US5049164A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Multilayer coated abrasive element for bonding to a backing
Assignee: Saint Gobain Abrasives Inc
•
Filing: 1990-01-05
•
Granted: 1991-09-17
•
Expires: 2010-01-05
Abstract
Abstract To prevent thermal stress from damaging a PCD or diamond, multilayer metal coatings for bonding polycrystalline diamond compacts and diamond crystals to a matrix comprise a first metal layer of a refractory metal, such as tungsten, a compliant metal layer of copper, and an outer metal layer of a refractory metal such as tungsten. Metallic bonding layers of a metal, such as nickel, are placed between the tungsten and copper layers for improved bonding. The method of manufacturing multilayer metal coatings comprises applying the inner metal layer by chemical vapor deposition, applying the first bonding layer metal by electrolytic deposition, applying the compliant layer metal by electrolytic deposition, applying the second bonding layer by electrolytic deposition and applying the outer layer by chemical vapor deposition. A superabrasive tool element comprises a coated diamond product bonded either to a matrix comprising tungsten carbide or iron powder or to a cemented tungsten carbide support.
Inventors
- 👤 Ralph M. Horton
- 👤 Royce A. Anthon
- 👤 James T. Hoggins
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 14:09
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; B; B22; B22F; B22F7/00; B22F7/06; C04B37/00; C04B37/02; C04B37/023; C04B37/026; C04B41/45; C04B41/52; C04B41/80; C04B41/81; C04B41/89; C09; C09K; C09K3/00; C09K3/14; C09K3/1436; C09K3/1445; C04B2235/00; C04B2235/65; C04B2235/656; C04B2235/6567; C04B2235/658; C04B2235/6582; C04B2237/00; C04B2237/02; C04B2237/12; C04B2237/122; C04B2237/123; C04B2237/124; C04B2237/125; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/343; C04B2237/36; C04B2237/361; C04B2237/363; C04B2237/365; C04B2237/40; C04B2237/401; C04B2237/405; C04B2237/406; C04B2237/407; C04B2237/50; C04B2237/52; C04B2237/59; C04B2237/592; C04B2237/61; C04B2237/70; C04B2237/704; C04B2237/708; C04B2237/72; C04B2237/76
Claims Analysis
Total Claims: 58
Claim 1
Independent Claim
181 words
A coated abrasive element for bonding at a surface thereof to a backing by means of a brazing or binder material comprising: a substrate material selected from the group consisting of single crystal diamond, polycrystalline diamond, polycrystalline cubic boron nitride, boron carbide, silicon carbide, alumina or combinations thereof; an inner layer of a metal or alloy coated on at least a portion of said substrate material, said inner metal layer being capable of reacting with said substrate material to form a bond therebetween; a compliant layer of a ductile metal or alloy coated on said inner layer, said compliant layer having a thickness sufficient to substantially prevent cracking of said polycrystalline element caused by the transfer of stress to said polycrystalline element during cooling after said coated abrasive element is bonded to said backing; and an outer layer of a metal or alloy coated on said compliant layer and having a melting point higher than said compliant layer, said outer layer being sufficiently thick so as to be substantially impervious to said brazing or binder material during bonding to said backing.
Claim 2
Dependent Claim
181 words
A coated abrasive element for bonding at a surface thereof to a backing by means of a brazing or binder material comprising: a substrate material selected from the group consisting of single crystal diamond, polycrystalline diamond, polycrystalline cubic boron nitride, boron carbide, silicon carbide, alumina or combinations thereof; an inner layer of a metal or alloy coated on at least a portion of said substrate material, said inner metal layer being capable of reacting with said substrate material to form a bond therebetween; a compliant layer of a ductile metal or alloy coated on said inner layer, said compliant layer having a thickness sufficient to substantially prevent cracking of said polycrystalline element caused by the transfer of stress to said polycrystalline element during cooling after said coated abrasive element is bonded to said backing; and an outer layer of a metal or alloy coated on said compliant layer and having a melting point higher than said compliant layer, said outer layer being sufficiently thick so as to be substantially impervious to said brazing or binder material during bonding to said backing.
