Abstract
Abstract A lost positive pattern comprising an open-pored plastics substrate containing pores with an average width of from one to three millimeters is used, in which, after a negative pattern has been made, the voids which it, as a core, contains are filled with metal by casting and the negative pattern is removed. The production of the negative pattern is preceded by the following method steps in which once the substrate of plastics material has been cleaned, it is wetted throughout with a keying resin film which partially dissolves the structure of its surface and in which at least one coat of an auto-crosslinking two-pack silicone is applied onto and into the whole of the substrate of plastics material to thicken the walls and/or the interlinking webs of the porous substrate of plastics material.
Inventors
- 👤 Olaf Ahlers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 07:15
CPC Classifications
B; B22; B22D; B22D25/00; B22D25/02; A; A61; A61F; A61F2/00; A61F2/02; A61F2/30; A61F2/30767; A61F2/30771; A61L; A61L27/00; A61L27/02; A61L27/04; A61L27/50; A61L27/56; A61F2002/3092; A61F2/3094; A61F2/30942; A61F2002/30957
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
164 words
A method of producing open-called metal structures using a lost positive pattern comprising an open-pored substrate of plastics material having a structure of surfaces and containing pores with an average width of from 1 to 3 mm, in which method, after a negative pattern forming a core containing voids has been made, the voids are filled with metal by casting and the negative pattern is finally removed, said method comprising the steps of: a) cleaning the substrate of plastics material, b) wetting the substrate of plastics material throughout with a keying resin film which partially dissolves the structure of the surfaces of the substrate of plastics material, and c) applying at least one coat of auto-crosslinking two-pack silicone onto and into the whole of the open-pored substrate of plastics material whereby to thicken at least one of the walls and interlinking webs of said open-pored substrate of plastics material, wherein said steps (a) to (c) are performed before the negative pattern has been made.
Claim 2
Independent Claim
164 words
A method of producing open-called metal structures using a lost positive pattern comprising an open-pored substrate of plastics material having a structure of surfaces and containing pores with an average width of from 1 to 3 mm, in which method, after a negative pattern forming a core containing voids has been made, the voids are filled with metal by casting and the negative pattern is finally removed, said method comprising the steps of: a) cleaning the substrate of plastics material, b) wetting the substrate of plastics material throughout with a keying resin film which partially dissolves the structure of the surfaces of the substrate of plastics material, and c) applying at least one coat of auto-crosslinking two-pack silicone onto and into the whole of the open-pored substrate of plastics material whereby to thicken at least one of the walls and interlinking webs of said open-pored substrate of plastics material, wherein said steps (a) to (c) are performed before the negative pattern has been made.
Claim 3
Dependent Claim
36 words
The method according to claim 1, and comprising the additional step of: d) stiffening further the structure of surfaces of the substrate of plastics material by a two-pack polyurethane resin after cross-linking of the two-pack silicone.
Claim 4
Dependent Claim
16 words
The method according to claim 1, wherein the keying resin film comprises an unsaturated silicone resin.
Claim 5
Dependent Claim
16 words
The method according to claim 2, wherein the keying resin film comprises an unsaturated silicone resin.
Claim 6
Dependent Claim
21 words
The method according to claim 1, wherein the two-pack silicone is an unsaturated two-pack silicone rubber which cross-links at ambient temperature.
Claim 7
Dependent Claim
22 words
The method according to claim 2, wherein the two pack silicone is an unsaturated two-pack silicone rubber which cross-links at ambient temperature.
Claim 8
Dependent Claim
21 words
The method according to claim 3, wherein the two-pack silicone is an unsaturated two-pack silicone rubber which cross-links at ambient temperature.
Claim 9
Dependent Claim
53 words
The method according to claim 1, wherein more than one coat of the two-pack silicone is applied onto and into the substrate of plastics material to provide a plurality of individual coats which each have a thickness and which are of different colours to allow the thickness of each coat to be seen.
Claim 10
Dependent Claim
53 words
The method according to claim 2, wherein more than one coat of the two-pack silicone is applied onto and into the substrate of plastics material to provide a plurality of individual coats which each have a thickness and which are of different colours to allow the thickness of each coat to be seen.
Claim 11
Dependent Claim
53 words
The method according to claim 3, wherein more than one coat of the two-pack silicone is applied onto and into the substrate of plastics material to provide a plurality of individual coats which each have a thickness and which are of different colours to allow the thickness of each coat to be seen.
Claim 12
Dependent Claim
53 words
The method according to claim 5, wherein more than one coat of the two-pack silicone is applied onto and into the substrate of plastics material to provide a plurality of individual coats which each have a thickness and which are of different colours to allow the thickness of each coat to be seen.
References Cited (Backward Citations)
US3946039A
Cited
GB1308958A
Cited
US3845181A
Cited
US3899556A
Cited
US4781721A
Cited
DE3224265A1
Cited
US4600546A
Cited
US4812278A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-08-26 | 1995-02-25 | 1995-08-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-08-26 | 1999-02-25 | 1999-08-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-08-26 | 2003-02-25 | 2003-08-27 | $7700.00 | Window Closed / Lapsed |