US5030401A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for molding powders
Assignee: JFE Engineering Corp
•
Filing: 1990-01-26
•
Granted: 1991-07-09
•
Expires: 2010-01-26
Abstract
Abstract A method for molding powders to form a shaped compact comprising the steps of forming a thin-wall resilient mold having an outer surface and having at least one opening adjacent a surface of a model of a desired shape, forming a mold support on the outer surface of the thin-wall resilient mold, so that the mold support adheres to the outer surface of the thin-walled resilient mold, removing the model from the thin-wall resilient mold whereby a cavity is formed in a portion of the thin-wall resilient mold, from which the model is removed, filling up the cavity of the thin-wall resilient mold with a powder as a forming material through the opening, sealing the opening of the thin-wall resilient mold after having evacuated air from the inside of the thin-wall resilient mold, removing the mold support from the thin-wall resilient mold, subjecting the thin-wall resilient mold filled with the powder to a cold isostatic press. The mold support can be made by cast molding or by applying a material such as water-glass, a hydrolysis liquid of metal alkoxide, liquid polyurethane resin, liquid epoxy resin or liquid gypsum.
Inventors
- 👤 Hiroaki Nishio
- 👤 Hideharu Yamamoto
- 👤 Jun Harada
- 👤 Takeshi Kawashima
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 13:27
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/02; B22F3/04; B22F3/12; B22F3/1208; B22F3/1216; B22F3/1233; B22F3/1258; B22F3/1275
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
145 words
A method for molding powders to form a shaped compact comprising the steps of: forming a thin-wall resilient mold around outer surfaces of a model of a desired shape, said thin-wall resilient mold having at least one opening; forming a mold support around and in conforming contact with outer surfaces of said thin-wall resilient mold; removing said model from said thin-wall resilient mold whereby a cavity is formed in a portion of said thin-wall resilient mold from which said model is removed; filling said cavity of the thin-wall resilient mold with a powder as a forming material through said opening; sealing said opening of the thin-wall resilient mold after having evacuated gas from the inside of the thin-wall resilient mold; removing said mold support from the thin-wall resilient mold; and subjecting said thin-wall resilient mold filled with said powder to a cold isostatic press treatment.
Claim 2
Independent Claim
145 words
A method for molding powders to form a shaped compact comprising the steps of: forming a thin-wall resilient mold around outer surfaces of a model of a desired shape, said thin-wall resilient mold having at least one opening; forming a mold support around and in conforming contact with outer surfaces of said thin-wall resilient mold; removing said model from said thin-wall resilient mold whereby a cavity is formed in a portion of said thin-wall resilient mold from which said model is removed; filling said cavity of the thin-wall resilient mold with a powder as a forming material through said opening; sealing said opening of the thin-wall resilient mold after having evacuated gas from the inside of the thin-wall resilient mold; removing said mold support from the thin-wall resilient mold; and subjecting said thin-wall resilient mold filled with said powder to a cold isostatic press treatment.
Claim 3
Dependent Claim
24 words
The method of claim 1, wherein said model is made of a material selected from the group consisting of metal, ceramics, plastic and wood.
Claim 4
Dependent Claim
15 words
The method of claim 1, wherein said model is made of material removable by melting.
Claim 5
Dependent Claim
13 words
The method of claim 3, wherein said material removable by melting is wax.
Claim 6
Dependent Claim
24 words
The method of claim 1, wherein said model is made of a material removable by dissolving said model in water or an organic solvent.
Claim 7
Dependent Claim
19 words
The method of claim 1, wherein said model is made of a material which can be removed by sublimation.
Claim 8
Dependent Claim
15 words
The method of claim 1, wherein said thin-wall resilient mold is made of natural rubber.
Claim 9
Dependent Claim
15 words
The method of claim 1, wherein said thin-wall resilient mold is made of synthetic rubber.
Claim 10
Dependent Claim
29 words
The method of claim 8, wherein said synthetic rubber is selected from the group consisting of styrene-butadiene rubber, polyisoprene rubber, isobutylene rubber, isoprene rubber, silicone rubber and urethane rubber.
Claim 11
Dependent Claim
18 words
The method of claim 1, wherein said thin-wall resilient mold has a thickness of 50 to 2000 μm.
Claim 12
Dependent Claim
14 words
The method of claim 1, wherein said mold support is made by cast molding.