Claim 3
Dependent Claim
38 words
An abrasive element of claim 1, wherein said substrate material is cubic boron nitride and said inner layer metal is selected from the group consisting of metals and alloys of group IVB, VB, VIB, VIIB, and VIIIB elements.
Claim 4
Dependent Claim
31 words
An abrasive element of claim 1, wherein said substrate material is single crystal or non-porous diamond and said inner layer metal is selected from the group consisting of titanium and chromium.
Claim 5
Dependent Claim
142 words
A coated abrasive element for bonding at a surface thereof to a backing by means of a brazing or binder material comprising: a polycrystalline element; an inner layer of a refractory metal or alloy coated on at least a portion of said polycrystalline element; a compliant layer of a ductile metal or alloy coated on said inner layer, said compliant layer having a thickness sufficient to substantially prevent cracking of said polycrystalline element caused by the transfer of stress to said polycrystalline element during cooling after said coated abrasive element is bonded to said backing; and an outer layer of a metal or alloy coated on said compliant layer and having a melting point higher than said compliant layer, said outer layer being sufficiently thick so as to be substantially impervious to said brazing or binder material during bonding to said backing.
Claim 6
Dependent Claim
142 words
A coated abrasive element for bonding at a surface thereof to a backing by means of a brazing or binder material comprising: a polycrystalline element; an inner layer of a refractory metal or alloy coated on at least a portion of said polycrystalline element; a compliant layer of a ductile metal or alloy coated on said inner layer, said compliant layer having a thickness sufficient to substantially prevent cracking of said polycrystalline element caused by the transfer of stress to said polycrystalline element during cooling after said coated abrasive element is bonded to said backing; and an outer layer of a metal or alloy coated on said compliant layer and having a melting point higher than said compliant layer, said outer layer being sufficiently thick so as to be substantially impervious to said brazing or binder material during bonding to said backing.
Claim 7
Dependent Claim
31 words
An abrasive element of claim 4, wherein said polycrystalline element comprises a material selected from the group consisting of polycrystalline diamond, polycrystalline cubic boron nitride, silicon carbide, alumina and combinations thereof.
Claim 8
Dependent Claim
26 words
An abrasive element of claim 4, wherein said compliant layer comprises a material selected from the group consisting of copper, gold, nickel, silver and alloys thereof.
Claim 9
Dependent Claim
34 words
An abrasive element of claim 4, wherein said inner layer comprises a material selected from the group consisting of group IVB metals, group VB metals, group VIB metals, group VIIIB metals and alloys thereof.
Claim 10
Dependent Claim
34 words
An abrasive element of claim 4, wherein said outer layer comprises a material selected from the group consisting of group IVB metals, group VB metals, group VIB metals, group VIIIB metals and alloys thereof.
Claim 11
Dependent Claim
34 words
An abrasive element of claim 4, wherein said inner layer and said outer layer are selected from the group consisting of tungsten, molybdenum, chromium, palladium, vanadium, titanium, zirconium, rhenium, niobium, tantalum and alloys thereof.
Claim 12
Dependent Claim
38 words
An abrasive element of claim 4, wherein said inner layer is sufficiently thick so as to substantially cover and seal a surface of said polycrystalline element and remain continuous when said abrasive element is bonded to said backing.
Claim 13
Dependent Claim
16 words
An abrasive element of claim 4, wherein said inner layer is at least 3 microns thick.
Claim 14
Dependent Claim
16 words
An abrasive element of claim 4, wherein said outer layer is at least 10 microns thick.
Claim 15
Dependent Claim
16 words
An abrasive element of claim 4, wherein said compliant layer is at least 10 microns thick.
Claim 16
Dependent Claim
63 words
An abrasive element of claim 4, further comprising at least one additional metal layer between said inner layer and said compliant layer or between said outer layer and said compliant layer, said additional metal layer consisting of a metal or metal alloy which is at least partially soluble in the materials which form the layers that are adjacent to said additional metal layer.
