Forming twin wells in semiconductor devices
Assignee: STMicroelectronics Ltd Great Britain
•
Filing: 1990-03-30
•
Granted: 1991-09-03
•
Expires: 2010-03-30
Abstract
Abstract A method of forming a well of one conductivity type in a silicon substrate having a first surface region thereof which is doped with a dopant of one conductivity type and a second surface region thereof which is doped with a dopant of opposite conductivity type. The first and second regions are covered by respective first and second portions of an oxide layer which has been grown on the silicon substrate, the first portion being thicker than the second portion. The substrate is oxidized thereby to increase the thickness of the oxide layer such that the difference in thickness between the first and second portions is reduced. The substrate is also heated to cause diffusion of the dopant of one conductivity type thereby to form a well and of the dopant of opposite conductivity type down into the substrate. The heating step is carried out before, during or after the oxidizing step. The oxide layer is then removed thereby to expose the substrate surface which has a step of around 400 Angstroms in the region of the well boundary.
Inventors
- 👤 Martin J. Teague
- 👤 Andrew D. Strachan
- 👤 Martin A. Henry
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 04:51
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6302; H10P14/6304; H10P14/6306; H10P14/6308; H10P14/6309; H10D; H10D84/00; H10D84/01; H10D84/0123; H10D84/0126; H10D84/0165; H10D84/0191; H10D84/02; H10D84/03; H10D84/038; H10P14/6322; H10P30/00; H10P30/20; H10P30/22; H10P32/00; H10P32/10; H10P32/14; H10P32/1404; H10P32/1406; H10P32/17; H10P32/171; Y; Y10; Y10S; Y10S148/00; Y10S148/07
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
197 words
A method of forming a well of one conductivity type in a silicon substrate, which method comprises the steps of: (a) providing a silicon substrate having a first surface region thereof which is doped with a dopant of one conductivity type and a second surface region thereof which is doped with a dopant of opposite conductivity type, the first and second regions being covered by respective first and second portions of an oxide layer which has been grown on the silicon substrate, the first portion being thicker than the second portion; (b) oxidizing the substrate thereby to increase the thickness of the oxide layer such that the difference in thickness between the first and second portions is reduced; (c) heating the substrate to cause diffusion of the said dopant of one conductivity type thereby to form a well of said one conductivity type in the substrate and also diffusion of the said dopant of opposite conductivity type down into the substrate, the heating step being carried out before, during or after oxidizing step (b); and (d) removing the oxide layer thereby to expose the substrate surface which has a step in the region of the well boundary.
Claim 2
Independent Claim
197 words
A method of forming a well of one conductivity type in a silicon substrate, which method comprises the steps of: (a) providing a silicon substrate having a first surface region thereof which is doped with a dopant of one conductivity type and a second surface region thereof which is doped with a dopant of opposite conductivity type, the first and second regions being covered by respective first and second portions of an oxide layer which has been grown on the silicon substrate, the first portion being thicker than the second portion; (b) oxidizing the substrate thereby to increase the thickness of the oxide layer such that the difference in thickness between the first and second portions is reduced; (c) heating the substrate to cause diffusion of the said dopant of one conductivity type thereby to form a well of said one conductivity type in the substrate and also diffusion of the said dopant of opposite conductivity type down into the substrate, the heating step being carried out before, during or after oxidizing step (b); and (d) removing the oxide layer thereby to expose the substrate surface which has a step in the region of the well boundary.
Claim 3
Dependent Claim
35 words
A method according to claim 1, wherein the oxidising step (b) and the heating step (c) are carried out as a single step in which the oxidation and heating are performed in different ambient atmospheres.
Claim 4
Dependent Claim
20 words
A method according to claim 2 wherein the oxidising and heating steps are carried out at substantially the same temperature.
Claim 5
Dependent Claim
29 words
A method according to claim 2 wherein the oxidizing step (b) is carried out by heating the substrate in an oxidising atmosphere at a temperature of around 1200° C.
Claim 6
Dependent Claim
29 words
A method according to claim 3 wherein the oxidizing step (b) is carried out by heating the substrate in an oxidising atmosphere at a temperature of around 1200° C.
Claim 7
Dependent Claim
18 words
A method according to claim 4 wherein the oxidizing step (b) is carried out for about 30 minutes.
Claim 8
Dependent Claim
18 words
A method according to claim 5 wherein the oxidizing step (b) is carried out for about 30 minutes.
