Process for producing phosphor
Assignee: Futaba Corp
•
Filing: 1990-11-23
•
Granted: 1991-09-24
•
Expires: 2010-11-23
Abstract
Abstract A phosphor producing process capable of providing a phosphor of good quality in a reduced period of time. A Li compound acting as a doping agent is added prior to primary calcination so that it may also act as a flux and removed by washing prior to secondary calcination. A ZnO.Ga2O3 solid solution thus obtained is activated in the secondary calcination using an atmosphere in which reducing gas and Zn gas are mixed. Thus, a ZnO.Ga2O3:Li, P phosphor is which the molar ratio between Zn and Ga2O3 is 1:1 and of which crystals exhibit good surface conditions can be produced in a reduced period of time.
Inventors
- 👤 Hitoshi Toki
- 👤 Yoshitaka Satoh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:36
CPC Classifications
C; C09; C09K; C09K11/00; C09K11/08; C09K11/62; C09K11/621; C09K11/623
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
149 words
A process for producing a ZnO·Ga 2 O 3 :Li phosphor comprising the steps of: mixing equimolar amounts of ZnO and Ga 2 O 3 and a Li compound in an amount which is in excess of that which is to be incorporated into phosphor to prepare a mixture; calcining said mixture in an air atmosphere at a temperature of no more than 1200° C. for three hours, to thereby form a solid solution; pulverizing said solid solution; washing said pulverized solid solution with nitric acid to remove excess Li compound; calcining said washed solid solution in a H 2 and N 2 reducing and Zn gas atmosphere at about 1100° C. so as to activate said washed solid solution, to thereby form said ZnO·Ga 2 O 3 :Li phosphor; and classifying said ZnO·Ga 2 O 3 :Li phosphor so as to effect a phosphor of uniform particle size.
Claim 2
Dependent Claim
149 words
A process for producing a ZnO·Ga 2 O 3 :Li phosphor comprising the steps of: mixing equimolar amounts of ZnO and Ga 2 O 3 and a Li compound in an amount which is in excess of that which is to be incorporated into phosphor to prepare a mixture; calcining said mixture in an air atmosphere at a temperature of no more than 1200° C. for three hours, to thereby form a solid solution; pulverizing said solid solution; washing said pulverized solid solution with nitric acid to remove excess Li compound; calcining said washed solid solution in a H 2 and N 2 reducing and Zn gas atmosphere at about 1100° C. so as to activate said washed solid solution, to thereby form said ZnO·Ga 2 O 3 :Li phosphor; and classifying said ZnO·Ga 2 O 3 :Li phosphor so as to effect a phosphor of uniform particle size.
Claim 3
Dependent Claim
22 words
A process as defined in claim 1, wherein said ZnO, Ga 2 O 3 and Li compound are subjected to dry mixing.
Claim 4
Dependent Claim
33 words
A process as defined in claim 1, wherein said Li compound is selected from the group consisting of Li 3 PO 4 lithium halide, lithium carbonate, lithium nitrate, lithium hydroxide and lithium sulfate.
Claim 5
Dependent Claim
30 words
A process as defined in claim 1, wherein said Li compound is mixed in an amount of 5×10 -1 mol based on 1 mole of ZnO·Ga 2 O 3 .
Claim 6
Dependent Claim
62 words
A process as defined in claim 1, wherein said solid solution is activated by placing said solid solution and ZnO in an oven maintained in said H and N 2 reducing gas atmosphere and calcining said ZnO in said oven, thereby produce Zn gas from the ZnO to cover said solid solution together with said H 2 and N 2 reducing gas.
Claim 7
Dependent Claim
44 words
A process as defined in claim 5, wherein said ZnO is placed at a position ahead of said solid solution in relation to flow of said reducing gas in said oven which position is at a temperature of between 1000° C. and 1070° C.
Claim 8
Dependent Claim
44 words
A process as defined in claim 1, wherein said solid solution is activated by placing said solid solution in an oven into which Zn gas produced by decomposing an organic zinc compound is introduced together with said H 2 and N 2 reducing gas.
Claim 9
Dependent Claim
15 words
A process as defined in claim 7, wherein said organic zinc compound is diethyl zinc.
Claim 10
Dependent Claim
15 words
A process as defined in claim 7, wherein said organic zinc compound is dimethyl zinc.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-23 | 1995-03-25 | 1995-09-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-23 | 1999-03-25 | 1999-09-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-23 | 2003-03-25 | 2003-09-24 | $7700.00 | Window Closed / Lapsed |