Claim 17
Dependent Claim
13 words
An abrasive element of claim 14, wherein said additional metal layer comprises nickel.
Claim 18
Dependent Claim
17 words
An abrasive element of claim 14, wherein said additional metal layer is at least 1 micron thick.
Claim 19
Dependent Claim
157 words
A coated abrasive element for bonding at a surface thereof to a backing by means of a brazing or binder material comprising: a polycrystalline diamond element; an inner layer of a carbide forming metal, said inner layer being adjacent to said polycrystalline diamond element and being sufficiently thick so as to substantially cover and seal a surface of said polycrystalline diamond element: a compliant layer of a ductile metal or alloy coated over said inner layer, said compliant layer being sufficiently thick so as to reduce the transfer of stress to said diamond element for preventing cracking of said diamond element during cooling after said coated abrasive element is bonded to said backing; and an outer layer of a metal or alloy coated over said compliant layer and having a melting point higher than that of said compliant layer, said outer layer being sufficiently thick so as to be substantially impervious during bonding to said binder material.
Claim 20
Dependent Claim
157 words
A coated abrasive element for bonding at a surface thereof to a backing by means of a brazing or binder material comprising: a polycrystalline diamond element; an inner layer of a carbide forming metal, said inner layer being adjacent to said polycrystalline diamond element and being sufficiently thick so as to substantially cover and seal a surface of said polycrystalline diamond element: a compliant layer of a ductile metal or alloy coated over said inner layer, said compliant layer being sufficiently thick so as to reduce the transfer of stress to said diamond element for preventing cracking of said diamond element during cooling after said coated abrasive element is bonded to said backing; and an outer layer of a metal or alloy coated over said compliant layer and having a melting point higher than that of said compliant layer, said outer layer being sufficiently thick so as to be substantially impervious during bonding to said binder material.
Claim 21
Dependent Claim
26 words
The abrasive element of claim 17, wherein said compliant layer comprises a material selected from the group consisting of copper, gold, nickel, silver and alloys thereof.
Claim 22
Dependent Claim
34 words
The abrasive element of claim 17, wherein said inner layer comprises a material selected from the group consisting of group IVB metals, group VB metals, group VIB metals, group VIIIB metals and alloys thereof.
Claim 23
Dependent Claim
34 words
The abrasive element of claim 17, wherein said outer layer comprises a material selected from the group consisting of group IVB metals, group VB metals, group VIB metals, group VIIIB metals and alloys thereof.
Claim 24
Dependent Claim
30 words
The abrasive element of claim 17, wherein said inner layer metal is selected from the group consisting of tungsten, molybdenum, chromium, vanadium, titanium, zirconium, rhenium, niobium, tantalum and alloys thereof.
Claim 25
Dependent Claim
30 words
The abrasive element of claim 17, wherein said outer layer metal is selected from the group consisting of tungsten, molybdenum, chromium, vanadium, titanium, zirconium, rhenium, niobium, tantalum and alloys thereof.
Claim 26
Dependent Claim
63 words
The abrasive element of claim 17, further including at least one additional metal layer between said inner layer and said compliant layer or between said outer layer and said compliant layer, said additional metal layer consisting of a metal or metal alloy which is at least partially soluble in the materials which form the layers that are adjacent to said additional metal layer.
