Undercoat composition and a metal substrate coated with a resin composition
Assignee: Sekisui Chemical Co Ltd
•
Filing: 1988-12-05
•
Granted: 1991-08-20
•
Expires: 2008-12-05
Abstract
Abstract There are provided an undercoat composition with excellent adhesiveness to both a resin coating layer and a metal layer, and a metal substrate coated with a resin composition. The undercoat composition and the resin-coated metal substrate offer excellent hot-water resistance and chemical resistance.
Inventors
- 👤 Toshimi Inai
- 👤 Koichi Karukaya
- 👤 Masao Ikeda
- 👤 Kazuyoshi Yamamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:59
CPC Classifications
C; C09; C09D; C09D181/00; C09D181/02; C08; C08L; C08L65/00; C08L81/00; C08L81/02; C08L81/06; C09D165/00; C09D181/06; C09D5/00; C09D5/002; Y; Y10; Y10S; Y10S525/00; Y10S525/906; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31515; Y10T428/31522; Y10T428/31533; Y10T428/31678; Y10T428/31681; Y10T428/31688
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
129 words
A metal substrate coated with a resin composition comprising the following components (a) and (b): (a) at least one resin selected from the group consisting of a polyaryletherketone resin with a repeating unit of the following formula I, a polyaryletherketone resin with a repeating unit of the following formula II, and a polyphenylene sulfide resin with a repeating unit of the following formula III: ##STR7## and (b) at least one resin selected from the group consisting of a polyarylethersulfone resin with a repeating unit of the following formula IV and a polyarylethersulfone resin with a repeating unit of the following formula V: ##STR8## wherein the surface of said metal substrate is first coated with an undercoat composition that comprises said component (a), said component (b), and a thermosetting resin.
Claim 2
Dependent Claim
129 words
A metal substrate coated with a resin composition comprising the following components (a) and (b): (a) at least one resin selected from the group consisting of a polyaryletherketone resin with a repeating unit of the following formula I, a polyaryletherketone resin with a repeating unit of the following formula II, and a polyphenylene sulfide resin with a repeating unit of the following formula III: ##STR7## and (b) at least one resin selected from the group consisting of a polyarylethersulfone resin with a repeating unit of the following formula IV and a polyarylethersulfone resin with a repeating unit of the following formula V: ##STR8## wherein the surface of said metal substrate is first coated with an undercoat composition that comprises said component (a), said component (b), and a thermosetting resin.
Claim 3
Dependent Claim
40 words
A metal substrate coated with a resin composition according to claim 1, wherein the ratio of said component (a) to component (b) that are contained in said resin composition is in the range of from 1:9 to 9:1 by weight.
Claim 4
Dependent Claim
35 words
A metal substrate coated with a resin composition according to claim 1, wherein said thermosetting resin is at least one selected from the group consisting of imide resins, epoxy resins, phenol resins, and furan resins.
Claim 5
Dependent Claim
40 words
A metal substrate coated with a resin composition according to claim 1, wherein the ratio of said component (a) to component (b) that are contained in said undercoat composition is in the range of from 1:9 to 9:1 by weight.
Claim 6
Dependent Claim
41 words
A metal substrate coated with a resin composition according to claim 1, wherein the ratio of the total weight of said component (a) and component (b) to said thermosetting resin is in the range of from 1:9 to 9:1 by weight.
Claim 7
Dependent Claim
14 words
The metal substrate of claim 3, wherein said thermosetting resin is an imide resin.
Claim 8
Dependent Claim
69 words
The metal substrate of claim 6, wherein said imide resin is selected from the group consisting of prepolymers comprising bismaleimide and diamine as polymer units, resin compositions comprising polyfunctional cyanate or a prepolymer of polyfunctional cyanate and amine, and bismaleimide or a prepolymer of bismaleimide and amine, imide prepolymers comprising polyfunctional amine, polyanhydride, or nadic anhydride as polymer units, and resin compositions comprising bismaleimide and alkenylphenol as polymer units.
References Cited (Backward Citations)
US4021596A
Cited
UST952005I4
Cited
US4167605A
Cited
US4156049A
Cited
USRE32595E
Cited
EP0323180A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-08-19 | 1995-02-18 | 1995-08-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-08-19 | 1999-02-18 | 1999-08-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-08-19 | 2003-02-18 | 2003-08-20 | $7700.00 | Window Closed / Lapsed |