Synthetic alkali metal alumino-silicates compositions and their methods of preparation
Assignee: JM Huber Corp
•
Filing: 1989-01-17
•
Granted: 1991-07-30
•
Expires: 2009-01-17
Abstract
Abstract A family of novel and unique synthetic alkali metal alumino-silicates (SAMS) are produced by the hydrothermal reaction between kaolin and alkali metal silicates. The integrated composition of the SAMS products is a unique entity having an overall composition of xM.sub.2 O:Al.sub.2 O.sub.3 :ySiO.sub.2 :zH.sub.2 O where x is the number of moles of alkali metal oxide and is an integer from 0.01 to 2.0, M is the alkali metal, y is the number of moles of SiO 2 in the unique SAMS compostions and is an integer greater than 2.0, and z is the number of moles of bound water and is an integer ranging from 1.0 to 5.0. The unique SAMS compositions are structured materials in which the structure can be controlled, and are therefore useful as functional fillers, as TiO 2 extenders, as silica extenders or as reinforcing agents for paper, paint, rubber, plastics and specialty products.
Inventors
- 👤 Satish K. Wason
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 09:58
CPC Classifications
C; C11; C11D; C11D3/00; C11D3/02; C11D3/12; C11D3/124; C11D3/1246; C11D3/128; C08; C08K; C08K3/00; C08K3/34; C09; C09C; C09C1/00; C09C1/40; C09C1/42; C09D; C09D5/00; C09D5/02; C09D5/024; C09D5/028; C09D7/00; C09D7/40; C09D7/42; D; D21; D21H; D21H17/00; D21H17/63; D21H17/67; D21H17/68; D21H19/00; D21H19/36; D21H19/38; D21H19/40; C01; C01P; C01P2002/00; C01P2002/02; C01P2002/70; C01P2002/72; C01P2002/74; C01P2002/80; C01P2002/82; C01P2002/85; C01P2004/00; C01P2004/01; C01P2004/03; C01P2004/04; C01P2004/20; C01P2004/30; C01P2004/32; C01P2004/50; C01P2004/51; C01P2004/60; C01P2004/61; C01P2004/62; C01P2004/80; C01P2004/82; C01P2006/00; C01P2006/10; C01P2006/12; C01P2006/14; C01P2006/19; C01P2006/20; C01P2006/21; C01P2006/60; C01P2006/80; C01P2006/82; C01P2006/90
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
80 words
An alkali metal alumino-silicate having a composition in terms of mole ratio of oxides as follows: xM.sub.2 O:Al.sub.2 O.sub.3 :ySiO.sub.2 :zH.sub.2 O where x is the number of moles of alkali metal oxide, M is an alkali metal, y is the number of moles of SiO 2 associated with the alkali metal alumino-silicate compositions, and z is the number of moles of bound water, and having the morphology of rimmed particles as depicted in any one of TEM FIGS. 18-23.
Claim 2
Dependent Claim
80 words
An alkali metal alumino-silicate having a composition in terms of mole ratio of oxides as follows: xM.sub.2 O:Al.sub.2 O.sub.3 :ySiO.sub.2 :zH.sub.2 O where x is the number of moles of alkali metal oxide, M is an alkali metal, y is the number of moles of SiO 2 associated with the alkali metal alumino-silicate compositions, and z is the number of moles of bound water, and having the morphology of rimmed particles as depicted in any one of TEM FIGS. 18-23.
Claim 3
Dependent Claim
152 words
An essentially x-ray amorphous alkali metal alumino-silicate having a composition in terms of mole ratio of oxides as follows: xM.sub.2 O:Al.sub.2 O.sub.3 :ySiO.sub.2 :zH.sub.2 O where M is the alkali metal, x is the number of moles of alkali metal oxide and is between 0.01 to 2.0, y is the number of moles of SiO 2 in the alkali metal alumino-silicate composition and is an integer greater than 2.0, and z is the number of moles of bound water and is an integer of 1.0 to 5.0, said alkali metal alumino-silicate having attenuated kaolin peaks in the XRD patterns from the kaolin remnants in the compositions and having the characteristic IR scan labelled SAMS shown in any one of FIGS. 3-6 and which are shown by any one of TEM FIGS. 18-23 to be altered kaolin platelets integrated with a rimmed area of essentially amorphous alkali metal silicate base-kaolin clay reaction product.
Claim 4
Dependent Claim
152 words
An essentially x-ray amorphous alkali metal alumino-silicate having a composition in terms of mole ratio of oxides as follows: xM.sub.2 O:Al.sub.2 O.sub.3 :ySiO.sub.2 :zH.sub.2 O where M is the alkali metal, x is the number of moles of alkali metal oxide and is between 0.01 to 2.0, y is the number of moles of SiO 2 in the alkali metal alumino-silicate composition and is an integer greater than 2.0, and z is the number of moles of bound water and is an integer of 1.0 to 5.0, said alkali metal alumino-silicate having attenuated kaolin peaks in the XRD patterns from the kaolin remnants in the compositions and having the characteristic IR scan labelled SAMS shown in any one of FIGS. 3-6 and which are shown by any one of TEM FIGS. 18-23 to be altered kaolin platelets integrated with a rimmed area of essentially amorphous alkali metal silicate base-kaolin clay reaction product.
Claim 5
Dependent Claim
91 words
An alkali metal alumino-silicate of composition of claim 2, where the alkali metal silicate is sodium and having a composition in terms of mole ratio of oxides, as follows: xNa.sub.2 O:Al.sub.2 O.sub.3 :ySiO.sub.2 :zH.sub.2 O where x is the number of moles of sodium oxide and is between 0.01 to 2.0, y is the number of moles of SiO 2 in the alkali metal alumino-silicate composition and is an integer greater than 2.0, and z is the number of moles of bound water and is an integer of 1.0 to 5.0.
Claim 6
Dependent Claim
37 words
A composition according to claim 1, wherein the alkali metal alumino-silicate compositions have an oil absorption range of about 40 to above 200 ml/100 g and a surface area of about 2 to 300 m 2 /g.
Claim 7
Dependent Claim
36 words
A composition according to claim 2, wherein the alkali metal alumino-silicate compositions have an oil absorption range of at least about 40 ml/100 g and a surface area range of 2 to 300 m 2 /g.
Claim 8
Dependent Claim
37 words
A composition according to claim 3, wherein the sodium alkali metal alumino-silicate compositions have an oil absorption range of at least about 40 ml/100 g and a surface area range of 2 to 300 m 2 /g.
References Cited (Backward Citations)
US4117191A
Cited
US4812299A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-07-29 | 1995-01-28 | 1995-07-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-07-29 | 1999-01-28 | 1999-07-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-07-29 | 2003-01-28 | 2003-07-30 | $7700.00 | Window Closed / Lapsed |