Claim 27
Dependent Claim
225 words
An abrasive element for bonding at a surface thereof to a backing by means of a brazing or binder material comprising: a polycrystalline element; an inner layer of a refractory metal selected from the group consisting of tungsten, molybdenum, chromium, vanadium, titanium, zirconium, rhenium, niobium, tantalum and alloys thereof, said inner layer being coated on a surface of said polycrystalline element and being sufficiently thick so as to substantially cover and seal said surface of said polycrystalline element; a compliant layer of a refractory metal selected from the group consisting of copper, gold, nickel, silver and alloys thereof, said compliant layer being coated on said inner layer and being sufficiently thick so as to reduce the transfer of stress to said polycrystalline element; and an outer layer of a refractory metal selected from the group consisting of tungsten, molybdenum, chromium, vanadium, titanium, zirconium, rhenium, niobium, tantalum and alloys thereof, said outer layer being sufficiently thick so as to be substantially impervious during bonding to said brazing or binder material; and at least one additional metal layer between said inner layer and said compliant layer or between said outer layer and said compliant layer, said additional metal layer consisting of a metal or metal alloy which is at least partially soluble in the materials which form the layers that are adjacent to said additional metal layer.
Claim 28
Dependent Claim
225 words
An abrasive element for bonding at a surface thereof to a backing by means of a brazing or binder material comprising: a polycrystalline element; an inner layer of a refractory metal selected from the group consisting of tungsten, molybdenum, chromium, vanadium, titanium, zirconium, rhenium, niobium, tantalum and alloys thereof, said inner layer being coated on a surface of said polycrystalline element and being sufficiently thick so as to substantially cover and seal said surface of said polycrystalline element; a compliant layer of a refractory metal selected from the group consisting of copper, gold, nickel, silver and alloys thereof, said compliant layer being coated on said inner layer and being sufficiently thick so as to reduce the transfer of stress to said polycrystalline element; and an outer layer of a refractory metal selected from the group consisting of tungsten, molybdenum, chromium, vanadium, titanium, zirconium, rhenium, niobium, tantalum and alloys thereof, said outer layer being sufficiently thick so as to be substantially impervious during bonding to said brazing or binder material; and at least one additional metal layer between said inner layer and said compliant layer or between said outer layer and said compliant layer, said additional metal layer consisting of a metal or metal alloy which is at least partially soluble in the materials which form the layers that are adjacent to said additional metal layer.
Claim 29
Dependent Claim
45 words
An abrasive element of claim 24, wherein said inner layer is at least 3 microns thick, said compliant layer is at least 10 microns thick, said outer layer is at least 10 microns thick, and said additional metal layer is at least 1 micron thick.
Claim 30
Dependent Claim
27 words
An abrasive element of claim 24, wherein said inner and said outer layers comprise tungsten, said compliant layer comprises copper, and said additional metal layer comprises nickel.
Claim 31
Dependent Claim
87 words
A coated abrasive element for bonding at a surface thereof to a backing by means of a brazing material comprising: a polycrystalline element; an inner layer consisting of tungsten coated on at least a portion of said polycrystalline element; a compliant layer consisting of copper coated on said inner layer, said compliant layer having a thickness sufficient to substantially prevent cracking of said polycrystalline element caused by the transfer of stress to said polycrystalline element during cooling after said coated abrasive element is bonded to said backing.
Claim 32
Dependent Claim
87 words
A coated abrasive element for bonding at a surface thereof to a backing by means of a brazing material comprising: a polycrystalline element; an inner layer consisting of tungsten coated on at least a portion of said polycrystalline element; a compliant layer consisting of copper coated on said inner layer, said compliant layer having a thickness sufficient to substantially prevent cracking of said polycrystalline element caused by the transfer of stress to said polycrystalline element during cooling after said coated abrasive element is bonded to said backing.
Claim 33
Dependent Claim
114 words
A matrix bit comprising an abrasive element bonded to a matrix backing, wherein said abrasive element comprises a polycrystalline diamond element having a plurality of layers which coat a portion thereof, including an inner layer of a carbide forming metal adjacent to said polycrystalline diamond element, said inner layer being at least 3 microns thick; a compliant layer of a ductile metal or alloy, said compliant layer being at least 10 microns thick; and an outer layer of a metal or alloy with a melting point higher than said compliant layer, said outer layer being at least 10 microns thick; and said compliant layer being located between said outer layer and said inner layer.
