Process of three dimensional lithography in amorphous polymers
Assignee: United States Department of the Navy
•
Filing: 1989-11-29
•
Granted: 1991-08-27
•
Expires: 2009-11-29
Abstract
Abstract A process of three dimensional lithography in amorphous polymers to form an instantaneous, permanent image in the polymer by the steps of providing an undoped, non-crystalline layer or film of a polymer having a stable amorphous state under human operating conditions. The film is preferably poly(ethyleneterphthalate) (PET), poly(aryl-ether-ether-ketone) (PEEK), poly(chloro-trifluoroethylene) (Kel-F®), poly(carbonate) (ie LEXAN 9032®), poly(sulfone), poly(methylmethacrylate(PMMA, or LUCITE®), a poly(cyanurate) such as bisphenol A dicyanate, or an epoxy (eg. Epon 820®). The film can be either self supporting or mounted on a substrate. The film is then covered (and optionally contacted) with a mask which serves to block the radiation from impinging on where no marking is desired. If the mask is in actual contact with the film, it is capable of also acting as a heat sink. Next, the film is exposed through the mask to radiation of sufficient intensity to cause ablation of the exposed areas imparting a distinct, three-dimensional impression in the film. The film may then, for example, be processed by metalization and coating with a protective layer to form a finished product of an optical data storage disk.
Inventors
- 👤 Mark F. Sonnenschein
- 👤 Charles M. Roland
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:11
CPC Classifications
G; G11; G11B; G11B7/00; G11B7/24; G11B7/241; G11B7/242; G11B7/244; G11B7/245; G03; G03F; G03F7/00; G03F7/004; G03F7/039; G03F7/20; G11B7/26; Y; Y10; Y10S; Y10S430/00; Y10S430/145; Y10S430/146
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
86 words
A process of lithographically imprinting a three dimensional image in a polymer film comprising: (a) providing an undoped, amorphous film of a polymer having a stable amorphous state and a glass transition temperature that is higher than normal room temperature; (b) covering the amorphous film with a mask containing an image; (c) exposing the amorphous film through the mask to infrared radiation of sufficient strength to cause ablation of the exposed areas of the amorphous film thereby imparting a distinct, three-dimensional impression in the amorphous film.
Claim 2
Dependent Claim
86 words
A process of lithographically imprinting a three dimensional image in a polymer film comprising: (a) providing an undoped, amorphous film of a polymer having a stable amorphous state and a glass transition temperature that is higher than normal room temperature; (b) covering the amorphous film with a mask containing an image; (c) exposing the amorphous film through the mask to infrared radiation of sufficient strength to cause ablation of the exposed areas of the amorphous film thereby imparting a distinct, three-dimensional impression in the amorphous film.
Claim 3
Dependent Claim
31 words
The process according to claim 1 wherein the film is selected from the group consisting of poly(ethylene terephthalate) (PET), poly(aryl-ether-ether-ketone) (PEEK), poly(chloro-trifluoroethylene), poly(carbonate), poly(sulfone), poly(methylmethacrylate)(PMMA), a poly(cyanurate), or an amorphous epoxy.
Claim 4
Dependent Claim
16 words
The process according to claim 1 wherein the glass transition point is greater than 70° C.
Claim 5
Dependent Claim
17 words
The process according to claim 3 wherein the radiation exposure is greater than 1.8 watts/cm 2 .
Claim 6
Dependent Claim
18 words
The process according to claim 4 wherein the radiation exposure is between 3.5 and 10 watts/cm 2 .
Claim 7
Dependent Claim
20 words
The process to according to claim 4 wherein the film is exposed to radiation for between 10 and 100 seconds.
Claim 8
Dependent Claim
19 words
The process according to claim 6 wherein the film is exposed to radiation for between 10 and 30 seconds.
Claim 9
Dependent Claim
11 words
The process according to claim 6 wherein the film is poly(ethyleneterephthalate).
Claim 10
Dependent Claim
11 words
The process according to claim 6 wherein the film is poly(aryl-ether-ether-ketone).
Claim 11
Dependent Claim
11 words
The process according to claim 6 wherein the film is poly(chlorotrifluoroethylene).
Claim 12
Dependent Claim
13 words
The process according to claim 6 wherein the film is bisphenol A dicyanate.
Claim 13
Dependent Claim
12 words
The process according to claim 6 wherein the film is amorphous epoxy.
Claim 14
Dependent Claim
11 words
The process according to claim 6 wherein the film is poly(carbonate).
Claim 15
Dependent Claim
10 words
The process according to claim 6 the film is poly(sulfone).
Claim 16
Dependent Claim
11 words
The process according to claim 6 wherein the film is poly(methylmethacrylate).
Claim 17
Dependent Claim
57 words
The process according to claim 4 wherein the mask comprises a transparent portion and an opaque portion, an image formed in the opaque portion which permits radiation to pass through the opaque portion, the opaque portion is in contact with the film and the opaque portion acts as both a heat sink and a block for radiation.
Claim 18
Dependent Claim
38 words
The process according to claim 4 wherein the polymer film is covered but is not in contact with the mask, whereby the mask blocks radiation, but heat dissipation of the non-irradiated regions is achieved by ambient air cooling.
Claim 19
Dependent Claim
20 words
The process according to claim 4 wherein a metal layer is applied to the film after the impressions are formed.
Claim 20
Dependent Claim
26 words
The process according to claim 18 wherein the film is protected by a protective layer of an optically clear protective covering applied over the metal layer.
Claim 21
Dependent Claim
21 words
The process according to claim 6 wherein the film is on a supporting substrate which prevents the film from being distorted.
Claim 22
Dependent Claim
19 words
The process according to claim 20 wherein the film and the supporting substrate are formed from the same material.
Claim 23
Dependent Claim
20 words
The process according to claim 19 wherein the film and the protective layer are formed from the same polymeric material.
Claim 24
Dependent Claim
12 words
The process according to claim 16 wherein the opaque portion is gold.
Claim 25
Dependent Claim
27 words
The process of claim 1, wherein said amorphous film exists in a stable amorphous state throughout a range of temperatures extending from arctic temperatures to desert temperatures.
References Cited (Backward Citations)
US4486463A
Cited
US4975358A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-08-26 | 1995-02-25 | 1995-08-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-08-26 | 1999-02-25 | 1999-08-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-08-26 | 2003-02-25 | 2003-08-27 | $7700.00 | Window Closed / Lapsed |