Method of in-mold sulfonation of molded plastic article
Assignee: Dow Chemical Co
•
Filing: 1989-07-12
•
Granted: 1991-07-09
•
Expires: 2009-07-12
Abstract
Abstract An in-mold sulfonation system for sulfonating the surface of plastic articles such as plastic containers during molding. Sulfur trioxide is introduced into a pre-mold chamber, converted to a relatively high pressure gaseous sulfur trioxide, and then injected into a mold such as a blow mold immediately before or immediately following full expansion of the formed plastic article in the mold cavity. Neutralization with a gaseous neutralizing agent follows. By controlling the timing and temperature of the in-mold sulfonation step it is possible to produce a plastic article having an effective barrier layer but containing a minimum of undesirable rinseable salts.
Inventors
- 👤 Wilhelm E. Walles
- 👤 Donald L. Tomkinson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:02
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/12; B; B29; B29C; B29C59/00; B29C49/00; B29C49/42; B29C49/46; B29C2049/4673; B29C2049/4698; B29K; B29K2023/00; B29K2023/04; B29K2023/06; B29K2995/00; B29K2995/0037; B29K2995/0065; B29K2995/0067; B29L; B29L2031/00; B29L2031/712; B29L2031/7172
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
121 words
A method for in-mold sulfonating a surface of a plastic article during molding thereof comprising: a) forming a thermoplastic resin into a plastic article in a mold by molding at a forming temperature and elevated pressure, b) producing a gaseous sulfur trioxide at a pressure which is higher than the molding pressure, c) introducing a measured amount of gaseous sulfur trioxide into contact with a surface of said plastic article in the mold while said article is substantially at the forming temperature and before any significant cooling of said plastic article takes place to thereby sulfonate said surface of said plastic article with said gaseous sulfur trioxide to produce a sulfonated surface, and d) cooling the molded, surface sulfonated plastic article.
Claim 2
Independent Claim
121 words
A method for in-mold sulfonating a surface of a plastic article during molding thereof comprising: a) forming a thermoplastic resin into a plastic article in a mold by molding at a forming temperature and elevated pressure, b) producing a gaseous sulfur trioxide at a pressure which is higher than the molding pressure, c) introducing a measured amount of gaseous sulfur trioxide into contact with a surface of said plastic article in the mold while said article is substantially at the forming temperature and before any significant cooling of said plastic article takes place to thereby sulfonate said surface of said plastic article with said gaseous sulfur trioxide to produce a sulfonated surface, and d) cooling the molded, surface sulfonated plastic article.
Claim 3
Dependent Claim
12 words
The method of claim 1 wherein said thermoplastic resin is a polyolefin.
Claim 4
Dependent Claim
34 words
The method of claim 2 wherein said thermoplastic resin is formed by blow molding at approximately 80-100 psi and said relatively high pressure gaseous sulfur trioxide is at a pressure of approximately 100-120 psi.
Claim 5
Dependent Claim
47 words
The method of claim 3 wherein said molding takes place at approximately 110° to 180° C., said relatively high pressure gaseous sulfur trioxide is at a temperature of 80° to 140° C., and said plastic article is at approximately 160° to 80° C. during said sulfonating step.
Claim 6
Dependent Claim
15 words
The method of claim 4 wherein said sulfonation step lasts approximately 0.1 to 2 min.
Claim 7
Dependent Claim
29 words
The method of claim 1 wherein said plastic article is hollow defining an interior and exterior surface and the surface of said plastic article sulfonated is the interior surface.
Claim 8
Dependent Claim
14 words
The method of claim 6 wherein said plastic article is a vehicle gasoline tank.
Claim 9
Dependent Claim
38 words
The method of claim 1 further including the step of neutralizing any sulfonic acid groups on the sulfonated surface of said plastic article with a gaseous neutralizing agent which contains less than 1 percent by weight of moisture.
Claim 10
Dependent Claim
19 words
The method of claim 1 wherein said sulfonating step takes place at a sulfur trioxide concentration of 15-25 percent.
Claim 11
Dependent Claim
31 words
The method of claim 1 comprising injecting a charge of liquid sulfur trioxide into a premold chamber and producing said relatively high pressure gaseous sulfur trioxide from said liquid sulfur trioxide.
Claim 12
Dependent Claim
26 words
The method of claim 10 wherein said liquid sulfur trioxide is essentially pure sulfur trioxide and said gaseous sulfur trioxide is nearly 100% sulfur trioxide gas.
References Cited (Backward Citations)
US2937066A
Cited
US2832696A
Cited
US3740258A
Cited
US3629025A
Cited
US3613957A
Cited
US3625751A
Cited
US3959561A
Cited
US3592724A
Cited
US3862284A
Cited
US4220739A
Cited
US4336015A
Cited
US4396567A
Cited
US4615914A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-07-08 | 1995-01-07 | 1995-07-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-07-08 | 1999-01-07 | 1999-07-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-07-08 | 2003-01-07 | 2003-07-09 | $7700.00 | Window Closed / Lapsed |