Claim 34
Dependent Claim
114 words
A matrix bit comprising an abrasive element bonded to a matrix backing, wherein said abrasive element comprises a polycrystalline diamond element having a plurality of layers which coat a portion thereof, including an inner layer of a carbide forming metal adjacent to said polycrystalline diamond element, said inner layer being at least 3 microns thick; a compliant layer of a ductile metal or alloy, said compliant layer being at least 10 microns thick; and an outer layer of a metal or alloy with a melting point higher than said compliant layer, said outer layer being at least 10 microns thick; and said compliant layer being located between said outer layer and said inner layer.
Claim 35
Dependent Claim
112 words
A cutting tool comprising an abrasive element bonded to a matrix backing, wherein said abrasive element comprises polycrystalline diamond element having a plurality of layers which coat a portion thereof, including an inner layer of a carbide forming metal adjacent to said polycrystalline diamond, said inner layer being at least 3 microns thick; a compliant layer of a ductile metal or alloy, said compliant layer being at least 10 microns thick; and an outer layer of a metal or alloy with a melting point higher than said compliant layer, said outer layer being at least 10 microns thick; and said compliant layer being located between said outer layer and said inner layer.
Claim 36
Dependent Claim
112 words
A cutting tool comprising an abrasive element bonded to a matrix backing, wherein said abrasive element comprises polycrystalline diamond element having a plurality of layers which coat a portion thereof, including an inner layer of a carbide forming metal adjacent to said polycrystalline diamond, said inner layer being at least 3 microns thick; a compliant layer of a ductile metal or alloy, said compliant layer being at least 10 microns thick; and an outer layer of a metal or alloy with a melting point higher than said compliant layer, said outer layer being at least 10 microns thick; and said compliant layer being located between said outer layer and said inner layer.
Claim 37
Independent Claim
101 words
A method of forming a matrix backing onto a tungsten coated polycrystalline diamond abrasive element including the steps of: placing said abrasive element and a matrix forming metal powder in a mold, said matrix forming metal powder being selected from a group consisting of tungsten carbide, cemented tungsten carbide, iron powder, tungsten powder and cast tungsten carbide; melting and infiltrating a binder infiltrant through said matrix forming metal powder at a temperature below 1070° C., said binder comprising a copper based alloy composed of about 55-60% by weight copper, about 20% by weight manganese and about 20-25% by weight of zinc.
Claim 38
Independent Claim
101 words
A method of forming a matrix backing onto a tungsten coated polycrystalline diamond abrasive element including the steps of: placing said abrasive element and a matrix forming metal powder in a mold, said matrix forming metal powder being selected from a group consisting of tungsten carbide, cemented tungsten carbide, iron powder, tungsten powder and cast tungsten carbide; melting and infiltrating a binder infiltrant through said matrix forming metal powder at a temperature below 1070° C., said binder comprising a copper based alloy composed of about 55-60% by weight copper, about 20% by weight manganese and about 20-25% by weight of zinc.
Claim 39
Independent Claim
165 words
A method of forming a matrix backing onto a multicoated abrasive element including the steps of: forming a multicoated abrasive element by applying an inner metal layer to a polycrystalline diamond element, said inner metal layer consisting of a carbide forming metal; applying a compliant metal layer on said inner metal layer, said compliant layer consisting of a ductile metal or alloy; applying an outer metal layer on said compliant layer, said outer metal layer consisting of a refractory metal or alloy; placing said multicoated abrasive element and a matrix forming metal powder in a mold, said matrix forming metal powder being selected from a group consisting of tungsten carbide, cemented tungsten carbide, tungsten powder, iron powder, and cast tungsten carbide; melting and infiltrating a binder infiltrant through said matrix forming metal powder at a temperature below 1070° C., said binder comprising a copper based alloy composed of about 55-60% by weight copper, about 20% by weight manganese and about 20-25% by weight of zinc.
