US5047188A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for preparation of modified methacrylic resin molding material
Assignee: Mitsubishi Chemical Corp
•
Filing: 1989-06-21
•
Granted: 1991-09-10
•
Expires: 2009-06-21
Abstract
Abstract Disclosed is a process for the preparation of a modified methacrylic resin molding material, wherein a volatile component is removed from a methacrylic polymer composition containing a volatile component including an unreacted monomer, a solvent or a by-product, and a modifying polymer is added to the methacrylic polymer composition to prepare a modified molding material. The removal of a volatile component from the methacrylic polymer composition and the addition and kneading of a modifying polymer into this polymer composition can be performed at a high efficiency by a process wherein a volatile component-removing extruder comprising a plurality of vent zones and a modifying polymer supply mechanism arranged upstream of the final vent zone but preferably downstream of the adjacent vent zone is used, the modifying polymer is fed from the modifying polymer supply mechanism and incorporated into the methacrylic polymer composition continuously flowing in the volatile component-removing extruder, and the volatile component is removed from the obtained mixture in the final vent zone and the mixture is then extruded.
Inventors
- 👤 Kazuya Okada
- 👤 Masahiro Taniguchi
- 👤 Yasunori Shimomura
- 👤 Hidemi Tanaka
- 👤 Tsutomu Matsui
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:00
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/005; B; B29; B29C; B29C48/00; B29C48/25; B29C48/36; B29C48/50; B29C48/76; C08F; C08F6/00; C08F6/06; C08F6/10; B29C48/03; B29C48/285; B29C48/29; B29K; B29K2105/00; B29K2105/0005
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
251 words
A process for the preparation of a modified methacrylic resin molding material in which volatile components are removed from a methacrylic polymer composition and the methacrylic polymer composition is mixed with a modifying polymer, which comprises: extruding said methacrylic polymer composition through a volatile component-removing extruder equipped with a plurality of vent zones from a first vent zone to a final vent zone, whereby the volatile components of unreacted monomer, solvent and by-product are vented from the extruder, and equipped with a screw type feeder modifying polymer supply means arranged between the final vent zone and the vent zone adjacent the final vent zone; and feeding modifying polymer into said extruder by means of said screw-type feeder and mixing said modifying polymer with said methacrylic polymer as the material continuously flows through said extruder, the venting of volatile components occurring through all vent zones and occurring as a mixture of polymer material is continuously extruded and said modifying polymer being at least one member selected from the group consisting of (i) a multi-stage polymer obtained by graft-polymerizing a vinyl monomer to an acrylic rubber, (ii) a polymer obtained by graft-polymerizing a vinyl monomer to a homopolymer or copolymer of butadiene as a rubber source, (iii) a quadripolymer comprising methyl methacrylate as the main component and styrene, α-methylstyrene and maleic anhydride as comonmer components, (iv) a terpolymer comprising methyl methacrylate as the main component and α-methylstyrene and cyclohexylmaleimide as comonomer components, (v) a methyl methacrylate/cyclohexylmaleimide copolymer, and (vi) a methyl methacrylate/N-phenylmaleimide copolymer.
Claim 2
Dependent Claim
251 words
A process for the preparation of a modified methacrylic resin molding material in which volatile components are removed from a methacrylic polymer composition and the methacrylic polymer composition is mixed with a modifying polymer, which comprises: extruding said methacrylic polymer composition through a volatile component-removing extruder equipped with a plurality of vent zones from a first vent zone to a final vent zone, whereby the volatile components of unreacted monomer, solvent and by-product are vented from the extruder, and equipped with a screw type feeder modifying polymer supply means arranged between the final vent zone and the vent zone adjacent the final vent zone; and feeding modifying polymer into said extruder by means of said screw-type feeder and mixing said modifying polymer with said methacrylic polymer as the material continuously flows through said extruder, the venting of volatile components occurring through all vent zones and occurring as a mixture of polymer material is continuously extruded and said modifying polymer being at least one member selected from the group consisting of (i) a multi-stage polymer obtained by graft-polymerizing a vinyl monomer to an acrylic rubber, (ii) a polymer obtained by graft-polymerizing a vinyl monomer to a homopolymer or copolymer of butadiene as a rubber source, (iii) a quadripolymer comprising methyl methacrylate as the main component and styrene, α-methylstyrene and maleic anhydride as comonmer components, (iv) a terpolymer comprising methyl methacrylate as the main component and α-methylstyrene and cyclohexylmaleimide as comonomer components, (v) a methyl methacrylate/cyclohexylmaleimide copolymer, and (vi) a methyl methacrylate/N-phenylmaleimide copolymer.
Claim 3
Dependent Claim
27 words
A process for the preparation of a modified methacrylic resin molding material according to claim 1, wherein the number of the vent zones is 2 to 6.
Claim 4
Dependent Claim
54 words
The process for the preparation of a modified methacrylic resin molding material according to claim 1, wherein the volatile component content of the methacrylic polymer composition in the extruder is controlled to a level below 5% by weight at the point where said modifying polymer is fed into said extruder through said screw-type feeder.
Claim 5
Dependent Claim
48 words
The process for the preparation of a modified methacrylic resin molding material according to claim 1, wherein the temperature of the first of said vent zones is within the range of 100° to about 250° C. and is at a pressure of about 500 to about 800 torr.
Claim 6
Dependent Claim
44 words
The process for the preparation of a modified methacrylic resin molding material according to claim 1, wherein the temperature of a second and a third of said vent zones ranges from about 220° to about 280° C. at a pressure lower than 700 torr.
References Cited (Backward Citations)
DE1454804A1
Cited
US3642752A
Cited
US3751527A
Cited
US3900453A
Cited
US3825515A
Cited
US3968090A
Cited
US3968059A
Cited
US4065532A
Cited
US3992500A
Cited
US4324868A
Cited
JPS58211434A
Cited
US4649005A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-09 | 1995-03-11 | 1995-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-09 | 1999-03-11 | 1999-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-09 | 2003-03-11 | 2003-09-10 | $7700.00 | Window Closed / Lapsed |