Preparation of flexible polyurethane foams having low compressive strength and block polyoxypropylenepolyoxyethylenepolyol mixtures which can be used for this purpose
Assignee: BASF SE
•
Filing: 1990-11-28
•
Granted: 1991-10-22
•
Expires: 2010-11-28
Abstract
Abstract Flexible polyurethane foams having low compressive strength and relatively good tensile strength are prepared by reacting a) a block polyoxypropylenepolyoxyethylenepolyol mixture which has a hydroxyl number of from 14 to 65, contains from 2 to 9% by weight, based on the weight of the polyoxypropylene units, of ethylene oxide units bonded in the terminal position and is prepared by anionic polymerization of the alkylene oxides with an initiator mixture having an average functionality of from 2.3 to 2.8 and consisting of water and glycerol and/or trimethylolpropane, or a mixture of these block polyoxypropylenepolyoxyethylenepolyol mixtures with bi- and/or trifunctional polyoxypropylenepolyoxyethylenepolyols having a hydroxyl number of from 20 to 70, and b) if required, low molecular weight chain extenders with c) organic and/or modified organic polyisocyanates in the presence of d) catalysts, e) blowing agents, preferably water, and if required, f) assistants and/or additives.
Inventors
- 👤 Heinz-Dieter Lutter
- 👤 Werner Hinz
- 👤 Walter Decker
- 👤 Reinhard Leppkes
- 👤 Erhard Reich
- 👤 Reinhard Peters
- 👤 Volker Haase
- 👤 Michael Lugmayr
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 18:44
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/48; C08G18/4833; C08G18/4837; C08G18/4841; C08G65/00; C08G65/02; C08G65/26; C08G65/2618; C08G65/2621; C08G65/2624; C08G2110/00; C08G2110/0008; C08G2110/0083; Y; Y10; Y10S; Y10S521/00; Y10S521/914
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
140 words
A process for the preparation of a flexible polyurethane foam having low compressive strength by reacting a) bifunctional or polyfunctional polyoxyalkylenepolyols and b) if required, low molecular weight chain extenders with c) organic and/or modified organic polyisocyanates, in the presence of d) catalysts, e) blowing agents and, if required, f) assistants and/or additives, wherein the polyoxyalkylenepolyols (a) used are a block polyoxypropylenepolyoxyethylenepolyol mixture which has a hydroxyl number of from 14 to 65, contains from 2 to 9% by weight, based on the weight of the polyoxypropylene units, of ethylene oxide units bonded in the terminal position, and was prepared by anionic polymerization, at elevated temperatures, of 1,2-propylene oxide with an initiator mixture having an average functionality of from 2.3 to 2.8 and consisting of water and glycerol and/or trimethylolpropane, and polymerization of ethylene oxide with the resulting polyoxypropylene adduct.
Claim 2
Dependent Claim
140 words
A process for the preparation of a flexible polyurethane foam having low compressive strength by reacting a) bifunctional or polyfunctional polyoxyalkylenepolyols and b) if required, low molecular weight chain extenders with c) organic and/or modified organic polyisocyanates, in the presence of d) catalysts, e) blowing agents and, if required, f) assistants and/or additives, wherein the polyoxyalkylenepolyols (a) used are a block polyoxypropylenepolyoxyethylenepolyol mixture which has a hydroxyl number of from 14 to 65, contains from 2 to 9% by weight, based on the weight of the polyoxypropylene units, of ethylene oxide units bonded in the terminal position, and was prepared by anionic polymerization, at elevated temperatures, of 1,2-propylene oxide with an initiator mixture having an average functionality of from 2.3 to 2.8 and consisting of water and glycerol and/or trimethylolpropane, and polymerization of ethylene oxide with the resulting polyoxypropylene adduct.
Claim 3
Dependent Claim
160 words
A two-stage process for the preparation of a flexible polyurethane foam having low compressive strength, wherein 1. in a first reaction stage, 1,2-propylene oxide is polymerized with an initiator mixture having an average functionality of from 2.3 to 2.8 and consisting of water and glycerol and/or trimethylolpropane, in the presence of at least one basic catalyst, at elevated temperatures, and ethylene oxide is polymerized with the resulting polyoxypropylene adduct, in an amount such that the resulting block polyoxypropylenepolyoxyethylenepolyol mixture has a hydroxyl number of from 14 to 65 and contains from 2 to 9% by weight, based on the weight of the polyoxypropylene units, of ethylene oxide units bonded in the terminal position, and 2. in a second reaction stage, a) the resulting block polyoxypropylenepolyoxyethylenepolyol mixture and b) if required, low molecular weight chain extenders are reacted with c) organic and/or modified organic polyisocyanates in the presence of d) catalysts, e) blowing agents and, if required, f) assistants and/or additives.
Claim 4
Dependent Claim
160 words
A two-stage process for the preparation of a flexible polyurethane foam having low compressive strength, wherein 1. in a first reaction stage, 1,2-propylene oxide is polymerized with an initiator mixture having an average functionality of from 2.3 to 2.8 and consisting of water and glycerol and/or trimethylolpropane, in the presence of at least one basic catalyst, at elevated temperatures, and ethylene oxide is polymerized with the resulting polyoxypropylene adduct, in an amount such that the resulting block polyoxypropylenepolyoxyethylenepolyol mixture has a hydroxyl number of from 14 to 65 and contains from 2 to 9% by weight, based on the weight of the polyoxypropylene units, of ethylene oxide units bonded in the terminal position, and 2. in a second reaction stage, a) the resulting block polyoxypropylenepolyoxyethylenepolyol mixture and b) if required, low molecular weight chain extenders are reacted with c) organic and/or modified organic polyisocyanates in the presence of d) catalysts, e) blowing agents and, if required, f) assistants and/or additives.
