High strength, heat-resistant aluminum-based alloys
Assignee: MASUMOTO TSUYOSHI (1/3)
•
Filing: 1989-04-28
•
Granted: 1991-10-01
•
Expires: 2009-04-28
Abstract
Abstract The present invention provides high strength, heat resistant aluminum-based alloys having a composition represented by the general formula, Al a M b X c wherein: M is at least one metal element selected from the group consisting of V, Cr, Mn, Fe, Co, Ni, Cu, Zr, Ti, Mo, W, Ca, Li, Mg, and Si; X is at least one metal element selected from the group consisting of Y, La, Ce, Sm, Nd, Hf, Nb, Ta and Mm (misch metal); and a, b and c are atomic percentages falling within the following ranges: 50≦a≦95, 0.5≦b≦35 and 0.5≦c≦25, the aluminum-based alloy being in an amorphous state, microcrystalline state or a composite state thereof. The aluminum-based alloys possess an advantageous combination of properties of high strength, heat resistance, superior ductility and good processability which make them suitable for various applications.
Inventors
- 👤 Tsuyoshi Masumoto
- 👤 Akihisa Inoe
- 👤 Katsumasa Odera
- 👤 Masahiro Oguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 18:21
CPC Classifications
C; C22; C22C; C22C21/00; C22C45/00; C22C45/08
Claims Analysis
Total Claims: 62
Claim 1
Independent Claim
115 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.dl M.sub.2d2 M.sub.3d3 Mm.sub.c' X".sub.C" wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; M 3 is at least one metal element selected from the group consisting of Mn, Cu, W, Ca and Li; X" is at least one metal element selected from the group consisting of Y, Ta, Nb and Hf; and a, d1, d2, d3, c' and c" are atomic percentages falling within the following ranges: 5≦ a≦95, 0.5≦b=d1+d2+d3≦35 and 0.5≦c=c'+c"≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 2
Dependent Claim
115 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.dl M.sub.2d2 M.sub.3d3 Mm.sub.c' X".sub.C" wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; M 3 is at least one metal element selected from the group consisting of Mn, Cu, W, Ca and Li; X" is at least one metal element selected from the group consisting of Y, Ta, Nb and Hf; and a, d1, d2, d3, c' and c" are atomic percentages falling within the following ranges: 5≦ a≦95, 0.5≦b=d1+d2+d3≦35 and 0.5≦c=c'+c"≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 3
Dependent Claim
47 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.b Mm.sub.c wherein: a, b and c are atomic percentages falling within the following ranges: 50≦a≦95, 0.5 ≦b≦35 and 0.5≦c≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 4
Dependent Claim
47 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.b Mm.sub.c wherein: a, b and c are atomic percentages falling within the following ranges: 50≦a≦95, 0.5 ≦b≦35 and 0.5≦c≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 5
Dependent Claim
69 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.b Mm.sub.c' X".sub.c" wherein : X" is at least one metal element selected from the group consisting of Y, Hf, Nb and Ta; and a, b, c' and c" are atomic percentages falling within the following ranges: 50≦a≦95, 0.5 ≦b≦35 and 0.5≦c=c'+c"≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 6
Dependent Claim
69 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.b Mm.sub.c' X".sub.c" wherein : X" is at least one metal element selected from the group consisting of Y, Hf, Nb and Ta; and a, b, c' and c" are atomic percentages falling within the following ranges: 50≦a≦95, 0.5 ≦b≦35 and 0.5≦c=c'+c"≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 7
Dependent Claim
46 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a3 Fe.sub.b3 Ce.sub.c3 wherein: a3, b3 and c3 are atomic percentages falling within the following ranges: 66≦a3≦95, 0.5≦b3≦9 and 2.5≦c3≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 8
Dependent Claim
46 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a3 Fe.sub.b3 Ce.sub.c3 wherein: a3, b3 and c3 are atomic percentages falling within the following ranges: 66≦a3≦95, 0.5≦b3≦9 and 2.5≦c3≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 9
Dependent Claim
47 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a4 Fe.sub.b4 Ce.sub.c4 wherein: a4, b4 and c4 are atomic percentages falling within the following ranges: 5≦ a4≦90.5, 9≦b4≦35 and 0.5≦c4≦25 wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 10
Dependent Claim
47 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a4 Fe.sub.b4 Ce.sub.c4 wherein: a4, b4 and c4 are atomic percentages falling within the following ranges: 5≦ a4≦90.5, 9≦b4≦35 and 0.5≦c4≦25 wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 11
Dependent Claim
48 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a9 Fe.sub.b9 Ce.sub.e1 Y.sub.e2 wherein: a9, b9, e1 and e2 are atomic percentages falling within the following ranges: 66≦a9≦95, 0.5≦b9≦9 and 3.5≦e1+e2≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 12
Dependent Claim