Claim 40
Independent Claim
165 words
A method of forming a matrix backing onto a multicoated abrasive element including the steps of: forming a multicoated abrasive element by applying an inner metal layer to a polycrystalline diamond element, said inner metal layer consisting of a carbide forming metal; applying a compliant metal layer on said inner metal layer, said compliant layer consisting of a ductile metal or alloy; applying an outer metal layer on said compliant layer, said outer metal layer consisting of a refractory metal or alloy; placing said multicoated abrasive element and a matrix forming metal powder in a mold, said matrix forming metal powder being selected from a group consisting of tungsten carbide, cemented tungsten carbide, tungsten powder, iron powder, and cast tungsten carbide; melting and infiltrating a binder infiltrant through said matrix forming metal powder at a temperature below 1070° C., said binder comprising a copper based alloy composed of about 55-60% by weight copper, about 20% by weight manganese and about 20-25% by weight of zinc.
Claim 41
Dependent Claim
25 words
The method of claim 31, wherein said compliant layer comprises a material selected from the group consisting of copper, gold, nickel, silver and alloys thereof.
Claim 42
Dependent Claim
33 words
The method of claim 31, wherein said inner layer comprises a material selected from the group consisting of group IVB metals, group VB metals, group VIB metals, group VIIIB metals and alloys thereof.
Claim 43
Dependent Claim
33 words
The method of claim 31, wherein said outer layer comprises a material selected from the group consisting of group IVB metals, group VB metals, group VIB metals, group VIIIB metals and alloys thereof.
Claim 44
Dependent Claim
32 words
The method of claim 31, wherein said inner layer comprises a material selected from the group consisting of tungsten, molybdenum, chromium, vanadium, tantalum, palladium, rhenium, titanium, zirconium, niobium, tantalum and alloys thereof.
Claim 45
Dependent Claim
32 words
The method of claim 31, wherein said outer layer comprises a material selected from the group consisting of tungsten, molybdenum, chromium, vanadium, titanium, tantalum, palladium, rhenium, zirconium, niobium, tantalum and alloys thereof.
Claim 46
Dependent Claim
34 words
The method of claim 31, wherein said inner layer is formed by chemical vapor deposition, said compliant layer is formed by electroplate deposition, and said outer metal layer is formed by chemical vapor deposition.
Claim 47
Independent Claim
189 words
A method of forming a matrix backing onto a multicoated abrasive element including the steps of: forming a multicoated abrasive element by applying an inner metal layer to a polycrystalline element, said inner layer metal being selected from the group consisting of tungsten, tantalum or molybdenum; applying to said inner metal layer a compliant metal layer consisting of a material selected from the group consisting of gold, copper, nickel, silver and alloys thereof; applying an outer metal layer on said compliant layer, said outer metal layer consisting of a metal selected from the group consisting of tungsten, tantalum, molybdenum, and alloys thereof; placing said multicoated abrasive element and a matrix forming metal powder in a mold, said matrix forming metal powder being selected from a group consisting of tungsten carbide, cemented tungsten carbide, tungsten powder, iron powder, and cast tungsten carbide; melting and infiltrating a binder infiltrant through said matrix forming metal powder at a temperature below 1070° C., said binder comprising a copper based alloy composed of about 55% to 60% by weight copper, about 20% by weight manganese and about 20% to 25% by weight of zinc.
Claim 48
Independent Claim
189 words
A method of forming a matrix backing onto a multicoated abrasive element including the steps of: forming a multicoated abrasive element by applying an inner metal layer to a polycrystalline element, said inner layer metal being selected from the group consisting of tungsten, tantalum or molybdenum; applying to said inner metal layer a compliant metal layer consisting of a material selected from the group consisting of gold, copper, nickel, silver and alloys thereof; applying an outer metal layer on said compliant layer, said outer metal layer consisting of a metal selected from the group consisting of tungsten, tantalum, molybdenum, and alloys thereof; placing said multicoated abrasive element and a matrix forming metal powder in a mold, said matrix forming metal powder being selected from a group consisting of tungsten carbide, cemented tungsten carbide, tungsten powder, iron powder, and cast tungsten carbide; melting and infiltrating a binder infiltrant through said matrix forming metal powder at a temperature below 1070° C., said binder comprising a copper based alloy composed of about 55% to 60% by weight copper, about 20% by weight manganese and about 20% to 25% by weight of zinc.
