Dispersion of fine particles of a polymer
Assignee: Kansai Paint Co Ltd
•
Filing: 1990-10-15
•
Granted: 1991-06-18
•
Expires: 2010-10-15
Abstract
Abstract A dispersion of fine particles of a gelled polymer obtainable by copolymerizing and crosslinking a vinyl monomer mixture containing at least 0.5% by weight each of at least two vinyl monomers in the presence of a macromonomer A, which has a molecular chain of poly(12-hydroxystearic acid) and has at least about one polymerizable unsaturated double bond per molecule in average, and a macromonomer B, which is a copolymer of an ethylenic unsaturated monomer and has a solubility parameter value of from 7.5 to 9.2 and about 1.0 to about 1.5 in average of polymerizable unsaturated double bonds, in an organic solvent which is capable of dissolving the macromonomers A and B but is substantially incapable of dissolving a polymer formed from said vinyl monomer mixture; and a curable resin composition comprising a dispersion of fine particles of the above-described gelled polymer, a base resin which is non-compatible with the macromonomer A but is compatible with the macromonomer B and which forms a continuous phase, and at least one crosslinking agent selected from the group consisting of an amino resin and a polyisocyanate compound.
Inventors
- 👤 Motoshi Yabuta
- 👤 Yasushi Nakao
- 👤 Shinji Sugiura
- 👤 Mitsuhiro Fukuda
- 👤 Yuzo Miyamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 19:01
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/42; C08G18/4266; C08G18/4283; C08F; C08F290/00; C08F290/02; C08F290/04; C08F290/06; C08F290/061; C08F290/08; C08F290/12; C08F290/14; C08F290/141; C08F299/00; C08F299/02; C08F299/022; C08G18/70; C08G18/81; C08G18/8108; C08G18/8141; C08G18/815; C08G18/8158; C08G18/8175
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
125 words
A dispersion of fine particles of a gelled polymer obtained by copolymerizing and crosslinking a vinyl monomer mixture containing at least 0.5% by weight each of at least two vinyl monomers in the presence of a macromonomer A, which has a molecular chain of poly(12-hydroxystearic acid) and has at least about one polymerizable unsaturated double bond per molecule in average, and a macromonomer B, which is a copolymer of an ethylenic unsaturated monomer and has a solubility parameter value of from 7.5 to 9.2 and about 1.0 to about 1.5 in average of polymerizable unsaturated double bonds, in an organic solvent which is capable of dissolving said macromonomers A and B but is substantially incapable of dissolving a polymer formed from said vinyl monomer mixture.
Claim 2
Dependent Claim
125 words
A dispersion of fine particles of a gelled polymer obtained by copolymerizing and crosslinking a vinyl monomer mixture containing at least 0.5% by weight each of at least two vinyl monomers in the presence of a macromonomer A, which has a molecular chain of poly(12-hydroxystearic acid) and has at least about one polymerizable unsaturated double bond per molecule in average, and a macromonomer B, which is a copolymer of an ethylenic unsaturated monomer and has a solubility parameter value of from 7.5 to 9.2 and about 1.0 to about 1.5 in average of polymerizable unsaturated double bonds, in an organic solvent which is capable of dissolving said macromonomers A and B but is substantially incapable of dissolving a polymer formed from said vinyl monomer mixture.
Claim 3
Dependent Claim
68 words
A dispersion as claimed in claim 1, wherein said macromonomer A is a macromonomer having about one in average of polymerizable unsaturated double bond per molecule and obtained by reacting a monoepoxy group-containing polymerizable unsaturated compound with a terminal carboxyl group of poly(12-hydroxystearic acid) by addition reaction, or by reacting a monoisocyanate group-containing polymerizable unsaturated compound with a terminal carboxyl group or secondary hydroxyl group of poly(12-hydroxystearic acid).
Claim 4
Dependent Claim
32 words
A dispersion as claimed in claim 2, wherein said monoepoxy group containing compound is selected from the group consisting of glycidyl acrylate, glycidyl methacrylate, allyl glycidyl ether, (3,4-epoxycyclohexyl)methyl methacrylate and (3,4-epoxycyclchexyl)methyl acrylate.
Claim 5
Dependent Claim
34 words
A dispersion as claimed in claim 2, wherein said monoisocyanate group-containing compound is selected from isocyanatoethyl acrylate, isocyanatoethyl methacrylate, m-isopropenyl-alpha,alpha-dimethylbenzyl isocyanate, and equimolar adducts between a diisocyanate compound and an hydroxyalkyl acrylate or methacrylate.