48 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a9 Fe.sub.b9 Ce.sub.e1 Y.sub.e2 wherein: a9, b9, e1 and e2 are atomic percentages falling within the following ranges: 66≦a9≦95, 0.5≦b9≦9 and 3.5≦e1+e2≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 13
Dependent Claim
47 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a10 Fe.sub.b10 Ce.sub.e'1 Y.sub.e'2 wherein: a10, b10, e'1 and e'2 are atomic percentages falling within the following ranges: 50≦a10≦90.5,9≦b10≦35 and 0.5≦e'1+e'2≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 14
Dependent Claim
47 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a10 Fe.sub.b10 Ce.sub.e'1 Y.sub.e'2 wherein: a10, b10, e'1 and e'2 are atomic percentages falling within the following ranges: 50≦a10≦90.5,9≦b10≦35 and 0.5≦e'1+e'2≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 15
Dependent Claim
72 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.b' M.sub.2b" Mm.sub.c wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; and a, b', b" and c are atomic percentages falling within the following ranges: 50≦a≦95, 0.5≦b=b'+b"≦35 and 0.5≦c≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 16
Dependent Claim
72 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.b' M.sub.2b" Mm.sub.c wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; and a, b', b" and c are atomic percentages falling within the following ranges: 50≦a≦95, 0.5≦b=b'+b"≦35 and 0.5≦c≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 17
Dependent Claim
90 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.b' M.sub.2b" Mm.sub.c' X".sub.c" wherein: is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; X" is at least one metal element selected from the group consisting of Y, Ta, Hf, and Nb; and a, b', b", c' and c" are atomic percentages falling within the following ranges: 50≦a≦95, 0.5≦b=b'+b"≦35 and 0.5≦c=c'+c"≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 18
Dependent Claim
90 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.b' M.sub.2b" Mm.sub.c' X".sub.c" wherein: is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; X" is at least one metal element selected from the group consisting of Y, Ta, Hf, and Nb; and a, b', b", c' and c" are atomic percentages falling within the following ranges: 50≦a≦95, 0.5≦b=b'+b"≦35 and 0.5≦c=c'+c"≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 19
Dependent Claim
92 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.b' M.sub.3b" x.sub.2c wherein: M 3 is at least one metal element selected from the group consisting of Mn, Cu, W, Ca and Li; X 2 is at least one metal element selected from the group consisting of Y, La, Ce, Sm, Nd, Hf, Nb, and Ta; and a, b', b" and c are atomic percentages falling within the following ranges: 50≦a≦95, 0.5≦b=b'+b"≦35 and 0.5≦c≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 20
Dependent Claim
92 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.b' M.sub.3b" x.sub.2c wherein: M 3 is at least one metal element selected from the group consisting of Mn, Cu, W, Ca and Li; X 2 is at least one metal element selected from the group consisting of Y, La, Ce, Sm, Nd, Hf, Nb, and Ta; and a, b', b" and c are atomic percentages falling within the following ranges: 50≦a≦95, 0.5≦b=b'+b"≦35 and 0.5≦c≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 21
Dependent Claim
69 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.b' M.sub.3b" Mm.sub.c wherein: M 3 is at least one metal element selected from the group consisting of Mn, Cu, W, Ca and Li; and a, b', b" and c are atomic percentages falling within the following ranges: 50≦a≦95, 0.5≦b=b'+b"≦35 and 0.5≦c≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 22
Dependent Claim
69 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.b' M.sub.3b" Mm.sub.c wherein: M 3 is at least one metal element selected from the group consisting of Mn, Cu, W, Ca and Li; and a, b', b" and c are atomic percentages falling within the following ranges: 50≦a≦95, 0.5≦b=b'+b"≦35 and 0.5≦c≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 23
Dependent Claim
89 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.b' M.sub.3b" Mm.sub.c' X".sub.c" wherein: M 3 is at least one metal element selected from the group consisting of Mn, Cu, W, Ca and Li; X" is at least one metal element selected from the group consisting of Y, Ta, Nb and Hf; and a, b', b", c' and c" are atomic percentages falling within the following ranges: 50≦a≦95, 0.5≦b=b'+b"≦35 and 0.5≦c=c'+c"≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 24
Dependent Claim
89 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.b' M.sub.3b" Mm.sub.c' X".sub.c" wherein: M 3 is at least one metal element selected from the group consisting of Mn, Cu, W, Ca and Li; X" is at least one metal element selected from the group consisting of Y, Ta, Nb and Hf; and a, b', b", c' and c" are atomic percentages falling within the following ranges: 50≦a≦95, 0.5≦b=b'+b"≦35 and 0.5≦c=c'+c"≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 25