Claim 13
Dependent Claim
34 words
The method of claim 11, wherein said cast molding is carried out by casting a material selected from the group consisting of liquid polyurethane resin, liquid epoxy resin and liquid gypsum into a mold.
Claim 14
Dependent Claim
19 words
The method of claim 12, wherein said cast molding is carried out by casting liquid gypsum into a mold.
Claim 15
Dependent Claim
15 words
The method of claim 1, wherein said mold support is made by applying a material.
Claim 16
Dependent Claim
33 words
The method of claim 14, wherein said material is selected from the group consisting of water-glass, hydrolysis liquid of metal alkoxide, liquid phenol resin, liquid polyurethane resin, liquid epoxy resin and liquid gypsum.
Claim 17
Dependent Claim
14 words
The method of claim 1, wherein said model is removed by melting the model.
Claim 18
Dependent Claim
14 words
The method of claim 1, wherein said model is removed by dissolving the model.
Claim 19
Dependent Claim
14 words
The method of claim 1, wherein said model is removed by sublimating the model.
Claim 20
Dependent Claim
11 words
The method of claim 1, wherein said powder is metal powder.
Claim 21
Dependent Claim
11 words
The method of claim 1, wherein said powder is ceramic powder.
Claim 22
Dependent Claim
15 words
The method of claim 1, wherein the mold support adheres to the thin-wall resilient mold.
Claim 23
Dependent Claim
13 words
The method of claim 5, wherein the material removable by dissolving is urea.
Claim 24
Dependent Claim
14 words
The method of claim 6, wherein the material is removable by sublimation is naphthalene.
Claim 25
Dependent Claim
31 words
The method of claim 14, wherein the material is applied on the surfaces of the model by brushing, dipping the model in the material or spraying the model with the material.
Claim 26
Dependent Claim
40 words
The method of claim 1, wherein the powder is selected from the group consisting of stainless steel powder, high-speed tool steel powder, a mixed powder of tungsten carbide-cobalt, alumina powder, silicon nitride powder, silicon carbide powder and titanium diboride powder.
Claim 27
Dependent Claim
19 words
The method of claim 25, wherein the powder comprises spherical particles of a size of 10 to 1000 μm.
Claim 28
Dependent Claim
25 words
The method of claim 1, which further comprises applying a mold releasing agent or an adhesive agent to the surface of the thin-wall resilient mold.
Claim 29
Dependent Claim
49 words
The method of claim 1, wherein said model is made from paraffin wax having a melting point of 48° to 50° C., said thin wall resilient mold is made from natural rubber, said mold support is made by casting liquid gypsum into a mold and said powder is alumina.
Claim 30
Dependent Claim
61 words
The method of claim 1, wherein said model is made from nylon, said thin-wall resilient mold is made from natural rubber, said mold support is made by applying a liquid comprising colloidal silica and alumina on the surface of the thin-wall resilient mold, said mold support adheres to the thin-walled resilient mold, said powder is alumina, and said gas is air.
Claim 31
Dependent Claim
149 words
The method of claim 2, wherein said thin-wall resilient mold is made of natural or a synthetic rubber selected from the group consisting of styrene-butadiene rubber, polyisoprene rubber, isobutylene rubber, isoprene rubber, silicone rubber, and urethane rubber, said thin-wall resilient mold has a thickness of 50 to 2000 μm, said mold support is made by casting in a mold a material selected from the group consisting of liquid polyrethane rubber, liquid epoxy resin and liquid gypsum or by applying a material selected from the group consisting of water-glass, a hydrolysis liquid of metal alkoxide, liquid phenol resin, liquid polyurethane resin, liquid epoxy resin and liquid gypsum, said mold support adheres to the thin-wall resilient mold, said powder is selected from the group consisting of metal powder and ceramic powder said gas is air and said model is removed by melting the model, dissolving the model or sublimating the model.
References Cited (Backward Citations)
US4777002A
Cited
US4552779A
Cited
US4615855A
Cited
US4812278A
Cited
US4927600A
Cited
JPS62286713A
Cited
JPS62294103A
Cited
EP0249936A2
Cited
JPS62297402A
Cited
US4761264A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-07-08 | 1995-01-07 | 1995-07-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-07-08 | 1999-01-07 | 1999-07-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-07-08 | 2003-01-07 | 2003-07-09 | $7700.00 | Window Closed / Lapsed |