Abstract
Abstract A composition for cleaning and improving the adhesion characteristics of a copper surface (which is in turn adhered to an underlying substrate) so as to enable a coating, e.g., of photoresist, to be adhered easily and completely to the copper surface, the cleaning and adhesion promoting composition consisting essentially of an aqueous solution of an alkane sulfonic acid, a surfactant and an oxidizing agent of a type, and present in an amount, sufficient to provide controlled conversion of the copper surface to a substantially clean, micro-roughened surface, without removing the copper surface from the underlying substrate, so that the adhesion characteristics of the copper surface are substantially increased for receiving and securely adhering a subsequently applied coating.
Inventors
- 👤 Peter E. Kukanskis
- 👤 Barry H. Williams
- 👤 Thomas J. Carmody
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 17:18
CPC Classifications
C; C23; C23G; C23G1/00; C23G1/02; C23G1/10; C23G1/103; H; H05; H05K; H05K3/00; H05K3/38; H05K3/382; H05K3/383; H05K2203/00; H05K2203/12; H05K2203/122; H05K2203/125; H05K3/02; H05K3/06; H05K3/061; H05K3/064
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
134 words
A process for cleaning and improving the adhesion characteristics of a copper surface, adhered to an underlying substrate, for enabling a subsequently applied coating to be easily and completely adhered to the copper surface, said process comprising contacting said copper surface with a composition consisting essentially of water, an alkane sulfonic acid, a surfactant, and an oxidizing agent for copper, said oxidizing agent being of a type, and present in an amount, sufficient to provide, in cooperating interaction with the surfactant, and under the conditions and time of said contacting, controlled conversion of the copper surface to a substantially clean, substantially uniformly micro-roughened surface without etching said copper surface from said underlying substrate, whereby the adhesion characteristics of said copper surface are substantially increased for receiving and securely adhering a subsequently applied coating thereto.
Claim 2
Dependent Claim
134 words
A process for cleaning and improving the adhesion characteristics of a copper surface, adhered to an underlying substrate, for enabling a subsequently applied coating to be easily and completely adhered to the copper surface, said process comprising contacting said copper surface with a composition consisting essentially of water, an alkane sulfonic acid, a surfactant, and an oxidizing agent for copper, said oxidizing agent being of a type, and present in an amount, sufficient to provide, in cooperating interaction with the surfactant, and under the conditions and time of said contacting, controlled conversion of the copper surface to a substantially clean, substantially uniformly micro-roughened surface without etching said copper surface from said underlying substrate, whereby the adhesion characteristics of said copper surface are substantially increased for receiving and securely adhering a subsequently applied coating thereto.
Claim 3
Dependent Claim
55 words
The process according to claim 1, wherein said alkane sulfonic acid is present in an amount of from about 5% to 60% by weight; said oxidizer is present in an amount of from about 0.1% to 60% by weight; and said surfactant is present in an amount of from about 0.001% and 10% by weight.
Claim 4
Dependent Claim
17 words
The process according to claim 2 wherein said surfactant is a mixture of nonionic and anionic surfactants.
Claim 5
Dependent Claim
61 words
The process according to claim 1, wherein said nonionic surfactant is selected from the group consisting of ethoxylated nonylphenols and octylphenols and alcohols of ethylene oxide, alkyl polyoxyalkylene ether, and block copolymers of ethylene and propylene oxide; and the anionic surfactant is selected from the group consisting of sulfonated aryl and alkyl hydrocarbons, sulfated aryl and alkyl hydrocarbons, and phosphate esters.
Claim 6
Dependent Claim
110 words
A process for cleaning and improving the adhesion characteristics of a copper surface adhered to an underlying substrate, for enabling a subsequently applied coating to be easily and completely adhered to the copper surface, said process comprising, contacting said copper surface with a composition consisting essentially of water, methane sulfonic acid, ferric nitrate, and a surfactant mixture of ethoxylated nonyl- and octylphenols and alcohols of ethylene oxide, alkyl polyoxyalkylene ether, and sulfonated aryl and alkyl hydrocarbons, for a time and at conditions effective to provide a controlled conversion of the copper surface to a substantially clean, substantially uniformly micro-roughened surface topography without removing said copper surface from said underlying substrate.
Claim 7
Dependent Claim
110 words
A process for cleaning and improving the adhesion characteristics of a copper surface adhered to an underlying substrate, for enabling a subsequently applied coating to be easily and completely adhered to the copper surface, said process comprising, contacting said copper surface with a composition consisting essentially of water, methane sulfonic acid, ferric nitrate, and a surfactant mixture of ethoxylated nonyl- and octylphenols and alcohols of ethylene oxide, alkyl polyoxyalkylene ether, and sulfonated aryl and alkyl hydrocarbons, for a time and at conditions effective to provide a controlled conversion of the copper surface to a substantially clean, substantially uniformly micro-roughened surface topography without removing said copper surface from said underlying substrate.
Claim 8
Dependent Claim
81 words
A process according to claim 5 wherein said composition consists essentially of water, between about 15%-40% by weight of an alkane sulfonic acid selected from the group consisting of methane sulfonic acid and ethane sulfonic acid; between about 1%-15% by weight of an oxidizer selected from the group consisting of ferric nitrate, peroxide, ferric chloride, and copper chloride; and between about 0.01%-3% by weight of a surfactant selected from the group consisting of nonionic surfactants and anionic surfactants, and mixtures thereof.
Claim 9
Dependent Claim
58 words
A process according to claim 6 wherein said composition consists essentially of water, about 35% by weight of an methane sulfonic acid (70%), about 7.5% by weight of ferric nitrate, and about 1.75% by weight of a surfactant mixture of ethoxylated nonyl- and octylphenols and alcohols of ethylene oxide, alkyl polyoxyalkylene ether, and sulfonated aryl and alkyl hydrocarbons.
Claim 10
Dependent Claim
26 words
The process according to claim 3 wherein said step of contacting said surface with said composition is achieved by immersing said copper surface in said composition.
Claim 11
Dependent Claim
26 words
The process according to claim 3 wherein said step of contacting said surface with said composition is achieved by spraying said composition onto said copper surface.
Claim 12
Dependent Claim
17 words
The process according to claim 3 wherein said copper surface is a copper-clad printed circuit board substrate.
Claim 13
Dependent Claim
22 words
The process according to claim 10 wherein said subsequently applied coating is selected from the group consisting of photoresist and oxide coatings.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-08-05 | 1995-02-04 | 1995-08-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-08-05 | 1999-02-04 | 1999-08-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-08-05 | 2003-02-04 | 2003-08-06 | $7700.00 | Window Closed / Lapsed |