Process for the manufacture of polymers

Claim 2

A process for the preparation of polymers containing at least one hydrophilic monomeric component and at least one hydrophobic monomeric component comprising the step of polymerizing the monomers in the presence of free radical polymerization initiators in an aqueous medium consisting of water and a cosolvent, wherein the amount of water miscible cosolvent is monitored so as to maintain the ratio of water to cosolvent equal or greater than unity during the reaction, thereby keeping the polymer as it forms in a sufficiently mobile condition and preventing homopolymerization and precipitation of the polymer from the hydrophobic monomer; thereby producing a polymer as a relatively high solids, low viscosity, opaque or semi-opaque product which is stable and slightly cloudy, opaque or semi-opaque, which exhibits no gelling, coagulation or product separation on standing and which, upon dilution to 0.25% solids content w/w, has a turbidity of at least 10 Nephelometric Turbidity units.

Claim 3

The process of claim 1 wherein the hydrophilic monomer is selected from the group consisting of ethylenically unsaturated amides and their N-substituted derivatives, ethylenically unsaturated carboxylic acids or dicarboxylic acids, ethylenically unsaturated quaternary ammonium, compounds, sulfoalkyl esters of unsaturated carboxylic acids, aminoalkyl esters of unsaturated carboxylic acid, vinyl or allyl amines, diallyl amines and diallyl ammonium compounds, vinyl heterocyclic amides, vinyl aryl sulfonates, vinyl alcohol obtained by the hydrolysis of vinyl acetate, acrolein, allyl alcohol, vinyl acetic acid, sodium vinyl sulfonate, sodium allyl sulfonate, their corresponding salts or mixtures thereof.

Claim 4

The process of claim 1 wherein the hydrophobic monomer is selected from the group consisting of aliphatic hydrocarbon moieties having at least five carbons, polynuclear aromatic hydrocarbon groups alkylaryls wherein the alkyl groups have one or more carbon atoms, haloalkyls of 5 or more carbon atoms, polyalkylenoxy groups wherein alkylene is propylene or high alkylene and there is at least one alkyleneoxy unit per hydrophobic moiety, siloxanes and mixtures thereof.

Claim 5

The process of claim 3 wherein the hydrophobic monomer is selected from the group consisting of the higher alkyl esters of alpha, beta ethylenically unsaturated carboxylic acids, alkyl esters and half esters derived from the reactions of alkanols having from 5 to 50 carbon atoms with ethylenically unsaturated carboxylic acids, alkylaryl esters of ethylenically unsaturated carboxylic acids, N-alkyl - ethylenically unsaturated amides, and derivatives thereof, a-olefins, vinyl alkylates wherein alkyl has at least 4 carbon atoms, vinyl alkyl esters, N-vinyl amides, alkylstyrenes, and mixtures thereof.

Claim 6

The process of claim 1 wherein the ratio of hydrophilic to hydrophobic monomers varies from about 100:1 to 5:1.

Claim 7

The process of claim 1 wherein the hydrophobic and hydrophilic monomers are selected so as to produce a polymer of the formula: ##STR8## wherein z is 1; (x+y): z is from 5:1 to 100:1; in which the monomer units may be in random order; y being from 0 up to a maximum equal to the value of x: and n is at least 1; R 1 represents --CO--O, --O--, --O--CO--, --CH 2 --, --CO--NH-- or is absent; R 2 represents from 1 to 50 independently selected alkyleneoxy groups, preferably ethylene oxide or propylene oxide groups, or is absent, provided that when R 3 is absent and R 4 represents hydrogen, then R 2 must contain an alkyleneoxy group with at least 3 carbon atoms; R 3 represents a phenylene linkage, or is absent; R 4 represents hydrogen or a C 5-24 alkyl or C 5-24 alkenyl group, with the provisos that: (a) when R 1 represents --O--CO--, R 2 and R 3 must be absent and R 4 must contain at least 5 carbon atoms and (b) when R 2 is absent, R 4 is not hydrogen and when R 3 is absent then R 4 must contain at least 5 carbon atoms; R 5 represents hydrogen or a group of formula --COOA 4 ; R 6 represents hydrogen or C 1-4 alkyl; and A 1 , A 2 , A 3 and A 4 are independently selected from hydrogen, alkali metals, alkaline earth metals, ammonium and amine bases.

