generally smaller dimensions, smaller density values and smaller conductivity values than the particles of the other wrought aluminum alloys, and (b) physically separating the mixture thus obtained by moving said mixture of flat particles in a generally longitudinal flow path along a vibrating separator table, thereby causing said particles to enter in substantially single file a rapidly changing magnetic field separation zone in which the magnetic field moves across the separator table in a direction generally perpendicular to the particle flow path, and providing the table with a slight lateral slope upwards in the direction of travel of the magnetic field, whereby the rapidly changing magnetic field moves the larger and more conductive particles laterally up the lateral slope, thereby forming on the table one flow path comprising the larger and more conductive particles laterally up the lateral slope, thereby forming on the table one flow path comprising the larger and more conductive particles containing said other wrought aluminum alloys and another path comprising the smaller and less conductive particles containing said aluminum-lithium alloy.
Claim 2
Independent Claim
211 words
A method of separating a mixture of aluminum-lithium alloy and other wrought aluminum alloys comprising the steps of: (a) crushing the mixture into the form of substantially flat particles in which the particles of aluminum-lithium alloy have generally smaller dimensions, smaller density values and smaller conductivity values than the particles of the other wrought aluminum alloys, and (b) physically separating the mixture thus obtained by moving said mixture of flat particles in a generally longitudinal flow path along a vibrating separator table, thereby causing said particles to enter in substantially single file a rapidly changing magnetic field separation zone in which the magnetic field moves across the separator table in a direction generally perpendicular to the particle flow path, and providing the table with a slight lateral slope upwards in the direction of travel of the magnetic field, whereby the rapidly changing magnetic field moves the larger and more conductive particles laterally up the lateral slope, thereby forming on the table one flow path comprising the larger and more conductive particles laterally up the lateral slope, thereby forming on the table one flow path comprising the larger and more conductive particles containing said other wrought aluminum alloys and another path comprising the smaller and less conductive particles containing said aluminum-lithium alloy.
Claim 3
Dependent Claim
28 words
The method according to claim 1 which comprises heat treating the mixture of metal alloys, thereby reducing fracture toughness of the aluminum-lithium alloy prior to crushing the mixture.
Claim 4
Dependent Claim
20 words
The method according to claim 2 wherein the crushing step comprises flattening the particles by passing them through a roller-crusher.
Claim 5
Dependent Claim
20 words
The method according to claim 3 which comprises shredding the heat treated alloy mixture prior to passing through the roller-crusher.
Claim 6
Dependent Claim
22 words
The method according to claim 2 which comprises moving the metal alloy flat particles along the separator table in a single layer.
Claim 7
Dependent Claim
38 words
The method according to claim 1 which comprises forming the rapidly changing magnetic field by permanent magnets moving in a path parallel to the separator table and perpendicular to the flow path of the particles along the table.
Claim 8
Dependent Claim
12 words
The method according to claim 6 wherein the slope is from 1°-10°.
Claim 9
Independent Claim
200 words
A method of separating a mixture of aluminum-lithium alloy and other wrought aluminum alloys, said aluminum-lithium alloy having smaller density values and smaller conductivity values that the other wrought aluminum alloys, comprising the steps of: (a) crushing the mixture into the form of substantially flat particles in which the particles of aluminum-lithium alloy have generally smaller dimensions than the particles of the other wrought aluminum alloys, and (b) physically separating the mixture thus obtained by moving said mixture of flat particles in a generally longitudinal flow path along a vibrating separator table, causing said particles to enter as separate discrete particles a rapidly changing magnetic field separation zone in which the magnetic field moves across the separator table in a direction generally perpendicular to the particle flow path, and providing the table with a slight lateral slope upwards in the direction of travel of the magnetic field, whereby the rapidly changing magnetic field moves the larger and more conductive particles laterally up the lateral slope, thereby forming on the table one flow path comprising the larger and more conductive particles containing said other wrought aluminum alloys and another path comprising the smaller and less conductive particles containing said aluminum-lithium alloy.
Claim 10
Independent Claim
200 words
A method of separating a mixture of aluminum-lithium alloy and other wrought aluminum alloys, said aluminum-lithium alloy having smaller density values and smaller conductivity values that the other wrought aluminum alloys, comprising the steps of: (a) crushing the mixture into the form of substantially flat particles in which the particles of aluminum-lithium alloy have generally smaller dimensions than the particles of the other wrought aluminum alloys, and (b) physically separating the mixture thus obtained by moving said mixture of flat particles in a generally longitudinal flow path along a vibrating separator table, causing said particles to enter as separate discrete particles a rapidly changing magnetic field separation zone in which the magnetic field moves across the separator table in a direction generally perpendicular to the particle flow path, and providing the table with a slight lateral slope upwards in the direction of travel of the magnetic field, whereby the rapidly changing magnetic field moves the larger and more conductive particles laterally up the lateral slope, thereby forming on the table one flow path comprising the larger and more conductive particles containing said other wrought aluminum alloys and another path comprising the smaller and less conductive particles containing said aluminum-lithium alloy.
References Cited (Backward Citations)
US3430870A
Cited
US3605243A
Cited
US4330090A
Cited
SU1139506A1
Cited
US4491473A
Cited
EP0154207A1
Cited
DE3416504A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-10-28 | 1995-04-29 | 1995-10-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-10-28 | 1999-04-29 | 1999-10-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-10-28 | 2003-04-29 | 2003-10-29 | $7700.00 | Window Closed / Lapsed |