Claim 49
Dependent Claim
34 words
The method of claim 38, wherein said inner layer is formed by chemical vapor deposition, said compliant layer is formed by electroplate deposition, and said outer metal layer is formed by chemical vapor deposition.
Claim 50
Independent Claim
180 words
A method of forming an abrasive tool including the step of brazing a coated abrasive element to a support at a temperature between 600°-1070° C., wherein the braze is an alloy whose metal base is selected from the group consisting of copper, silver, gold or nickel, and said coated abrasive element comprises a polycrystalline diamond element having a plurality of layers which coat a portion thereof, including an inner layer of a metal selected from the group consisting of tungsten, molybdenum, chromium, vanadium, titanium, zirconium, niobium, tantalum, and alloys thereof, said inner layer being adjacent to said polycrystalline diamond and being at least 3 microns thick; an outer layer of a metal selected from the group consisting of tungsten, molybdenum, chromium, vanadium, titanium, zirconium, rhenium, niobium, tantalum, and alloys thereof, said outer layer being at least 10 microns thick; and a compliant layer of a ductile material selected from the group consisting of copper, gold, nickel, silver and alloys thereof; said compliant layer being located between said outer layer and said inner layer and being at least 10 microns thick.
Claim 51
Independent Claim
180 words
A method of forming an abrasive tool including the step of brazing a coated abrasive element to a support at a temperature between 600°-1070° C., wherein the braze is an alloy whose metal base is selected from the group consisting of copper, silver, gold or nickel, and said coated abrasive element comprises a polycrystalline diamond element having a plurality of layers which coat a portion thereof, including an inner layer of a metal selected from the group consisting of tungsten, molybdenum, chromium, vanadium, titanium, zirconium, niobium, tantalum, and alloys thereof, said inner layer being adjacent to said polycrystalline diamond and being at least 3 microns thick; an outer layer of a metal selected from the group consisting of tungsten, molybdenum, chromium, vanadium, titanium, zirconium, rhenium, niobium, tantalum, and alloys thereof, said outer layer being at least 10 microns thick; and a compliant layer of a ductile material selected from the group consisting of copper, gold, nickel, silver and alloys thereof; said compliant layer being located between said outer layer and said inner layer and being at least 10 microns thick.
Claim 52
Independent Claim
135 words
A method of forming an abrasive tool including the step of attaching a coated abrasive element to a support by means of brazing said coated abrasive element to said support at a temperature of less than 900° C., wherein said coated abrasive element comprises a polycrystalline diamond element having a plurality of layers which coat a portion thereof, including an inner layer of a metal selected from the group consisting of tungsten, molybdenum, chromium, vanadium, titanium, zirconium, niobium, tantalum, and alloys thereof, said inner layer being adjacent to said polycrystalline diamond and being at least 3 microns thick, and a compliant layer of a ductile material selected from the group consisting of copper, gold, nickel, silver and alloys thereof, said compliant layer being adjacent to said inner layer and being at least 10 microns thick.
Claim 53
Independent Claim
135 words
A method of forming an abrasive tool including the step of attaching a coated abrasive element to a support by means of brazing said coated abrasive element to said support at a temperature of less than 900° C., wherein said coated abrasive element comprises a polycrystalline diamond element having a plurality of layers which coat a portion thereof, including an inner layer of a metal selected from the group consisting of tungsten, molybdenum, chromium, vanadium, titanium, zirconium, niobium, tantalum, and alloys thereof, said inner layer being adjacent to said polycrystalline diamond and being at least 3 microns thick, and a compliant layer of a ductile material selected from the group consisting of copper, gold, nickel, silver and alloys thereof, said compliant layer being adjacent to said inner layer and being at least 10 microns thick.