Claim 8

The process of claim 1 wherein the hydrophobic and hydrophilic monomers are selected so as to produce a polymer of the formula: ##STR9## wherein: Q 1 is a multifunctional monomer, wherein the monomers of the polymer may be connected to Q 1 in any direction, in any order; Q 2 is a molecular entity of the formula: ##STR10## wherein z is 1; (x+y): z is from 5:1 to 100:1; in which the monomer units may be in random order; y being from 0 up to a maximum equal to the value of x: and n is at least 1; v is 1; and (x+y+p+q+r): z is from 5:1 to 100:1 in which the monomer units may be in random order; R 1 represents --CO--O, --O--, --O--CO--, --CH 2 --, --CO--NH-- or is absent; R 2 represents from 1 to 50 independently selected alkyleneoxy groups, preferably ethylene oxide or propylene oxide groups, or is absent, provided that when R 3 is absent and R 4 represents hydrogen, then R 2 must contain an alkyleneoxy group with at least 3 carbon atoms; R 3 represents a phenylene linkage, or is absent; R 4 represents hydrogen or a C 5-24 alkyl or C 5-24 alkenyl group, with the provisos that: (a) when R 1 represents --O--CO--, R 2 and R 3 must be absent and R 4 must contain at least 5 carbon atoms and (b) when R 2 is absent, R 4 is not hydrogen and when R 3 is absent then R 4 must contain at least 5 carbon atoms; R 5 represents hydrogen or a group of formula --COOA 4 ; R 6 represents hydrogen or C 1-4 alkyl; Q 1 is a multifunctional monomer, wherein the monomers of the polymer may be connected to Q 1 in any direction, in any order; R 7 and R 8 represent --CH 3 or --H; R 9 and R 10 represent substituent groups selected from the group consisting of amino, amine, amide, sulphonate, sulphate, phosphonate, phosphate, hydroxy, carboxyl and oxide groups or (C 2 H 4 O) t H, wherein t is from 1-50, and wherein the monomer units may be in random order; and A 1 , A 2 , A 3 and A 4 are independently selected from hydrogen, alkali metals, alkaline earth metals, ammonium and amine bases.

Claim 9

The process of claim 1 wherein the hydrophobic and hydrophilic monomers are selected so as to produce a polymer of the formula: ##STR11## wherein Q 3 is derived from a monomeric unit: ##STR12## Q 4 is derived from the molecular entity: ##STR13## and Q 5 is derived from a monomeric unit: ##STR14## R 1 represents --CO--O, --O--, --O--CO--, --CH 2 --, --CO--NH-- or is absent; R 2 represents from 1 to 50 independently selected alkyleneoxy groups, preferably ethylene oxide or propylene oxide groups, or is absent, provided that when R 3 is absent and R 4 represents hydrogen, then R 2 must contain an alkyleneoxy group with at least 3 carbon atoms; R 3 represents a phenylene linkage, or is absent; R 4 represents hydrogen or a C 5-24 alkyl or C 5-24 alkenyl group, with the provisos that: R 5 represents hydrogen or a group of formula --COOA 4 ; R 6 represents hydrogen or C 1-4 alkyl; and (a) when R 1 represents --O--CO--, R 2 and R 3 must be absent and R 4 must contain at least 5 carbon atoms and (b) when R 2 is absent, R 4 is not hydrogen and when R 3 is absent then R 4 must contain at least 5 carbon atoms; (a+b+c): Q 4 is from 5:1 to 100:1, in which the monomer units may be in random order, a, b, c, d, e, f, g, h may be an integer of zero, n is at least 1; w is zero to 4; R 11 is independently selected from hydrogen or C 1 -C 4 alkyl; R 12 is independently selected from C 5 to C 24 alkyl or alkenyl, aryl, cycloalkyl, hydroxyalkyl, or alkoxyalkyl; and B 1 , B 2 , B 3 , B 4 are organic or inorganic anions.

Claim 10

The process of claim 1 wherein the cosolvent is selected from the group consisting of isopropanol, n-propanol, acetone, lower (C 1 to C 4 ) alcohols, esters, and ketones.

Claim 11

The process of claim 9 wherein the cosolvent is isopropanol or normal propanol.

Claim 12

The process of claim 1 wherein the free radical polymerization initiator is a thermal decomposition initiator.

Claim 13

The process of claim 1 wherein the free radical polymerization initiator is a redox initiator.

Claim 14

The process of claim 1 wherein the initiator is present in an amount of 0.1 to 5% by weight based on the sum of the monomers.

Claim 15

The process of claim 1 wherein the monomers are present in a total weight of 10 to 55% of the polymerization mixture.

Claim 16

The process of claim 1 wherein the hydrophilic monomer is acrylic acid, the hydrophobic monomer is a methacrylic ester of chain length 10 to 18, isopropanol or normal propanol is used as the cosolvent, and wherein the water to cosolvent ratio during the reaction is within the range of 1.4 to 3.7.

Claim 17

The process of claim 1 wherein the hydrophilic monomer is acrylic acid, the hydrophobic monomer is a half ester maleate containing 12 to 18 carbon atoms, isopropanol or normal propanol is used as the cosolvent and wherein the water to cosolvent ratio during the reaction is within the range of 1.2 to 5.3.

Claim 18

The process of claim 1 wherein the hydrophilic monomers are acrylic acid and maleic acid, the hydrophobic monomer is a methacrylate ester of chain length 10 to 18, isopropanol or normal propanol is used as the cosolvent and wherein the water to cosolvent ratio during the reaction is within the range of 1.0 to 3.6.

Claim 19

The process of claim 1 wherein the hydrophilic monomer is dimethyl diallyl ammonium chloride, the hydrophobic monomer is a methacrylate ester of chain length 10 to 18, isopropanol or normal propanol is used as the cosolvent, and wherein the water to cosolvent ratio during the reaction is within the range of 1.6 to 8.0.

Claim 20

The process of claim 1 wherein the hydrophilic monomer is acrylic acid, the hydrophobic monomer is a vinyl ester, isopropanol or normal propanol is used as the cosolvent and wherein the water to cosolvent ratio during the reaction is within the range of 1.4 to 3.7.