Claim 9
Dependent Claim
33 words
A method according to claim 1 wherein prior to oxidizing step (b) the first and second portions of the oxide layer have a thickness of around 3000 Angstroms and around 500 Angstroms respectively.
Claim 10
Dependent Claim
16 words
A method according to claim 1 wherein the height of the step is around 400 Angstroms.
Claim 11
Dependent Claim
16 words
A method according to claim 8 wherein the height of the step is around 400 Angstroms.
Claim 12
Dependent Claim
55 words
A method according to claim 1 wherein prior to step (a) the oxide layer is of substantially uniform thickness and the first portion of the oxide layer is formed by masking the second portion of the oxide layer with a masking layer and selectively growing oxide on the first surface region of the silicon substrate.
Claim 13
Dependent Claim
57 words
A method according to claim 1 wherein the dopant of opposite conductivity type is implanted into the second surface region of the silicon substrate after formation of the first and second portions of the oxide layer, the first portion of the oxide layer acting to mask the first surface region of the silicon substrate from dopant implantation.
Claim 14
Dependent Claim
23 words
A method according to claim 12 wherein the dopant of opposite conductivity type is implanted at an energy of 60 keV per ion.
Claim 15
Dependent Claim
31 words
A method according to claim 1 wherein the said second surface region of the silicon substrate is comprised in a pseudowell of opposite conductivity type to that of the said well.
Claim 16
Dependent Claim
23 words
A method according to claim 1 wherein the well boundary surrounds the first surface region which is lower than the second surface region.
Claim 17
Independent Claim
209 words
A method of forming a well of one conductivity type in a silicon substrate, which method comprises the steps of: (a) providing a silicon substrate having a first surface region thereof which is doped with a dopant of one conductivity type and a second surface region thereof which is doped with a dopant of opposite conductivity type, the first and second regions being covered by respective first and second portions of an oxide layer which has been grown on the silicon substrate, the first portion being greater than 800 Angstroms thicker than the second portion; (b) oxidizing the substrate thereby to increase the thickness of the oxide layer such that the difference in thickness between the first and second portions is reduced to around 800 Angstroms; (c) heating the substrate to cause diffusion of the said dopant of one conductivity type thereby to form a well of said one conductivity type in the substrate and also diffusion of the said dopant of opposite conductivity type down into the substrate, the heating step being carried out before, during or after oxidizing step (b); and (d) removing the oxide layer thereby to expose the substrate surface which has a step of around 400 Angstroms in the region of the well boundary.
Claim 18
Independent Claim
209 words
A method of forming a well of one conductivity type in a silicon substrate, which method comprises the steps of: (a) providing a silicon substrate having a first surface region thereof which is doped with a dopant of one conductivity type and a second surface region thereof which is doped with a dopant of opposite conductivity type, the first and second regions being covered by respective first and second portions of an oxide layer which has been grown on the silicon substrate, the first portion being greater than 800 Angstroms thicker than the second portion; (b) oxidizing the substrate thereby to increase the thickness of the oxide layer such that the difference in thickness between the first and second portions is reduced to around 800 Angstroms; (c) heating the substrate to cause diffusion of the said dopant of one conductivity type thereby to form a well of said one conductivity type in the substrate and also diffusion of the said dopant of opposite conductivity type down into the substrate, the heating step being carried out before, during or after oxidizing step (b); and (d) removing the oxide layer thereby to expose the substrate surface which has a step of around 400 Angstroms in the region of the well boundary.
Claim 19
Dependent Claim
23 words
A method according to claim 16, wherein before oxidising step (b) the first portion is around 2500 Angstroms thicker than the second portion.
Claim 20
Dependent Claim
19 words
A method according to claim 16 wherein the second portion of the oxide layer is around 500 Angstroms thick.
Claim 21
Dependent Claim
55 words
A method according to claim 18 wherein prior to step (a) the oxide layer is of substantially uniform thickness and the first portion of the oxide layer is formed by masking the second portion of the oxide layer with a masking layer and selectively growing oxide on the first surface region of the silicon substrate.
Claim 22
Dependent Claim
57 words
A method according to claim 19 wherein the dopant of opposite conductivity type is implanted into the second surface region of the silicon substrate after formation of the first and second portions of the oxide layer, the first portion of the oxide layer acting to mask the first surface region of the silicon substrate from dopant implantation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-02 | 1995-03-04 | 1995-09-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-02 | 1999-03-04 | 1999-09-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-02 | 2003-03-04 | 2003-09-03 | $7700.00 | Window Closed / Lapsed |