Ethylene/polycyclic monomer copolymer, process for preparation thereof, and optical article

Claim 2

A random copolymer which comprises recurring units from ethylene and recurring units from a polycyclic monomer represented by the following general formula (I): ##STR18## wherein e, m, and n are 0 or 1, p is an integer of at least 0, R 1 , R 2 , R 3 , and R 4 independently represent a hydrogen atom or an alkyl group having 1 to 10 carbon atoms, and R 3 and R 4 may together form a ring; the molar ratio of ethylene/polycyclic monomer of the general formula (I) is in the range of from 90/10 to 10/90; a substantial part of the units derived from the polycyclic monomer represented by general formula (I) have a structure represented by general formula (II): ##STR19## wherein e, m, n, p, R 1 , R 2 , R 3 and R 4 are as defined above; and the intrinsic viscosity (η) of the random copolymer is 0.1 to 15 dl/g, as measured at 135° C. in decalin.

Claim 3

A random copolymer as set forth in claim 1, wherein the polycyclic monomer is a pentacyclo(10.2.1.1 5 ,8.0 2 ,11.0 4 ,9)hexadec-6-ene represented by general formula (III): ##STR20## wherein e and n are 0 or 1, R 1 , R 2 , R 3 , and R 4 independently represent a hydrogen atom or an alkyl group having 1 to 10 carbon atoms, and R 3 and R 4 may together form a ring; and a substantial part of the units derived from the polycyclic monomer represented by general formula (III) have a structure represented by general formula (IV): ##STR21## wherein e, n, R 1 , R 2 , R 3 and R 4 are as defined above.

Claim 4

A random copolymer as set forth in claim 2, which consists essentially of recurring units of ethylene and recurring units from the pentacyclo(10.2.1.1 5 ,8.0 2 ,11.0 4 ,9) hexadec-6-ene represented by general formula (III).

Claim 5

A random copolymer as set forth in claim 2, which consists essentially of recurring units from ethylene, recurring units from the polycyclic monomer represented by general formula (III), and recurring units from at least one monomer selected from the group consisting of α-olefins having 3 to 10 carbon atoms and cyclo-olefins having 5 to 18 carbon atoms, wherein the molar ration of ethylene/polycyclic monomer of general formula (III) is in the range of from 90/10 to 10/90; the molar ratio of the monomer selected from the group consisting of the α-olefins and cyclo-olefins to the polycyclic monomer represented by the general formula (III) is not higher than 90/10; and a substantial part of the units derived from the polycyclic monomer represented by general formula (III) have a structure represented by general formula (IV).

Claim 6

A process for the preparation of a random copolymer, which comprises copolymerizing ethylene with a polycyclic monomer represented by general formula (I): ##STR22## wherein e, m, and n are 0 or 1, p is an integer of at least 0, and R 1 , R 2 , R 3 , and R 4 independently represent a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, and R 3 and R 4 may together form a ring; in a hydrocarbon medium in the presence of a catalyst formed of a hydrocarbon-soluble vanadium compound and a halogen-containing organic aluminum compound to form a random copolymer in which the molar ratio of ethylene/polycyclic monomer represented by general formula (I) is in the range of from 90/10 to 10/90; and a substantial part of the units derived from the polycyclic monomer represented by general formula (I) have a structure represented by general formula (II): ##STR23## wherein e, m, n, p, R 1 , R 2 , R 3 and R 4 are as defined above; and the intrinsic viscosity (η) of the random copolymer is 0.1 to 15 dl/g, as measured at 135° C. in decalin.

Claim 7

A process for the preparation of a random copolymer, which comprises copolymerizing ethylene with a polycyclic monomer represented by general formula (I): ##STR22## wherein e, m, and n are 0 or 1, p is an integer of at least 0, and R 1 , R 2 , R 3 , and R 4 independently represent a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, and R 3 and R 4 may together form a ring; in a hydrocarbon medium in the presence of a catalyst formed of a hydrocarbon-soluble vanadium compound and a halogen-containing organic aluminum compound to form a random copolymer in which the molar ratio of ethylene/polycyclic monomer represented by general formula (I) is in the range of from 90/10 to 10/90; and a substantial part of the units derived from the polycyclic monomer represented by general formula (I) have a structure represented by general formula (II): ##STR23## wherein e, m, n, p, R 1 , R 2 , R 3 and R 4 are as defined above; and the intrinsic viscosity (η) of the random copolymer is 0.1 to 15 dl/g, as measured at 135° C. in decalin.

Claim 8

A process for the preparation of a random copolymer according to claim 5, wherein the polycyclic monomer is a pentacyclo (10.2.1.1 5 ,8.0 2 ,11.0 4 ,9) hexadec-6-ene represented by general formula (III): ##STR24## wherein e and n are 0 or 1, R 1 , R 2 , R 3 , and R 4 independently represent a hydrogen atom or an alkyl group having 1 to 10 carbon atoms, and R 3 and R 4 may together form a ring; and in the obtained copolymer, a substantial part of the units from said polycyclic monomer have a structure represented by general formula (IV): ##STR25## wherein e, n, R 1 , R 2 , R 3 and R 4 are as defined above.

Claim 9

A process for the preparation of a random copolymer according to claim 6, wherein a monomer mixture consisting essentially of ethylene and the pentacyclo((10.2.1.1 5 ,8.0 2 ,11.0 4 ,9)-hexadec-6-ene is copolymerized.

Claim 10

A process for the preparation of a random copolymer according to claim 6, wherein ethylene is copolymerized with a polycyclic monomer represented by general formula (III) and at least one monomer selected from the group consisting of α-olefins having 3 to 10 carbon atoms and cyclo-olefins having 5 to 18 carbon atoms to obtain a copolymer in which the molar ration of ethylene/polycyclic monomer represented by general formula (III) is in the range of from 90/10 to 10/90; the molar ratio of the monomer selected from the group consisting of the α-olefins and cyclo-olefins to the polycyclic monomer represented by general formula (III) is not higher than 90/10; and a substantial part of the units derived from the polycyclic monomer represented by general formula (III) have a structure represented by general formula (IV).

Claim 11

A process for the preparation of a random copolymer according to claim 5, wherein the hydrocarbon-soluble vanadium compound is selected from the group consisting of VCl 4 , VCl 3 , and compounds represented by the formula VO(OR) t X 3-t in which R represents an alkyl group having 1 to 10 carbon atoms, X represents a halogen atom and t is a number from 0 to 3; the halogen-containing organic aluminum compound is selected from the group consisting of compounds represented by R' u AlX' 3-u in which R' represents an alkyl group having 1 to 10 carbon atoms, X' represents a halogen atom and u is a positive number smaller than 3; the molar ratio of the vanadium compound to the organic aluminum compound is in the range of from 1 to 30; and the concentration of the vanadium compound in the hydrocarbon medium is 0.1 to 30 millimoles per liter.

Claim 12

An optical article comprising a molded body made of a random copolymer as set forth in claim 1.

Claim 13

An optical article comprising a molded body made of a random copolymer as set forth in claim 2.