Process for producing styrene-based polymer

Claim 2

A process for producing a styrene polymer which comprises contacting a styrene monomer with alkylaluminoxane, adding a transition metal compound to the resulting mixture and then polymerizing the styrene monomer, wherein the styrene monomer is contacted with the alkylaluminoxane at 0° C. to 100° C. for from 5 minutes to 1 hour.

Claim 3

The process according to claim 1, wherein the styrene monomer is contacted with the alkylaluminoxane at 20° C. to 80° C. for from 10 minutes to one hour.

Claim 4

The process according to claim 1, wherein the alkylaluminoxane is a reaction product of an alkyl aluminum compound and water.

Claim 5

The process according to claim 1, wherein the said alkylaluminoxane is a chain-like alkylaluminoxane represented by the formula: ##STR4## wherein n represents the degree of polymerization and a number of 2 to 50, and R 1 represents an alkyl group having 1 to 8 carbon atoms, or a cyclic alkylaluminoxane having a recurring unit represented by the formula: ##STR5## wherein R 1 has the same meaning, as that defined above.

Claim 6

The process according to claim 1, wherein the alkylaluminoxane is subjected to heat treatment at 30° to 200° C. for from 20 minutes to 8 hours before the contacting with the styrene monomer.

Claim 7

The process according to claim 1, wherein the said alkylaluminoxane is subjected to heat treatment at 40° to 150° C. for from 30 minutes to 5 hours before the contacting with the styrene monomer.

Claim 8

The process according to claim 1, wherein the said alkylaluminoxane contains 50% or less of a high magnetic field component of methyl proton signal region based on aluminum-methyl group (Al--CH 3 ) bonding measured by the proton nuclear magnetic resonance method.

Claim 9

The process according to claim 3, wherein the alkyl aluminum compound is reacted with water in the presence of an aluminum compound.

Claim 10

The process according to claim 8, wherein the said aluminum compound is a compound represented by the formula: AlR.sup.2.sub.i R.sup.3.sub.j R.sup.4.sub.3-(i+j) (III) wherein R 2 , R 3 and R 4 each represent a hydrogen atom, an alkyl group or alkoxy group having 1 to 8 carbon atoms, or a halogen atom; i and j each are integers of 0 to 3 and i+j is an integer of 0 to 3.

Claim 11

The process according to claim 9, wherein the said aluminum compound is selected from the group consisting of trimethylaluminum, triethylaluminum, tripropylaluminum, triisobutylaluminum, trioctylaluminum, chlorodimethylaluminum, chlorodiethylaluminum, hydrogenated diethylaluminum, hydrogenated diisobutylaluminum and diethylaluminum ethoxide.

Claim 12

The process according to claim 1, wherein the said transition metal compound is selected from a titanium compound, a zirconium compound and a vanadium compound.

Claim 13

The process according to claim 11, wherein the said titanium compound is used and is at least one compound selected from the group consisting of a titanium compound and a titanium chelate compound represented by the formula: TiR.sup.5.sub.a R.sup.6.sub.b R.sup.7.sub.c R.sup.8.sub.4-(a+b+c)(IV) and TiR.sup.5.sub.d R.sup.6.sub.e R.sup.7.sub.3-(d+e) (V) wherein R 5 , R 6 , R 7 and R 8 each represent a hydrogen atom, an alkyl group having 1 to 20 carbon atoms, an alkoxy group having 1 to 20 carbon atoms, an aryl group having 6 to 20 carbon atoms, an alkylaryl group, an arylalkyl group, an acyloxy group having 1 to 20 carbon atoms, a cyclopentadienyl group, a substituted cyclopentadienyl group, an indenyl group or a halogen atom; a, b and c each are an integer from 0 to 4; and d and e each are an integer from 0 to 3.

Claim 14

The process according to claim 11, wherein said titanium compound is used and is a compound represented by the formula: TiRXYZ (VI) wherein R represents a cyclopentadienyl group, a substituted cyclopentadienyl group or an indenyl group; X, Y and Z are independently hydrogen atom, an alkyl group having 1 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, an aryl group having 6 to 20 carbon atoms, an aryloxy group having 6 to 20 carbon atoms, an arylalkyl group having 6 to 20 carbon atoms or a halogen atom.

Claim 15

The process according to claim 11, wherein the said titanium compound is used and is a condensed titanium compound represented by the formula: ##STR6## wherein R 9 and R 10 each represent a halogen atom, an alkoxy group having 1 to 20 carbon atoms or an acyloxy group; and m is an integer of 2 to 20.