Claim 5
Dependent Claim
48 words
A process as claimed in claims 1 or 2, wherein the block polyoxypropylenepolyoxyethylenepolyol mixture has a hydroxyl number of from 14 to 40 and contains from 3 to 8% by weight, based on the weight of the polyoxypropylene units, of ethylene oxide units bonded in the terminal position.
Claim 6
Dependent Claim
42 words
A process as claimed in claims 1 or 2, wherein the initiator mixture for the preparation of the block polyoxypropylenepolyoxyethylenepolyol mixture consists of a mixture of water and glycerol and/or water and trimethylolpropane in a molar ratio of from 2.3:1 to 1:4.
Claim 7
Dependent Claim
35 words
A process as claimed in claims 1 or 2 wherein the initiator mixture for the preparation of the block polyoxypropylenepolyoxyethylenepolyol mixture consists of a water/glycerol mixture in a molar ratio of from 2.3:1 to 1:4.
Claim 8
Dependent Claim
148 words
A process as claimed in claim 1, wherein the bifunctional or polyfunctional polyoxyalkylenepolyols (a) used are a mixture which contains, based on the total weight of (a), ai) from 10 to 60% by weight of a block polyoxypropylenepolyoxyethylenepolyol mixture which has a hydroxyl number of from 14 to 40, contains from 3 to 8% by weight, based on the weight of the polyoxypropylene units, of ethylene oxide units bonded in the terminal position and was prepared by anionic polymerization, at elevated temperatures, of 1,2-propylene oxide with an initiator mixture having an average functionality of from 2.3 to 2.7 and consisting of water and glycerol and trimethylolpropane or of water and glycerol or trimethylolpropane, and polymerization of ethylene oxide with the resulting polyoxypropylene adduct, and aii) from 40 to 90% by weight of at least one bi- and/or trifunctional polyoxypropylenepolyoxyethylenepolyol having a hydroxyl number of from 20 to 70.
Claim 9
Dependent Claim
112 words
A process as claimed in claims 1 or 2, wherein the organic or modified organic polyisocyanates or organic and modified organic polyisocyanates (c) used are: mixtures of diphenylmethane 4,4'- and 2,4'-diisocyanate, mixtures of diphenylmethane diisocyanates and polyphenylenepolymethylene polyisocyanates containing not less than 35% by weight, based on the total weight, of diphenylmethane diisocyanates, mixtures of diphenylmethane 4,4'- and 2,4'-diisocyanate and mixtures of toluylene 2,4- and 2,6-diisocyanate, mixtures of diphenylmethane diisocyanates and polyphenylpolymethylene polyisocyanates and mixtures of toluylene 2,4- and 2,6-diisocyanates, urethane-containing polyisocyanate mixtures having an NCO content of from 28 to 14% by weight, based on the total weight, and derived from diphenylmethane diisocyanates, or mixtures of diphenylmethane diisocyanates and polyphenylpolymethylene polyisocyanates.
Claim 10
Dependent Claim
38 words
A process as claimed in claims 1 or 2, wherein water is used as the blowing agent (e), in an amount of from 0.1 to 8 parts by weight per 100 parts by weight of the polyoxyalkylenepolyols (a).
Claim 11
Dependent Claim
89 words
A novel block polyoxypropylenepolyoxyethylenepolyol mixture which has a hydroxyl number of from 14 to 65, contains from 2 to 9% by weight, based on the weight of the polyoxypropylene units, of ethylene oxide units bonded in the terminal position and is prepared by anionic polymerization, at elevated temperatures, of 1,2-propylene oxide with an initiator mixture having an average functionality of from 2.3 to 2.8 and consisting of water and glycerol and trimethylolpropane or of water and glycerol and trimethylolpropane, and polymerization of ethylene oxide with the resulting polyoxypropylene adduct.
Claim 12
Dependent Claim
89 words
A novel block polyoxypropylenepolyoxyethylenepolyol mixture which has a hydroxyl number of from 14 to 65, contains from 2 to 9% by weight, based on the weight of the polyoxypropylene units, of ethylene oxide units bonded in the terminal position and is prepared by anionic polymerization, at elevated temperatures, of 1,2-propylene oxide with an initiator mixture having an average functionality of from 2.3 to 2.8 and consisting of water and glycerol and trimethylolpropane or of water and glycerol and trimethylolpropane, and polymerization of ethylene oxide with the resulting polyoxypropylene adduct.
Claim 13
Dependent Claim
55 words
A novel polyoxyalkylenepolyol mixture containing ai) from 10 to 60% by weight of a block polyoxypropylenepolyoxyethylenepolyol mixture as claimed in claim 9 and aii) from 40 to 90% by weight of at least one bi- and/or trifunctional polyoxypropylenepolyoxyethylenepolyol having a hydroxyl number of from 20 to 70, the percentages being based on the total weight.
References Cited (Backward Citations)
US4385133A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-10-21 | 1995-04-22 | 1995-10-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-10-21 | 1999-04-22 | 1999-10-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-10-21 | 2003-04-22 | 2003-10-22 | $7700.00 | Window Closed / Lapsed |