US5024824A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Layered automotive catalytic composite
Assignee: Umicore Autocat USA Inc
•
Filing: 1989-07-25
•
Granted: 1991-06-18
•
Expires: 2009-07-25
Abstract
Abstract This invention relates to a catalytic composite for treating an exhaust gas comprising a first support which is a refractory inorganic oxide having dispersed thereon at least one noble metal component and having dispersed immediately thereon an overlayer comprising at least one oxygen storage component and optionally a second support which is a refractory inorganic oxide. The first support may be selected from the group consisting of alumina, silica, titania, zirconia and aluminosilicates with alumina being preferred. Additionally, the noble metal component may be selected from the group consisting of platinum, palladium, rhodium, ruthernium and iridium. The oxygen storage component is an oxide of a metal which includes cerium, iron, nickel, cobalt lanthanum, neodymium, praesodymium, etc. and mixtures thereof. Cerium oxide is a preferred oxygen storage component. Finally, the second support may be selected from the group consisting of alumina, silica, titania, zirconia and aluminosilicates, with alumina preferred. This invention also relates to a process for minimizing the content of hydrogen sulfide in an automotive exhaust gas which comprises contacting said exhaust gas with a catalytic composite comprising a first support which is a refractory inorganic oxide having dispersed thereon at least one noble metal component and having dispersed immediately thereon an overlayer comprising at least one oxygen storage component and optionally a second support which is a refractory inorganic oxide.
Inventors
- 👤 Michael G. Henk
- 👤 II Jack C. Summers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 23:33
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01D53/92; B01D53/94; B01D53/9445; B01D53/945; B01J; B01J23/00; B01J23/38; B01J23/54; B01J23/56; B01J23/63; B01J23/70; B01J23/89; B01J37/00; B01J37/02; B01J37/024; Y; Y02; Y02T; Y02T10/00; Y02T10/10; Y02T10/12
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
129 words
A process for minimizing the content of hydrogen sulfide in an automotive exhaust gas which comprises contacting said exhaust gas with the catalytic composite comprising a first support which is a refractory inorganic oxide selected from the group consisting of alumina, silica, titania, zirconia, aluminosilicates and mixtures thereof, having dispersed thereon at least one noble metal component selected from the group consisting of platinum, palladium, rhodium, ruthenium, and iridium substantially in the absence of an oxygen storage component and having dispersed immediately thereon an overlayer separated from said noble metal component comprising at least one oxygen storage component which is an oxide of a metal selected from the group consisting of iron, nickel, cobalt, and the rare earths and optionally a second support which is a refractory inorganic oxide.
Claim 2
Dependent Claim
129 words
A process for minimizing the content of hydrogen sulfide in an automotive exhaust gas which comprises contacting said exhaust gas with the catalytic composite comprising a first support which is a refractory inorganic oxide selected from the group consisting of alumina, silica, titania, zirconia, aluminosilicates and mixtures thereof, having dispersed thereon at least one noble metal component selected from the group consisting of platinum, palladium, rhodium, ruthenium, and iridium substantially in the absence of an oxygen storage component and having dispersed immediately thereon an overlayer separated from said noble metal component comprising at least one oxygen storage component which is an oxide of a metal selected from the group consisting of iron, nickel, cobalt, and the rare earths and optionally a second support which is a refractory inorganic oxide.
Claim 3
Dependent Claim
15 words
The process of claim 1 where said first support is in the shape of pellets.
Claim 4
Dependent Claim
20 words
The process of claim 1 where said first support is deposited on a solid ceramic or metallic honeycomb monolithic carrier.
Claim 5
Dependent Claim
11 words
The process of claim 1 where said first support is alumina.
Claim 6
Dependent Claim
53 words
The process of claim 1 where the noble metal component is platinum, palladium or a mixture thereof, each metal present in a concentration in the range of about 0.01 to 4 weight percent of said first support and optionally rhodium in a concentration of 0.01 to 2 weight percent of said first support.
Claim 7
Dependent Claim
15 words
The process of claim 5 where the metals are a mixture of platinum and rhodium.
Claim 8
Dependent Claim
15 words
The process of claim 5 where the metals are a mixture of palladium and rhodium.
Claim 9
Dependent Claim
16 words
The process of claim 5 where the metals are a mixture of platinum, palladium and rhodium.
Claim 10
Dependent Claim
30 words
The process of claim 1 where said oxygen storage component in said overlayer is present in a concentration of about 2 to about 75 weight percent of said first support.
Claim 11
Dependent Claim
23 words
The process of claim 1 where said second support is present in a concentration of 0 to 80 weight percent of said overlayer.
Claim 12
Dependent Claim
15 words
The process of claim 1 where said oxygen storage component is a rare earth oxide.
Claim 13
Dependent Claim
13 words
The process of claim 11 where said oxygen storage component is lanthanum oxide.
Claim 14
Dependent Claim
13 words
The process of claim 11 where said oxygen storage component is cerium oxide.
Claim 15
Dependent Claim
19 words
The process of claim 11 where said oxygen storage component consists of a mixture of lanthanum and cerium oxides.
Claim 16
Dependent Claim
22 words
The process of claim 1 where said second support is selected from the group consisting of alumina, silica, titania, zirconia and aluminosilicates.
Claim 17
Dependent Claim
11 words
The process of claim 14 where said second support is alumina.
Claim 18
Dependent Claim
139 words
A process for minimizing the content of hydrogen sulfide in an automotive exhaust gas which comprises contacting said exhaust gas with the catalytic composite comprising a first support which is in the shape of a pellet and which is a refractory inorganic oxide selected from the group consisting of alumina, silica, titania, zirconia, aluminosilicates and mixtures thereof, having dispersed in the interior of said pellet at least one noble metal component selected from the group consisting of platinum, palladium, rhodium, ruthenium, and iridium substantially in the absence of an oxygen storage component and having dispersed on or near the surface of said pellet an overlayer separated from said noble metal component and comprising at least one oxygen storage component which is an oxide of a metal selected from the group consisting of iron, nickel, cobalt, and the rare earths.
Claim 19
Dependent Claim
139 words
A process for minimizing the content of hydrogen sulfide in an automotive exhaust gas which comprises contacting said exhaust gas with the catalytic composite comprising a first support which is in the shape of a pellet and which is a refractory inorganic oxide selected from the group consisting of alumina, silica, titania, zirconia, aluminosilicates and mixtures thereof, having dispersed in the interior of said pellet at least one noble metal component selected from the group consisting of platinum, palladium, rhodium, ruthenium, and iridium substantially in the absence of an oxygen storage component and having dispersed on or near the surface of said pellet an overlayer separated from said noble metal component and comprising at least one oxygen storage component which is an oxide of a metal selected from the group consisting of iron, nickel, cobalt, and the rare earths.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-06-17 | 1994-12-17 | 1995-06-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-06-17 | 1998-12-17 | 1999-06-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-06-17 | 2002-12-17 | 2003-06-18 | $7700.00 | Window Closed / Lapsed |