Single diaphragm forming of drapeable thermoplastic impregnated composite materials
Assignee: Cytec Technology Corp
•
Filing: 1989-06-26
•
Granted: 1991-08-06
•
Expires: 2009-06-26
Abstract
Abstract A process for preparing non-planar thermoplastic fiber reinforced composites utilizes drapeable thermoplastic impregnated fiber reinforced prepregs in a pressure thermoforming process employing but one diaphragm. The single diaphragm when initially used is flat, but becomes deformed, following its first use, to the shape of the finished part. The diaphragm thus deformed may be repeatedly used as it will still fit over the prepreg layup.
Inventors
- 👤 Steven H. Olson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 11:19
CPC Classifications
B; B29; B29C; B29C51/00; B29C51/26; B29C51/28; B29C70/00; B29C70/04; B29C70/28; B29C70/40; B29C70/42; B29C70/44; B29C43/00; B29C43/02; B29C43/10; B29C43/12; B29K; B29K2105/00; B29K2105/06; B29K2105/08; B29K2105/10; B29K2105/101
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
310 words
A process for repetitive thermoforming for the preparation of non-planar fiber reinforced thermoplastic composites, comprising: a. selecting a tool having surface contours identical to one face of the composite desired to be prepared; b. laying upon the tool surface one or more layers of a drapeable prepreg; c. employing not more than one deformable, planar diaphragm located on the side of the drapeable prepreg laid up in step (b) most remote from the tool surface; d. establishing a pressure differential between the side of the diaphragm most remote from the tool surface and the tool or surface of the prepreg adjacent to the tool and heating the prepreg laid up in step (b) to a processing temperature under conditions such as to fuse and consolidate thermoplastic located within the prepreg and form an integral thermoplastic fiber reinforced composite part; such that the planar diaphragm has been deformed to coincide with the surface of the composite part most remote from the tool; e. removing said deformed diaphragm and said integral composite part from the tool; f. selecting the same tool utilized in step (a) for a repetition of the thermoforming process and then; g. repeating step (b); h. employing as a diaphragm the non-planar, deformed diaphragm formed in step (d) on the side of the prepreg laid up in step (g) most remote from the tool surface; i. establishing a pressure differential between the side of the diaphragm most remote from the tool surface and the tool or surface of the prepreg adjacent to the tool and heating the prepreg laid up in step (g) under conditions such as to fuse and consolidate thermoplastic located within the prepreg to form an integral thermoplastic fiber reinforced composite part; j. removing said non-planar deformed diaphragm and said integral composite part formed in step (i) from the tool; and k. optionally repeating steps (f)-(j).
Claim 2
Dependent Claim
310 words
A process for repetitive thermoforming for the preparation of non-planar fiber reinforced thermoplastic composites, comprising: a. selecting a tool having surface contours identical to one face of the composite desired to be prepared; b. laying upon the tool surface one or more layers of a drapeable prepreg; c. employing not more than one deformable, planar diaphragm located on the side of the drapeable prepreg laid up in step (b) most remote from the tool surface; d. establishing a pressure differential between the side of the diaphragm most remote from the tool surface and the tool or surface of the prepreg adjacent to the tool and heating the prepreg laid up in step (b) to a processing temperature under conditions such as to fuse and consolidate thermoplastic located within the prepreg and form an integral thermoplastic fiber reinforced composite part; such that the planar diaphragm has been deformed to coincide with the surface of the composite part most remote from the tool; e. removing said deformed diaphragm and said integral composite part from the tool; f. selecting the same tool utilized in step (a) for a repetition of the thermoforming process and then; g. repeating step (b); h. employing as a diaphragm the non-planar, deformed diaphragm formed in step (d) on the side of the prepreg laid up in step (g) most remote from the tool surface; i. establishing a pressure differential between the side of the diaphragm most remote from the tool surface and the tool or surface of the prepreg adjacent to the tool and heating the prepreg laid up in step (g) under conditions such as to fuse and consolidate thermoplastic located within the prepreg to form an integral thermoplastic fiber reinforced composite part; j. removing said non-planar deformed diaphragm and said integral composite part formed in step (i) from the tool; and k. optionally repeating steps (f)-(j).
Claim 3
Dependent Claim
24 words
The process of claim 1 wherein said prepregs contain fiber reinforcement selected from the group consisting of glass, carbon, boron nitride, and silicon carbide.
Claim 4
Dependent Claim
22 words
The process of claim 1 wherein said prepregs are prepared by powder impregnation of fiber reinforcement or are prepared from hybrid yarn.
Claim 5
Dependent Claim
23 words
The process of claim 2 wherein said prepregs are prepared by powder impregnation of said fiber reinforcement or are prepared from hybrid yarn.
Claim 6
Dependent Claim
56 words
The process of claim 1 wherein said diaphragm is sealingly clamped to the tool and the pressure differential required for thermoforming is supplied by exposing the side of the diaphragm most remote from the tool to an internal pressure of an autoclave while maintaining pressure on the tool side of the diaphragm at a lesser pressure.
Claim 7
Dependent Claim
22 words
The process of claim 1 wherein the drapeability of the prepregs prior to layup is improved by adding thereto a volatile liquid.
Claim 8
Dependent Claim
11 words
The process of claim 6 wherein said volatile liquid is water.
Claim 9
Dependent Claim
42 words
The process of claim 1 wherein said thermoplastic is selected from the group consisting of polyimides, polyetherimides, and polyarylene polymers wherein aryl groups are separated by sulfide, sulfone, ether, ketone, carbonate, and C 1 -C 10 lower alkyl groups or mixtures thereof.
Claim 10
Dependent Claim
28 words
The process of claim 8 wherein said thermoplastic is a polyetheretherketone, a polysulfone, a polyethersulfone, a polyphenylene sulfide, a polyether imide, a polyetherketone, a polyimide, or mixtures thereof.
Claim 11
Dependent Claim
35 words
The process of claim 1 wherein said diaphragm comprises 1 or more layers of a thermoplastic which is deformable at the processing temperature of step 10(d) but having a fusion temperature above said processing temperature.
Claim 12
Dependent Claim
15 words
The process of claim 1 wherein said diaphragm comprises a ductile metal having high elongation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-08-05 | 1995-02-04 | 1995-08-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-08-05 | 1999-02-04 | 1999-08-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-08-05 | 2003-02-04 | 2003-08-06 | $7700.00 | Window Closed / Lapsed |