Polyester film
Assignee: Hoechst AG
•
Filing: 1990-09-28
•
Granted: 1991-07-16
•
Expires: 2010-09-28
Abstract
Abstract The invention concerns a polyester film with improved abrasion resistance, dimensional stability, drawability and slip properties. The film is characterized by the fact that it contains 0.005 to 5.0% by weight of organic, preferably hardened or crosslinked, particles with narrow particle size distribution in a range between 0.01 and 5 microns, as well as a nucleating agent in an amount from 0.01 to 10% by weight, both values related to the weight of the polymers which form the film.
Inventors
- 👤 Hermann Dallmann
- 👤 Werner Schaefer
- 👤 Wolfgang Gawrisch
- 👤 Hartmut Hensel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 13:15
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/18; C08L; C08L67/00; C08L67/02; C08J2367/00; C08J2367/02; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31551; Y10T428/31565; Y10T428/31652; Y10T428/31663; Y10T428/31786; Y10T428/31797
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
150 words
An abrasion-resistant polyester film manufactured from a composition comprising a polyester chemically modified with from 0.005 to 5.0 percent by weight, based upon the total weight of said composition, of crosslinked organic particles covalently bonded to and substantially homogeneously distributed throughout said polyester, said particles having a grain size distribution of from 0.01 to 5.0 microns, wherein the quotient of the weight average particle diameter and the number average particle diameter is 1.1 or less, said chemically-modified polyester additionally containing from 0.01 to 10.0 percent, based upon the weight of the polyester, of a nucleating agent selected from the group consisting of alkali metal salts of ester waxes, akaline earth salts of ester waxes, alkali metal salts of partially saponified ester waxes and alkaline earth salts of partially saponified ester waxes; and further comprising at least one additional crosslinkable coating layer on at least one major surface of said film.
Claim 2
Dependent Claim
150 words
An abrasion-resistant polyester film manufactured from a composition comprising a polyester chemically modified with from 0.005 to 5.0 percent by weight, based upon the total weight of said composition, of crosslinked organic particles covalently bonded to and substantially homogeneously distributed throughout said polyester, said particles having a grain size distribution of from 0.01 to 5.0 microns, wherein the quotient of the weight average particle diameter and the number average particle diameter is 1.1 or less, said chemically-modified polyester additionally containing from 0.01 to 10.0 percent, based upon the weight of the polyester, of a nucleating agent selected from the group consisting of alkali metal salts of ester waxes, akaline earth salts of ester waxes, alkali metal salts of partially saponified ester waxes and alkaline earth salts of partially saponified ester waxes; and further comprising at least one additional crosslinkable coating layer on at least one major surface of said film.
Claim 3
Dependent Claim
20 words
The film of claim 1 wherein the second layer is composed of a different thermoplastic polymer than the first layer.
Claim 4
Dependent Claim
11 words
The film of claim 1 wherein the layers are extruded simultaneously.
Claim 5
Dependent Claim
148 words
A film laminate comprising: (a) a first film layer; and (b) a second abrasion-resistant polyester layer, said abrasion-resistant polyester layer manufactured from a composition comprising a polyester chemically modified with from 0.005 to 5.0 percent by weight, based upon the total weight of said composition, of crosslinked organic particles covalently bonded to and substantially homogeneously distributed throughout said polyester, said particles having a grain size distribution of from 0.01 to 5.0 microns, wherein the quotient of the weight average particle diameter and the number average particle diameter is 1.1 or less, said chemically modified polyester additionally containing from 0.01 to 10.0 percent based upon the weight of the polyester, of a nucleating agent selected from the group consisting of alkali metal salts of ester waxes, alkaline earth salts of ester waxes, alkali metal salts of partially saponified ester waxes, and alkaline earth salts of partially saponified ester waxes.
Claim 6
Dependent Claim
148 words
A film laminate comprising: (a) a first film layer; and (b) a second abrasion-resistant polyester layer, said abrasion-resistant polyester layer manufactured from a composition comprising a polyester chemically modified with from 0.005 to 5.0 percent by weight, based upon the total weight of said composition, of crosslinked organic particles covalently bonded to and substantially homogeneously distributed throughout said polyester, said particles having a grain size distribution of from 0.01 to 5.0 microns, wherein the quotient of the weight average particle diameter and the number average particle diameter is 1.1 or less, said chemically modified polyester additionally containing from 0.01 to 10.0 percent based upon the weight of the polyester, of a nucleating agent selected from the group consisting of alkali metal salts of ester waxes, alkaline earth salts of ester waxes, alkali metal salts of partially saponified ester waxes, and alkaline earth salts of partially saponified ester waxes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-07-15 | 1995-01-14 | 1995-07-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-07-15 | 1999-01-14 | 1999-07-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-07-15 | 2003-01-14 | 2003-07-16 | $7700.00 | Window Closed / Lapsed |