Claim 6
Dependent Claim
129 words
A dispersion as claimed in claim 1, wherein said macromonomer A is a macromonomer having in average about 1 to about 10 polymerizable double bonds per molecule obtainable by providing a reaction product having in average about one polymerizable double bond per molecule obtained by adding an epoxy group-containing polymerizable unsaturated compound to a terminal carboxyl group of a poly(12-hydroxystearic acid) or by reacting an isocyanate group-containing polymerizable unsaturated compound with a terminal carboxyl group or secondary hydroxyl group of said poly(12-hydroxystearic acid), further reacting said reaction product with a polymerizable unsaturated monomer mixture containing a polymerizable unsaturated monomer having an epoxy group by graft copolymerization or block copolymerization to form a grafted epoxy group-containing copolymer, and reacting a polymerizable unsaturated carboxylic acid with said grafted epoxy group-containing copolymer.
Claim 7
Dependent Claim
106 words
A dispersion as claimed in claim 5, wherein said macromonomer A is a macromonomer having in average from 4 to 7 polymerizable double bonds per molecule obtainable by providing a polymerizable unsaturated group-containing reaction product having in average about one polymerizable double bond per molecule obtained as by adding glycidyl methacrylate to a terminal carboxyl group of a poly(12-hydroxystearic acid), further reacting said reaction product with a polymerizable unsaturated monomer mixture mainly composed of methyl methacrylate and containing glycidyl methacrylate by graft copolymerization or block copolymerization to form a grafted epoxy group-containing copolymer, and reacting acrylic acid or methacrylic acid with said grafted epoxy group-containing copolymer.
Claim 8
Dependent Claim
24 words
A dispersion as claimed in claim 1, wherein said macromonomer B has from 1.0 to 1.5 in average of polymerizable double bonds per molecule.
Claim 9
Dependent Claim
32 words
A dispersion as claimed in claim 1, wherein said macromonomer B has a number average molecular weight of from 3,000 to 20,000 and a hydroxyl value of from 45 to 150 mgKOH/g.
Claim 10
Dependent Claim
69 words
A dispersion as claimed in claim 1, wherein said macromonomer B is a polymer having a polymerizable double bond obtainable by reacting glycidyl acrylate or glycidyl methacrylate with a carboxyl group in a copolymer derived from a vinyl monomer having no reactive group mainly composed of a long chain alkyl ester of acrylic acid or methacrylic acid, a carboxyl group-containing vinyl monomer and optionally a hydroxyl group-containing vinyl monomer.
Claim 11
Dependent Claim
52 words
A dispersion as claimed in claim 1, wherein combination of said complementary groups is selected from the group consisting of an epoxy group/a carboxyl group, a hydroxyl group/an isocyanate group, an epoxy group/an amino group, an isocyanate group/an amino group, an alkoxysilyl group/a hydroxyl group, and an epoxy group/a phosphoric acid group.
Claim 12
Dependent Claim
40 words
A dispersion as claimed in claim 10, wherein combination of said complementary groups is selected from the group consisting of an epoxy group/a carboxyl group, a hydroxyl group/anisocyanate group, alkoxysilyl group/a hydroxyl group, and an epoxy group/a phosphoric acid group.
Claim 13
Dependent Claim
32 words
A dispersion as claimed in claim 1, wherein said vinyl monomer mixture contains from 0.5 to 20% by weight each of at least two vinyl monomers each having a complementary functional group.
Claim 14
Dependent Claim
23 words
A dispersion as claimed in claim 1, wherein said vinyl monomer mixture further contains less than 5% by weight of a polyvinyl monomer.
Claim 15
Dependent Claim
27 words
A dispersion as claimed in claim 1, wherein said vinyl monomer mixture contains no less than 50% by weight of at least one copolymerizable other vinyl monomer.
Claim 16
Dependent Claim
21 words
A dispersion as claimed in clam 14, wherein said other vinyl monomer is an ester of acrylic acid or methacrylic acid.
Claim 17
Dependent Claim
36 words
A dispersion as claimed in claim 14, wherein said macromonomer A and said macromonomer B are contained in a blend ratio A/B with a range of from 70/30 to 20/80 as weight ratio of solid content.
Claim 18
Dependent Claim
45 words
A dispersion as claimed in claim 1, wherein proportion of said dispersion stabilizer as sum of said macromonomer A and said macromonomer B to said vinyl monomer mixture is within a range of from 10/90 to 60/40 as weight ratio of dispersion stabilizer/vinyl monomer mixture.
References Cited (Backward Citations)
US4829120A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-06-17 | 1994-12-17 | 1995-06-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-06-17 | 1998-12-17 | 1999-06-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-06-17 | 2002-12-17 | 2003-06-18 | $7700.00 | Window Closed / Lapsed |