Claim 54
Dependent Claim
21 words
The method of claim 41, wherein said brazing is done with a brazing material comprising silver or a silver based alloy.
Claim 55
Independent Claim
171 words
A method of forming a mosaic cutter comprising the steps of: placing a plurality of coated cutters into a mold assembly; placing a matrix powder into said mold over at least a portion of said plurality of cutters; and melting and infiltrating a binder infiltrant through said matrix powder, thereby bonding said matrix powder to said coated cutters; wherein said coated cutters comprise a polycrystalline diamond substrate, an inner layer of a carbide forming metal or alloy coated on at least a portion of said polycrystalline diamond, a compliant layer of a ductile metal or alloy coated on said inner layer, said compliant layer having a thickness sufficient to substantially prevent cracking of said polycrystalline diamond caused by the transfer of stress to said polycrystalline diamond during cooling after said infiltration, and an outer layer of a metal or alloy coated on said compliant layer and having a melting point higher than said compliant layer, said outer layer being sufficiently thick so as to be substantially impervious to said binder infiltrant.
Claim 56
Independent Claim
171 words
A method of forming a mosaic cutter comprising the steps of: placing a plurality of coated cutters into a mold assembly; placing a matrix powder into said mold over at least a portion of said plurality of cutters; and melting and infiltrating a binder infiltrant through said matrix powder, thereby bonding said matrix powder to said coated cutters; wherein said coated cutters comprise a polycrystalline diamond substrate, an inner layer of a carbide forming metal or alloy coated on at least a portion of said polycrystalline diamond, a compliant layer of a ductile metal or alloy coated on said inner layer, said compliant layer having a thickness sufficient to substantially prevent cracking of said polycrystalline diamond caused by the transfer of stress to said polycrystalline diamond during cooling after said infiltration, and an outer layer of a metal or alloy coated on said compliant layer and having a melting point higher than said compliant layer, said outer layer being sufficiently thick so as to be substantially impervious to said binder infiltrant.
Claim 57
Independent Claim
141 words
A method of forming a drill bit comprising the steps of: brazing a coated element to a cemented tungsten carbide support; and attaching said support to a bit; wherein, said coated element comprises a polycrystalline diamond substrate, an inner layer of a carbide forming metal or alloy coated on at least a portion of said polycrystalline diamond, a compliant layer of a ductile metal or alloy coated on said inner layer, said compliant layer having a thickness sufficient to substantially prevent cracking of said polycrystalline diamond caused by the transfer of stress to said polycrystalline diamond during cooling after said infiltration, and an outer layer of a metal or alloy coated on said compliant layer and having a melting point higher than said compliant layer, said outer layer being sufficiently thick so as to be substantially impervious to said binder infiltrant.
Claim 58
Independent Claim
141 words
A method of forming a drill bit comprising the steps of: brazing a coated element to a cemented tungsten carbide support; and attaching said support to a bit; wherein, said coated element comprises a polycrystalline diamond substrate, an inner layer of a carbide forming metal or alloy coated on at least a portion of said polycrystalline diamond, a compliant layer of a ductile metal or alloy coated on said inner layer, said compliant layer having a thickness sufficient to substantially prevent cracking of said polycrystalline diamond caused by the transfer of stress to said polycrystalline diamond during cooling after said infiltration, and an outer layer of a metal or alloy coated on said compliant layer and having a melting point higher than said compliant layer, said outer layer being sufficiently thick so as to be substantially impervious to said binder infiltrant.
References Cited (Backward Citations)
US4268276A
Cited
US4311489A
Cited
US4298356A
Cited
US4441894A
Cited
US4449989A
Cited
US4469489A
Cited
US4576612A
Cited
US4629473A
Cited
US4776863A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-16 | 1995-03-18 | 1995-09-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-16 | 1999-03-18 | 1999-09-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-16 | 2003-03-18 | 2003-09-17 | $7700.00 | Window Closed / Lapsed |