Dependent Claim
72 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a5 Fe.sub.b'5 M.sub.2b"5 Y.sub.c5 wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; and a5, b'5, b"5 and c5 are atomic percentages falling within the following ranges: 66.5≦a5≦95, 0.5≦b'5≦8.6,0<b"5≦34.5, and 3.5<c5≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 26
Dependent Claim
72 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a5 Fe.sub.b'5 M.sub.2b"5 Y.sub.c5 wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; and a5, b'5, b"5 and c5 are atomic percentages falling within the following ranges: 66.5≦a5≦95, 0.5≦b'5≦8.6,0<b"5≦34.5, and 3.5<c5≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 27
Dependent Claim
73 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a6 Fe.sub.b'6 M.sub.2b"6 Y.sub.c6 wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; and a6, b'6, b"6 and c6 are atomic percentages falling within the following ranges: 50≦a6≦91, 8.6<b'6<35, 0<b"6<26.5, and 0.5≦c6≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 28
Dependent Claim
73 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a6 Fe.sub.b'6 M.sub.2b"6 Y.sub.c6 wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; and a6, b'6, b"6 and c6 are atomic percentages falling within the following ranges: 50≦a6≦91, 8.6<b'6<35, 0<b"6<26.5, and 0.5≦c6≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 29
Dependent Claim
73 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a7 Fe.sub.b'7 M.sub.2b"7 Ce.sub.c7 wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, ti, Mo and Si; and a7, b'7, b"7 and c7 are atomic percentages falling within the following ranges: 66.5≦a7≦94, 0.5 ≦b'7≦8.6,0<b"7≦34.5, and 2.2<c7≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 30
Dependent Claim
73 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a7 Fe.sub.b'7 M.sub.2b"7 Ce.sub.c7 wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, ti, Mo and Si; and a7, b'7, b"7 and c7 are atomic percentages falling within the following ranges: 66.5≦a7≦94, 0.5 ≦b'7≦8.6,0<b"7≦34.5, and 2.2<c7≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 31
Dependent Claim
72 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a8 Fe.sub.b'8 M.sub.2b"8 Ce.sub.c8 wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; and A8, b'8, b"8 and c8 are atomic percentages falling within the following ranges: 50≦a8<90.9, 8.6<b'8<35,0<b"8≦26.5 and 0.5≦c8≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 32
Dependent Claim
72 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a8 Fe.sub.b'8 M.sub.2b"8 Ce.sub.c8 wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; and A8, b'8, b"8 and c8 are atomic percentages falling within the following ranges: 50≦a8<90.9, 8.6<b'8<35,0<b"8≦26.5 and 0.5≦c8≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 33
Dependent Claim
59 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a11 Fe.sub.b11 M.sub.2b'11 Ce.sub.e3 Y.sub.e4 wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; and a11, b11, b'11, e3 and e4 are atomic percentages falling within the following ranges:
Claim 34
Dependent Claim
59 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a11 Fe.sub.b11 M.sub.2b'11 Ce.sub.e3 Y.sub.e4 wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; and a11, b11, b'11, e3 and e4 are atomic percentages falling within the following ranges:
Claim 35
Dependent Claim
15 words
5≦a11≦94, 0.5≦b11≦8.6,0<b'11≦34.5 and 3.5<e3+e4≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 36
Dependent Claim
15 words
5≦a11≦94, 0.5≦b11≦8.6,0<b'11≦34.5 and 3.5<e3+e4≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 37
Dependent Claim
73 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a12 Fe.sub.b12 M.sub.2b'12 Ce.sub.e'3 Y.sub.e'4 wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; and a12, b12, b12', e'3 and e'4 are atomic percentages falling within the following ranges: 50≦a12<90.9,8.6<b12<35,0<b'12≦26.5 and 0.5≦e'3+e'4≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 38
Dependent Claim
73 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a12 Fe.sub.b12 M.sub.2b'12 Ce.sub.e'3 Y.sub.e'4 wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; and a12, b12, b12', e'3 and e'4 are atomic percentages falling within the following ranges: 50≦a12<90.9,8.6<b12<35,0<b'12≦26.5 and 0.5≦e'3+e'4≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 39
Dependent Claim
117 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.d1 M.sub.2d2 M.sub.3d3 X.sub.2c wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; M 3 is at least one metal element selected from the group consisting of Mn, Cu, W, Ca and Li; X 2 is at least one metal element selected from the group consisting of Y, La, Ce, Sm, Nd, Hf, Nb and Ta; and a, d1, d2, d3 and c are atomic percentages falling within the following ranges: 5≦ a≦95,0.5≦b=d1+d2+d3≦35 and 0.5≦c≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 40
