Method of reducing critical current density of oxide superconductors by radiation damage
Assignee: Nokia Bell Labs
•
Filing: 1988-03-29
•
Granted: 1991-10-01
•
Expires: 2008-03-29
Abstract
Abstract The critical current density J c of a superconductive oxide film can be tailored, without substantial change in the critical temperature T c (R═0), by introduction of radiation damage into the superconductor. Exemplarily, this is done by exposure to energetic (e.g., 1 MeV) ions. The ability to tailor J c permits optimization of SQUIDS and other thin film devices, and makes it possible to produce superconductive interconnects that comprise "fuses" or current limiters.
Inventors
- 👤 Kenneth T. Short
- 👤 Alice E. White
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:13
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/01; H10N60/0884; H10N60/0912; H10N60/0941; Y; Y10; Y10S; Y10S505/00; Y10S505/70; Y10S505/701; Y10S505/702; Y10S505/725; Y10S505/73
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
206 words
Method of producing an article comprising a layer of superconductive oxide on a substrate, associated with at least a part of the superconductive oxide layer being a critical current density J cf , the method comprising a) forming the layer of superconductive oxide on the substrate; and b) providing means for making electrical contact with the layer characterized in that c) associated with the at least part of the layer formed in step a) is an initial critical current density J ci , and a critical temperature T c (R=0), with J ci >J cf ; and the method comprises d) exposing the at least part of the oxide layer to a flux of particles, with the particle species, energy, and fluence selected such that the critical current density of the at least part of the oxide layer is reduced to J cf with the normalized change ΔT c in T c (R=0) being less than 0.2 of the normalized change ΔJ c in J c , where ΔT c =(T cf -T ci )/T cf and ΔJ c =(J ci -J cf )/J ci , and T ci and T cf are the initial and final value of the critical temperature T c (R=0), respectively.
Claim 2
Dependent Claim
206 words
Method of producing an article comprising a layer of superconductive oxide on a substrate, associated with at least a part of the superconductive oxide layer being a critical current density J cf , the method comprising a) forming the layer of superconductive oxide on the substrate; and b) providing means for making electrical contact with the layer characterized in that c) associated with the at least part of the layer formed in step a) is an initial critical current density J ci , and a critical temperature T c (R=0), with J ci >J cf ; and the method comprises d) exposing the at least part of the oxide layer to a flux of particles, with the particle species, energy, and fluence selected such that the critical current density of the at least part of the oxide layer is reduced to J cf with the normalized change ΔT c in T c (R=0) being less than 0.2 of the normalized change ΔJ c in J c , where ΔT c =(T cf -T ci )/T cf and ΔJ c =(J ci -J cf )/J ci , and T ci and T cf are the initial and final value of the critical temperature T c (R=0), respectively.
Claim 3
Dependent Claim
65 words
The method of claim 1, wherein the superconductive oxide is a (La)-cuprate, (Ba)-cuprate, or (Bi)-cuprate, wherein step d) is carried out such that a nuclear energy between about 0.02 and about 0.4 eV/atom is deposited in the at least part of the oxide layer, and wherein the normalized change in T c (R=0) is at most 20% of the normalized change in T c .
Claim 4
Dependent Claim
22 words
The method of claim 2, wherein the particles are ions selected from the group consisting of He, O, F, Ne, and Ar.
Claim 5
Dependent Claim
24 words
The method of claim 1, wherein J cf ≲0.5J ci , and wherein the change in T c (R=0) is at most about 10%.
Claim 6
Dependent Claim
65 words
The method of claim 1, wherein the article comprises a SQUID, the at least part of the oxide layer comprising a superconductive weak link, and wherein J cf is selected such that 2I o L/Φ o is approximately equal to 1, where I o is the critical current through the weak link, L is the SQUID self-inductance, and Φ o is the fundamental flux quantum.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-30 | 1995-04-01 | 1995-10-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-30 | 1999-04-01 | 1999-10-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-30 | 2003-04-01 | 2003-10-01 | $7700.00 | Window Closed / Lapsed |