Claim 16

The process according to claim 11, wherein the said zirconium compound is used and is selected from tetrabenzylzirconium, zirconium tetraethoxide, zirconium tetrabutoxide, bisindenylzirconium dichloride, trisiopropoxyzirconium chloride, zirconium benzyl dichloride and tributoxyzirconium chloride.

Claim 17

The process according to claim 11, wherein the said vanadium compound is used and is selected from bisacetylacetonatovanadium, triacetylacetonatovanadium, triethoxyvanadyl and tripropoxyvanadyl.

Claim 18

The process according to claim 10, wherein said styrene monomer is styrene, p-methylstyrene, m-methylstryrene, o-methyl-styrene, 2,4-dimethylstyrene, 2,5-dimethylstyrene, 3,4-dimethylstyrene, 3,5-dimethylstyrene, p-ethylstyrene, m-ethylstryrene, p-tert-butylstyrene; p-chlorostyrene, m-chlorostyrene, o-chlorostyrene, p-bromostryrene, m-bromostyrene, o-methyl-bromostyrene, p-fluorostyrene, m-fluorostyrene, o-fluorostyrene, o-methyl-p-fluorostyrene; p-methoxystyrene, m-methoxystyrene, o-methoxystyrene, p-ethoxystyrene, m-ethoxystyrene; o-ethoxystyrene; p-carboxymethylstyrene, m-carboxymethylstyrene, o-carboxymethylstyrene; p-vinylbenzyl-propyl ether; or a mixture of two or more of the above.

Claim 19

The process according to claim 11, wherein said styrene monomer is styrene, p-methylstyrene, m-methylstyrene, o-methyl-styrene, 2,4-dimethylstyrene, 2,5-dimethylstyrene, 3,4-dimethylstyrene, 3,5-dimethylstyrene, p-ethylstyrene, m-ethylstyrene, p-tert-butylstyrene; p-chlorostyrene, m-chlorostyrene, o-chlorostyrene, p-bromostyrene, m-bromostyrene, o-methyl-bromostyrene, p-fluorostyrene, m-fluorostyrene, o-fluorostyrene, o-methyl-p-fluorostyrene; p-methoxystyrene, m-methoxystyrene, o-methoxystyrene, p-ethoxystyrene, m-ethoxystyrene; o-ethoxystyrene; p-carboxymethylstyrene, m-carboxymethylstyrene, o-carboxymethylstyrene; p-vinylbenzyl-propyl ether; or a mixture of two or more of the above.

Claim 20

The process according to claim 12, wherein the titanium compound is cyclopentadienyltrimethyltitanium, cyclopentadienyltriethyltitanium, cyclopentadienyltripropyltitanium, cyclopentadienyltributyltitanium, methylcyclopentadienyltrimethyltitanium, 1,2-dimethylcyclopentadienyltrimethyltitanium, pentamethylcyclopentadienyltrimethyltitanium, pentamethylcyclopentadienyltriethyltitanium, pentamethylcyclopentadienyltripropyltitanium, pentamethylcyclopentadienyltributyltitanium, cyclopentadienylmethyltitanium dichloride, cyclopentadienylethyltitanium dichloride, pentamethylcyclopentadienylmethyltitanium dichloride, pentamethylcyclopentadienylethyltitanium dichloride, cyclopentadienyldimethyltitanium monochloride, cyclopentadienyldiethyltitanium monochloride, cyclopentadienyltitanium trimethoxide, cyclopentadienyltitanium triethoxide, cyclopentadienyltitanium tripropoxide, cyclopentadienyltitanium triphenoxide, pentamethylcyclopentadienyltitanium trimethoxide, pentamethylcyclopentadienyltitanium triethoxide, pentamethylcyclopentadienyltitanium tripropoxide, pentamethylcylopentadienyltitanium tributoxide, pentamethylcyclopentadienyltitanium triphenoxide, cyclopentadienyltitanium trichloride, pentamethylcyclopentadienyltitanium trichloride, cyclopentadienylmethoxytitanium dichloride, cyclopentadienyldimethoxytitanium chloride, pentamethylcyclopentadienylmethoxytitanium dichloride, cyclopentadienyltribenzyltitanium, pentamethylcyclopentadienylmethyldiethoxytitanium, indenyltitanium trichloride, indenyltitanium trimethoxide, indenyltitanium triethoxide, indenyltrimethyltitanium and indenyltribenzyltitanium.