Dependent Claim
117 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.d1 M.sub.2d2 M.sub.3d3 X.sub.2c wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; M 3 is at least one metal element selected from the group consisting of Mn, Cu, W, Ca and Li; X 2 is at least one metal element selected from the group consisting of Y, La, Ce, Sm, Nd, Hf, Nb and Ta; and a, d1, d2, d3 and c are atomic percentages falling within the following ranges: 5≦ a≦95,0.5≦b=d1+d2+d3≦35 and 0.5≦c≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 41
Dependent Claim
92 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.dl M.sub.2d2 M.sub.3d3 Mm.sub.c wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; M 3 is at least one metal element selected from the group consisting of Mn, Cu, W, Ca and Li; and a, d1, d2, d3 and c are atomic percentages falling within the following ranges: 50≦a≦95,0.5≦b=d1+d2+d3≦35and 0.5≦c≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 42
Dependent Claim
92 words
A high strength, heat resistant aluminum-based alloy having a composition represented by the general formula: Al.sub.a Fe.sub.dl M.sub.2d2 M.sub.3d3 Mm.sub.c wherein: M 2 is at least one metal element selected from the group consisting of V, Cr, Co, Ni, Zr, Ti, Mo and Si; M 3 is at least one metal element selected from the group consisting of Mn, Cu, W, Ca and Li; and a, d1, d2, d3 and c are atomic percentages falling within the following ranges: 50≦a≦95,0.5≦b=d1+d2+d3≦35and 0.5≦c≦25, wherein said aluminum-based alloy is composed of a microcrystalline composite structure.
Claim 43
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 1, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 44
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 2, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 45
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 3, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 46
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 4, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 47
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 5, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 48
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 6, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 49
Dependent Claim
35 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 7, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline matrix phase and a stable or metasable intermetallic phase.
Claim 50
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 8, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 51
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 9, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 52
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 10, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrysalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 53
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 11, in which said microcrysalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 54
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 12, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 55
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 13, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 56
Dependent Claim
35 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 14, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline matrix phase and a stable or metastable intermetallic phase.
Claim 57
Dependent Claim
35 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 15, in which microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 58
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 16, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystlline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 59
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 17, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 60
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 18, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 61
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 19, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
Claim 62
Dependent Claim
36 words
A high-strength, heat resistant aluminum-based alloy as claimed in claim 20, in which said microcrystalline composite structure consists of an aluminum matrix solid solution, a microcrystalline aluminum matrix phase and a stable or metastable intermetallic phase.
References Cited (Backward Citations)
US4435213A
Cited
US4743317A
Cited
DE3524276A1
Cited
JPS62250148A
Cited
JPS62250147A
Cited
GB2196647A
Cited
GB2196646A
Cited
EP0289835A1
Cited
US4787943A
Cited
EP0303100A1
Cited
US4909867A
Cited
US4851193A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-30 | 1995-04-01 | 1995-10-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-30 | 1999-04-01 | 1999-10-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-30 | 2003-04-01 | 2003-10-01 | $7700.00 | Window Closed / Lapsed |