Abstract A sintered silicon nitride contains at least 90% of β-type silicon nitride, wherein said β-type silicon nitride consists essentially of 35 to 80% of large crystal particles with the remainder of small crystal particles, said large crystal particles having a mean particle length being at least two times as long as that of said small crystal particles. This sintered silicon nitride is obtained by a method wherein one batch of starting silicon nitride powders, whose primary particles have a mean particle size of 0.1 to 0.5 μm, and another batch of starting silicon nitride powders, whose primary particles have a mean particle size of 0.5 to 0.7 μm, are blended with a sintering aid or aids at a given weight ratio, and the thus obtained blend is formed or compacted and sintered.
A sintered silicon nitride comprising at least 90% of β-type silicon nitride, said β-type silicon nitride consisting essentially of 35 to 80% of large crystal particles having a mean particle length of 5.0 to 14 μm with the remainder being small crystal particles having a mean particle length of 0.5 to 5 μm, wherein the large and small crystal particles have an aspect ratio of at least 3 and the mean particle length of the large crystal particles is at least twice the mean particle length of the small crystal particles.
Claim 2
Dependent Claim
91 words
A sintered silicon nitride comprising at least 90% of β-type silicon nitride, said β-type silicon nitride consisting essentially of 35 to 80% of large crystal particles having a mean particle length of 5.0 to 14 μm with the remainder being small crystal particles having a mean particle length of 0.5 to 5 μm, wherein the large and small crystal particles have an aspect ratio of at least 3 and the mean particle length of the large crystal particles is at least twice the mean particle length of the small crystal particles.
Claim 3
Dependent Claim
95 words
A method for making a sintered silicon nitride as recited in claim 1, comprising blending a batch of silicon nitride powder A in which the primary particles have a mean particle size of 0.1 to 0.5 μm and a batch of silicon nitride powder B in which the primary particles have a mean particle size of 0.5 to 0.7 μm, the weight ratio of B/A being in the range of 35/65 to 80/20, with a sintering aid, forming or compacting the blend and then sintering the blend so as to obtain the sintered silicon nitride.