Method for the production of electrically conducting, IR reflecting, fluorine-doped tin oxide layers on the surface of objects of glass or ceramic or of enamel coatings and a preparation for the application of such layers
Assignee: TH GOLDSCHMIDT AG GOLDSCHMIDTSTRASSE 100 4300 ESSEN 1 FEDERAL REPUBLIC OF GERMANY
•
Filing: 1990-03-12
•
Granted: 1991-08-27
•
Expires: 2010-03-12
Abstract
Abstract A method and composition are disclosed for the production of electrically conducting, IR reflecting, fluorine-doped tin oxide layers on surfaces of a glass or ceramic objects or of enamel coatings. The method comprises applying an organic solution of a mixture of alkyltin oxide and trifluoroacetic acid to the surface, which has been heated to 400° to 700° C., wherein trifluoroacetic acid is present in the solution in a substoichiometric amount. The composition useful for carrying out the method comprises an organic solution of alkyltin oxide and trifluoroacetic acid in a substoichiometric amount relative to the alkyltin oxide. Variable doping with fluorine and, with that, optimization of the surface resistance value as well as of the IR reflection become possible by means of the invention.
Inventors
- 👤 Erich Ruf
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 14:35
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/25; C03C17/253; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/211; C03C2217/24; C03C2217/241; C03C2218/00; C03C2218/10; C03C2218/11; C03C2218/112
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
93 words
A method for the production of electrically conducting, IR reflecting, fluorine-doped tin oxide layers free of any cloudiness on the surface of glass or ceramic objects or on enamel layers, by application of a clear organic solution of a mixture of alkyltin oxide and trifluoroacetic acid to the surface which has been heated to 400° to 700° C., comprising applying a solution of a mixture of alkyltin oxide and trifluoroacetic acid to the heated surface, wherein the trifluoroacetic acid is present in a substoichiometric amount in the solution relative to the alkyltin oxide.
Claim 2
Independent Claim
93 words
A method for the production of electrically conducting, IR reflecting, fluorine-doped tin oxide layers free of any cloudiness on the surface of glass or ceramic objects or on enamel layers, by application of a clear organic solution of a mixture of alkyltin oxide and trifluoroacetic acid to the surface which has been heated to 400° to 700° C., comprising applying a solution of a mixture of alkyltin oxide and trifluoroacetic acid to the heated surface, wherein the trifluoroacetic acid is present in a substoichiometric amount in the solution relative to the alkyltin oxide.
Claim 3
Dependent Claim
27 words
The method of claim 1, in which the alkyltin oxide in the solution is selected from monobutyl tin oxide, dibutyltin oxide, tributyltin oxide or a combination thereof.
Claim 4
Dependent Claim
84 words
The method of claim 1 in which the solution applied contains a mixture of alkyltin oxide and trifluoroacetic acid selected from the group consisting of a) monobutyltin oxide and trifluoroacetic acid in a molar ratio of monobutyltin oxide:trifluoroacetic acid ranging from 1:<3 to 1:0.15, b) dibutyltin oxide and trifluoroacetic acid in a molar ratio of dibutyltin oxide:trifluoroacetic acid ranging from 1 :<2 to 1:0.74 or c) tributyltin oxide and trifluoroacetic acid in a molar ratio of tributyltin oxide:trifluoroacetic acid ranging from 1:<2 to 1:0.15.
Claim 5
Dependent Claim
62 words
The method of claim 3, in which the solution applied contains a mixture of alkyltin oxide and trifluoroacetic acid selected from the group consisting of a) monobutyltin oxide:trifluoroacetic acid in a molar ratio of 1:<2 to 1:0.15, b) dibutyltin oxide:trifluoroacetic acid in a molar ratio of 1:<1.5 to 1:0.74 or c) tributyltin oxide:trifluoroacetic acid in a molar ratio of 1:<1.5 to 1:0.15.
Claim 6
Dependent Claim
22 words
The method of claim 1, in which the solution applied contains ethyl acetate, methyl ethyl ketone or a combination thereof as solvent.
Claim 7
Dependent Claim
40 words
The method of claim 1, in which said solution is produced by mixing alkyltin oxide, trifluoroacetic acid in a substoichiometric amount with respect to said alkyltin oxide and an organic solvent at ambient temperature until a clear solution is obtained.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-08-26 | 1995-02-25 | 1995-08-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-08-26 | 1999-02-25 | 1999-08-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-08-26 | 2003-02-25 | 2003-08-27 | $7700.00 | Window Closed / Lapsed |