Preparation of highly oxidized RBa2 Cu4 O8 superconductors
Assignee: CALIFORNIA 300 LAKESIDE DRIVE 22ND FLOOR OAKLAND CA 94612-3550 A CORP OF, University of, Regents of
•
Filing: 1990-06-22
•
Granted: 1991-06-18
•
Expires: 2010-06-22
Abstract
Abstract Novel superconducting materials in the form of compounds, structures or phases are formed by performing otherwise known syntheses in a highly oxidizing atmosphere rather than that created by molecular oxygen at atmospheric pressure or below. This leads to the successful synthesis of novel superconducting compounds which are thermodynamically stable at the conditions under which they are formed. The compounds and structures thus formed are substantially nonsusceptible to variations in their oxygen content when subjected to changing temperatures, thereby forming a temperature-stable substantially single phase crystal.
Inventors
- 👤 Donald E. Morris
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 06:09
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/622; C04B35/64; C04B35/01; C04B35/45; H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0661; H10N60/0828; Y; Y10; Y10S; Y10S505/00; Y10S505/725; Y10S505/742; Y10S505/775; Y10S505/776; Y10S505/779; Y10S505/78
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
164 words
A process for producing a superconducting material, said process comprising: (a) forming a composition by admixing (i) a compound of a metal selected from the group consisting of yttrium and rare earth metals with (ii) a compound of barium and (iii) a compound of copper, said compounds selected from the group consisting of oxides, nitrates and carbonates thereof, in relative amounts such that the atomic ratio of said metal to barium to copper in said composition is approximately 1:2:4; (b) heating said composition in an oxygen-containing atmosphere having an oxidizing potential greater than 50% molecular oxygen at a pressure of at least 30 atmospheres to a temperature and for a length of time sufficient to effect interdiffusion of said compounds and the formation of a substantially single phase crystalline or polycrystalline lattice structure having approximately the empirical formula RBa 2 Cu 4 O 8 where R is said metal of compound (i), which lattice structure is temperature stable at temperatures below about 750° C.
Claim 2
Dependent Claim
164 words
A process for producing a superconducting material, said process comprising: (a) forming a composition by admixing (i) a compound of a metal selected from the group consisting of yttrium and rare earth metals with (ii) a compound of barium and (iii) a compound of copper, said compounds selected from the group consisting of oxides, nitrates and carbonates thereof, in relative amounts such that the atomic ratio of said metal to barium to copper in said composition is approximately 1:2:4; (b) heating said composition in an oxygen-containing atmosphere having an oxidizing potential greater than 50% molecular oxygen at a pressure of at least 30 atmospheres to a temperature and for a length of time sufficient to effect interdiffusion of said compounds and the formation of a substantially single phase crystalline or polycrystalline lattice structure having approximately the empirical formula RBa 2 Cu 4 O 8 where R is said metal of compound (i), which lattice structure is temperature stable at temperatures below about 750° C.
Claim 3
Dependent Claim
21 words
A process in accordance with claim in which said oxygen-containing atmosphere of step (b) is at least about 50% molecular oxygen.
Claim 4
Dependent Claim
22 words
A process in accordance with claim 1 in which said oxygen-containing atmosphere of step (b) is at least about 90% molecular oxygen.
Claim 5
Dependent Claim
20 words
A process in accordance with claim 1 in which said oxygen-containing atmosphere of step (b) is substantially 100% molecular oxygen.
Claim 6
Dependent Claim
20 words
A process in accordance with claim 1 in which said pressure of step (b) is at least about 50 atmospheres.
Claim 7
Dependent Claim
20 words
A process in accordance with claim 1 in which said pressure of step (b) is at least about 80 atmospheres.
Claim 8
Dependent Claim
36 words
A process in accordance with claim 1 in which said metal of compound (i) of step (a) is a member selected from the group consisting of yttrium, neodymium, samarium, europium, gadolinium, dysprosium, holmium, erbium and thulium.
Claim 9
Dependent Claim
19 words
A process in accordance with claim 1 in which said metal of compound (i) of step (a) is yttrium.
Claim 10
Dependent Claim
17 words
A process in accordance with claim 1 in which said compounds (i). (ii), and (iii) are oxides.
Claim 11
Dependent Claim
14 words
A process in accordance with claim 1 in which said compound (iii) is CuO.
Claim 12
Dependent Claim
31 words
A process in accordance with claim 1 in which said compound (ii) is a member selected from the group consisting of BaCO 3 and BaO, and said compound (iii) is CuO.
Claim 13
Dependent Claim
30 words
A process in accordance with claim 1 in which R is yttrium, said compound (i) is Y 2 O 3 , compound (ii) is BaO, and compound (iii) is CuO.
Claim 14
Dependent Claim
30 words
A process in accordance with claim 1 in which step (b) comprises heating said composition to a temperature of at least about 800° C. for at least about 8 hours.
Claim 15
Dependent Claim
30 words
A process in accordance with claim 1 in which step (b) comprises heating said composition to a temperature of at least about 900° C. for at least about 10 hours.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-06-17 | 1994-12-17 | 1995-06-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-06-17 | 1998-12-17 | 1999-06-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-06-17 | 2002-12-17 | 2003-06-18 | $7700.00 | Window Closed / Lapsed |