High silicon, low carbon austemperable cast iron
Assignee: Applied Process Inc
•
Filing: 1990-04-27
•
Granted: 1991-08-27
•
Expires: 2010-04-27
Abstract
Abstract An austemperable cast iron which includes an ausferritic matrix, the cast iron having a silicon content of from about 1.6 to about 2.4 weight percent, and a carbon content of from about 1.6 to about 2.2 weight percent, such that the carbon equivalent of the cast iron is from about 2.1 to about 3.0 weight percent. The austempered cast iron is prepared by melting the cast iron composition; to about 1650°-1900° F. and maintaining the temperature of the casting at that temperature until substantially all of the eutectic carbide particles convert to temper graphite nodules to form a temper graphite-containing casting, then cooling the temper graphite-containing casting to about 1500°-1750° F. and maintaining the temperature of the tempered graphite-coating at about 1500°-1750° F. until a fully austenitic matrix is achieved, and then quenching and cooling the ausferritic matrix casting to room temperature before bainite is formed.
Inventors
- 👤 Bela V. Kovacs
- 👤 John R. Keough
- 👤 Douglas M. Pramstaller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 22:02
CPC Classifications
C; C21; C21D; C21D5/00; C22; C22C; C22C37/00; C22C37/10
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
91 words
An austemperable cast iron, comprising: an ausferritic matrix, the cast iron having a silicon content of from about 1.6 to about 2.4 weight percent and a carbon content of from about 1.6 to about 2.2 weight percent, such that the carbon equivalent of said cast iron shall be from about 2.1 to about 3.0 weight percent, the ausferritic matrix being formed prior to cooling the cast iron to room temperature and before a substantial amount of bainite is formed so that as little bainite as possible is incorporated into the matrix.
Claim 2
Dependent Claim
91 words
An austemperable cast iron, comprising: an ausferritic matrix, the cast iron having a silicon content of from about 1.6 to about 2.4 weight percent and a carbon content of from about 1.6 to about 2.2 weight percent, such that the carbon equivalent of said cast iron shall be from about 2.1 to about 3.0 weight percent, the ausferritic matrix being formed prior to cooling the cast iron to room temperature and before a substantial amount of bainite is formed so that as little bainite as possible is incorporated into the matrix.
Claim 3
Dependent Claim
16 words
The austemperable cast iron of claim 1, wherein said silicon content is about 1.8 weight percent.
Claim 4
Dependent Claim
16 words
The austemperable cast iron of claim 1, wherein said carbon content is about 2.0 weight percent.
Claim 5
Dependent Claim
15 words
The austemperable cast iron of claim 1, wherein said carbon equivalent is about 2.6 percent.
Claim 6
Dependent Claim
21 words
The austemperable cast iron of claim 1, further comprising a manganese content of from about 0.1 to about 0.8 weight percent.
Claim 7
Dependent Claim
18 words
The austemperable cast iron of claim 1, further comprising a manganese content of less than 0.3 weight percent.
Claim 8
Dependent Claim
103 words
An austemperable cast iron, comprising: an ausferritic matrix including a combination of acicular ferrite and stable austenite supersaturated with carbon, the cast iron having a silicon content of from about 1.6 to about 2.4 weight percent, and a carbon content of from about 1.6 to about 2.2 weight percent, such that the carbon equivalent of said cast iron shall be from about 2.1 to about 3.0 weight percent, the ausferritic matrix being formed prior to cooling the cast iron to room temperature and before a substantial amount of bainite is formed so that as little bainite as possible is incorporated into the matrix.
Claim 9
Dependent Claim
103 words
An austemperable cast iron, comprising: an ausferritic matrix including a combination of acicular ferrite and stable austenite supersaturated with carbon, the cast iron having a silicon content of from about 1.6 to about 2.4 weight percent, and a carbon content of from about 1.6 to about 2.2 weight percent, such that the carbon equivalent of said cast iron shall be from about 2.1 to about 3.0 weight percent, the ausferritic matrix being formed prior to cooling the cast iron to room temperature and before a substantial amount of bainite is formed so that as little bainite as possible is incorporated into the matrix.
Claim 10
Dependent Claim
102 words
An austemperable cast iron, comprising: an ausferritic matrix which includes a combination of acicular ferrite and stable austenite super saturated with carbon, the cast iron having a silicon content of about 1.8 weight percent, a carbon content of about 2.0 weight percent, and a manganese content of less than 0.3 weight percent, such that the carbon equivalent of the cast iron shall be about 2.6 weight percent, the ausferritic matrix being formed prior to cooling the cast iron to room temperature and before a substantial amount of bainite is formed so that as little bainite as possible is incorporated into the matrix.
Claim 11
Dependent Claim
102 words
An austemperable cast iron, comprising: an ausferritic matrix which includes a combination of acicular ferrite and stable austenite super saturated with carbon, the cast iron having a silicon content of about 1.8 weight percent, a carbon content of about 2.0 weight percent, and a manganese content of less than 0.3 weight percent, such that the carbon equivalent of the cast iron shall be about 2.6 weight percent, the ausferritic matrix being formed prior to cooling the cast iron to room temperature and before a substantial amount of bainite is formed so that as little bainite as possible is incorporated into the matrix.
Claim 12
Dependent Claim
69 words
An austemperable cast iron, comprising: an ausferritic matrix, the cast iron including a silicon content of nodular iron and a carbon content of malleable iron which forms a hybrid iron capable of being austempered, the ausferritic matrix being formed prior to cooling the cast iron to room temperature and before a substantial amount of bainite is formed so that as little bainite as possible is incorporated into the matrix.
Claim 13
Dependent Claim
69 words
An austemperable cast iron, comprising: an ausferritic matrix, the cast iron including a silicon content of nodular iron and a carbon content of malleable iron which forms a hybrid iron capable of being austempered, the ausferritic matrix being formed prior to cooling the cast iron to room temperature and before a substantial amount of bainite is formed so that as little bainite as possible is incorporated into the matrix.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-08-26 | 1995-02-25 | 1995-08-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-08-26 | 1999-02-25 | 1999-08-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-08-26 | 2003-02-25 | 2003-08-27 | $7700.00 | Window Closed / Lapsed |