Powder particles for fine-grained hard material alloys and a process for the preparation of powder particles for fine-grained hard material alloys
Assignee: Santrade Ltd
•
Filing: 1989-10-26
•
Granted: 1991-07-16
•
Expires: 2009-10-26
Abstract
Abstract The present invention relates to powder particles consisting of hard principles and binder metal for the manufacture of superior, uniquely fine-grained hard material alloys and to a procedure for the preparation of said particles. The preparation is performed in an economical way because the procedure starts from conventional melt metallurgical raw materials. A pre-alloy consisting of hard principle forming and binder phase forming elements is subjected to a heat treatment such as nitriding and carburizing after being crushed. The final product is particles composed by hard principle phases and binder metal phases formed "in situ" in an effective binding.
Inventors
- 👤 Carl S. G. Ekemar
- 👤 Rolf G. Oskarsson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 07:23
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/02; B22F9/04; B22F2009/041
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
206 words
Method of making powder particles of a mean particle size between 1 and 16 μm with at most 5% of the particles having a particle size>30 μm for the preparation of a fine-grained hard material alloy for cutting tools consisting essentially of hard principles in an amount of 25-90 volume % and binder metal with the alloy containing greater contents of hard principles than in high speed steel, in which the hard principles are compounds of one or more elements in the groups IVA, VA and VIA of the periodical system and Si with C, N and/or B, and the binder metal being based upon Fe, Co and/or Ni, characterized in that melt metallurgical raw materials containing the metallic alloying elements for both the hard principle forming and the binder metal forming elements, but without intentional additions of the elements C, N, B and O, are melted and cast to a pre-alloy, which in solidified condition consists essentially of brittle, intermetallic phases with hard principle forming and binder metal forming elements mixed in atomic scale, after which the pre-alloy is crushed and/or milled to powder and the powder is subjected to treatment for the simultaneous in situ formation of hard principles grains and binder metal constituents.
Claim 2
Dependent Claim
206 words
Method of making powder particles of a mean particle size between 1 and 16 μm with at most 5% of the particles having a particle size>30 μm for the preparation of a fine-grained hard material alloy for cutting tools consisting essentially of hard principles in an amount of 25-90 volume % and binder metal with the alloy containing greater contents of hard principles than in high speed steel, in which the hard principles are compounds of one or more elements in the groups IVA, VA and VIA of the periodical system and Si with C, N and/or B, and the binder metal being based upon Fe, Co and/or Ni, characterized in that melt metallurgical raw materials containing the metallic alloying elements for both the hard principle forming and the binder metal forming elements, but without intentional additions of the elements C, N, B and O, are melted and cast to a pre-alloy, which in solidified condition consists essentially of brittle, intermetallic phases with hard principle forming and binder metal forming elements mixed in atomic scale, after which the pre-alloy is crushed and/or milled to powder and the powder is subjected to treatment for the simultaneous in situ formation of hard principles grains and binder metal constituents.
Claim 3
Dependent Claim
32 words
Method according to claim 1, characterized in that the preparation of the melt before the casting is performed within a temperature range of 50°-300° C. above the liquidus temperature of the pre-alloy.
Claim 4
Dependent Claim
34 words
Method according to claim 1, characterized in that the treatment for the simultaneous in situ formation of hard principle grains and binder metal elements is conducted at a temperature of from about 200°-1200° C.
Claim 5
Dependent Claim
28 words
Method according to claim 2, characterized in that the casting is performed at a temperature in a range within 100°-250° C. above the liquidus temperature of the pre-alloy.
Claim 6
Dependent Claim
17 words
Method according to claim 3, characterized in that the temperature range for treatment is about 300°-1000° C.
References Cited (Backward Citations)
US3459546A
Cited
US3591362A
Cited
US3650729A
Cited
DE2033100A1
Cited
JPS4828247A
Cited
US3916497A
Cited
US3953194A
Cited
SU647349A1
Cited
US4192672A
Cited
DE3011962A1
Cited
JPS5726101A
Cited
WO1983001917A1
Cited
US4619699A
Cited
US4687511A
Cited
JPS63100108A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-07-15 | 1995-01-14 | 1995-07-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-07-15 | 1999-01-14 | 1999-07-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-07-15 | 2003-01-14 | 2003-07-16 | $7700.00 | Window Closed / Lapsed |