Silicate treatment of molecular sieve agglomerates
Assignee: Honeywell UOP LLC
•
Filing: 1990-07-25
•
Granted: 1991-09-03
•
Expires: 2010-07-25
Abstract
Abstract Molecular sieve agglomerates that can have improved physical and chemical properties are prepared by methods which comprise contacting the agglomerates with an alkali metal silicate solution. Molecular sieve agglomerates which comprise binders such as kaolin can additionally be contacted with an alkali hydroxide solution to convert the kaolin to Zeolite A prior to contacting the agglomerates with the alkali metal silicate solution to further improve properties. The molecular sieve agglomerates prepared according to the present invention are suitable for use as refrigerant desiccants.
Inventors
- 👤 Medhat K. Tannous
- 👤 John D. Sherman
- 👤 Alan P. Cohen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 11:16
CPC Classifications
B; B01; B01J; B01J20/00; B01J20/02; B01J20/10; B01J20/16; B01J20/18; B01J20/186; Y; Y10; Y10S; Y10S423/00; Y10S423/24
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
148 words
Method for preparing attrition resistant molecular sieve agglomerates comprising: (a) forming an initial molecular sieve agglomerate comprising a zeolite and a binder comprising kaolin clay; (b) heating the initial agglomerate at a temperature of from about 550°-650° C. and sufficient to set the binder and form a calcined agglomerate; (c) contacting said calcined agglomerate with an alkali hydroxide solution comprising from about 5 to about 50% by weight of sodium hydroxide at conditions effective to convert the kaolin binder to Zeolite A to form a converted agglomerate; (d) contacting the converted agglomerate with an aqueous alkali metal silicate solution containing from about 1 to 10 wt. % alkali metal oxide and from about 2 to 20 wt. % silicon dioxide to form a treated agglomerate; and (e) drying the treated agglomerate at a temperature of from about ambient temperature to 650° C. and sufficient to remove water therefrom.
Claim 2
Dependent Claim
148 words
Method for preparing attrition resistant molecular sieve agglomerates comprising: (a) forming an initial molecular sieve agglomerate comprising a zeolite and a binder comprising kaolin clay; (b) heating the initial agglomerate at a temperature of from about 550°-650° C. and sufficient to set the binder and form a calcined agglomerate; (c) contacting said calcined agglomerate with an alkali hydroxide solution comprising from about 5 to about 50% by weight of sodium hydroxide at conditions effective to convert the kaolin binder to Zeolite A to form a converted agglomerate; (d) contacting the converted agglomerate with an aqueous alkali metal silicate solution containing from about 1 to 10 wt. % alkali metal oxide and from about 2 to 20 wt. % silicon dioxide to form a treated agglomerate; and (e) drying the treated agglomerate at a temperature of from about ambient temperature to 650° C. and sufficient to remove water therefrom.
Claim 3
Dependent Claim
22 words
Method of claim 1 wherein said zeolite is the potassium-exchanged form of Zeolite A having uniform pore diameters of about 3 Angstroms.
Claim 4
Dependent Claim
22 words
Method of claim 1 wherein said zeolite is the sodium-exchanged form of Zeolite A having uniform pore diameters of about 4 Angstroms.
Claim 5
Dependent Claim
22 words
Method of claim 1 wherein the binder comprises from about 5 percent to about 40 percent by weight of said initial agglomerate.
Claim 6
Dependent Claim
12 words
Method of claim 1 wherein the alkali metal oxide is potassium oxide.
Claim 7
Dependent Claim
24 words
Method of claim 1 wherein said drying is conducted by heating in air to a temperature of from about 200° C. to 650° C.
Claim 8
Dependent Claim
22 words
Method of claim 1 wherein the alkali hydroxide solution comprises from about 5 to about 10 percent by weight of sodium hydroxide.
Claim 9
Dependent Claim
21 words
Method of claim 1 wherein said contacting is performed at a temperature of from about 40° C. to about 110° C.
Claim 10
Dependent Claim
21 words
Method of claim 8 wherein said contacting is performed at a temperature of from about 90° C. to about 95° C.
Claim 11
Dependent Claim
38 words
Method of claim 1 which further comprises contacting said converted agglomerate with a sufficient quantity of water to have a pH of between about 9 to about 12 prior to said contacting with the alkali metal silicate solution.
Claim 12
Dependent Claim
14 words
Method of claim 10 wherein the pH of the converted agglomerate is about 10.
References Cited (Backward Citations)
US3114603A
Cited
US3119660A
Cited
GB972833A
Cited
US3536521A
Cited
US3624003A
Cited
US3625866A
Cited
US4405503A
Cited
US4452909A
Cited
US4818508A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-02 | 1995-03-04 | 1995-09-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-02 | 1999-03-04 | 1999-09-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-02 | 2003-03-04 | 2003-09-03 | $7700.00 | Window Closed / Lapsed |