Method of forming patterned oxide superconducting films

Claim 2

A process to produce a high T c electrically superconducting article having a pattern, which method comprises: (A) combining compounds selected from: (i) at least one unsaturated organic acid metal salt of a Group IIA element, (ii) at least one unsaturated organic acid metal salt of bismuth or a Group III A, III B, IVA, VA element, and (iii) an unsaturated organic acid copper salt, to produce a solution or a suspension in an organic solvent, wherein the ratio of metal atoms in (i), (ii) and (iii) is selected wherein each unsaturated organic acid metal salt above contains at least one C=C bond or two or more C.tbd.C bonds, to produce a high T c electrically superconducting article upon its subsequent high temperature pyrolysis in an oxygen or air atmosphere; (B) coating the surface of an article with the solution of step (A); (C) covering selected portions of the coated article with a mask pattern; (D) subjecting the coated surface to electromagnetic radiation effective to polymerize and crosslink the portion of the compounds (i), (ii) and (iii) exposed to the radiation; (E) removing the unpolymerized and uncrosslinked compounds (i), (ii) and (iii), to produce a solid residue on the coated surface; (F) calcining the solid residue of step (E) in sufficient oxygen or air at a temperature of between 700° and 900° C. for a time effective to obtain a mixed metal oxide; and (G) slowly cooling the solid residue obtained at a temperature of between about 900° C. and about 500° C. at a rate of between about 1° and 5° C. per minute in excess air or oxygen and subsequently slowly annealing the mixed metal oxide obtained in flowing oxygen or air by slowly cooling from about 500° C. to ambient temperature at a rate of between about 1° and 5° C. per minute.

Claim 3

The process of claim 1 wherein in step A the unsaturated organic acid has is at least one C=C and the process further includes at least one crosslinking compound and a polymerization catalyst

Claim 4

The process of claim 1 wherein in step (B) the surface of the article is precoated with a silane coupling or silanizing agent to improve adhesion of the coating.

Claim 5

The process of claim 1 wherein the at least one unsaturated organic acid group for each element is independently selected from organic -C.tbd.C-C.tbd.C- containing acids or from: ##STR6## where R 11 and R 12 in each group is independently selected from hydrogen, alkyl, aryl, alkenyl or dialkenyl each group independently having from 1 to 10 carbon atoms, or substituted alkyl, aryl, alkenyl or dialkenyl each group independently having from 1 to 10 carbon atoms; R 13 in each group is independently selected from hydrogen or alkyl having from 1 to 6 carbon atoms; and R 14 in each group independently selected from a direct bond (-), or -(CH 2 ) n - where n is an integer from 1 to 10.

Claim 6

The process of claim 1 wherein the Group IIIA, IIIB, IVA, VA elements are each independently selected from bismuth, lanthanum, yttrium, praseodymium, lead, thallium, samarium, europium, gadolinium, dysprosium, holmium, erbium or mixtures thereof, the Group IIA elements are each independently selected from barium, strontium, calcium or mixtures thereof, and (iii) copper.

Claim 7

The process of claim 1 wherein bismuth is present in step (A) having five substituents having at least one unsaturated organic acid and the remaining substituents are selected from phenyl, tolyl, xylyl or naphthyl.

Claim 8

The process of claim 6 wherein bismuth is present in step (A) as triphenylbismuth dimethacrylate.

Claim 9

The process of claim 4 wherein the at least one organic acid group has two or more conjugated C.tbd.C bonds of the structure CH 3 -(CH 2 ) m -C.tbd.C-C.tbd.C(-CH 2 ) n (-C=O)-O-wherein m is an integer between 1 and 10, and n is an integer between 1 and 8.

Claim 10

The process of claim 1 wherein in step (A)(i) the Group IIA elements are calcium (oleate)(methacrylate) and strontium (methacrylate) 2 , in step (A)(iii) the salt is triphenyl bismuth (V) dimethacrylate, in step (A) (iii) the salt is copper (II) dimethacrylate, in a metal ratio Bi/Sr/Ca/Cu of about 2 to 2 to 1 to 2, dissolved in pyridine, contacted with pentaerythritol triacrylate and a photoinitiator, in step (D) subjecting the coating to ultraviolet radiation for a time effective to crosslink the materials exposed, in step (E) contacting the exposed film with n-butanol and diethylether to remove unpolymerized materials, and in step (F) heating the crosslinked film to 860° C. at about 200° C. per hr, heating at 860° C. for about 1 hr and cooling the oxide at a rate of about 1° C. per minute to ambient temperature.

Claim 11

A process of manufacturing a high T c electrically superconducting article of a specific pattern, which method comprises: (a) preparing a solution comprising an organic solvent and at least three carboxylic acid metal compounds selected from the following structures: ##STR7## R.sup.2 M.sup.2 R.sup.7 (II) R.sup.3 -M.sup.3 -R.sup.8 (III) R.sup.4 -M.sup.4 -R.sup.9 (IV) R.sup.5 -M.sup.5 -R.sup.10 (V) R.sup.19 -M.sup.6 (VI) ##STR8## wherein R.sup.1, R.sup.2, R.sup.3, R.sup.4 and R.sup.5 are each independently selected from organic -C.tbd.C-.tbd.C- containing acids or from: ##STR9## wherein R.sup.11 and R.sup.12 in each of R.sup.1 to R.sup.5 is independently selected from hydrogen, alkyl, aryl, alkenyl or dialkenyl each group independently having from 1 to 10 carbon atoms, or substituted alkyl, aryl, alkenyl or dialkenyl each group independently having from 1 to 10 carbon atoms; R 13 in each of R 1 to R 5 is independently selected from hydrogen or alkyl having from 1 to 6 carbon atoms; and R 14 in each of R 1 to R 5 is independently selected from a direct bond (-), or -(CH 2 ) n - where n is an integer from 1 to 10; R 6 , R 7 , R 8 , R 9 and R 10 are each independently selected from R 1 or -(C=O)R 15 wherein R 15 is alkyl having from 1 to 20 carbon atoms, R 16 , R 17 and R 18 are present and are selected from phenyl, tolyl or xylyl only when M 1 as bismuth is present, R 19 is independently selected from R 1 to R 5 or R 6 to R 10 , R 20 , R<and R 22 are each independently selected from R 1 to R 5 or R 6 to R 10 , R 23 , R 24 , R 25 and R 26 are each independently selected from R 1 to R 5 or R 6 to R 10 , M 1 and M 2 are each independently selected from bismuth, lead, samarium, europium, or mixtures thereof, M 3 and M 4 are each independently selected from barium, strontium, calcium or mixtures thereof, M 5 is copper; M 6 is copper; M 7 is selected from thallium, yttrium, bismuth, aluminum, lanthanum, samarium, dysprosium or holmium, and M 8 is selected from lead, tin or hafnium, with the proviso that compounds (I) to (VIII), are selected to comprise: (i) at least one unsaturated organic acid metal salt of Group IIA element, (ii) at least one unsaturated organic acid metal salt of Group IIIA, IIIB, IVA and VA element, and (iii) an unsaturated organic acid copper, wherein the ratio of metal atoms in Compounds I, II, III, IV, V, VI, VII and VIII is selected to produce a high T c electrically superconducting article upon subsequent oxidation; (b) coating the surface of an article with the solution of step (a), optionally containing a crosslinking agent and initiator; (c) covering selected portions of the coated article with a mask pattern; (d) subjecting the coated surface to electromagnetic radiation effective to polymerize and crosslink the portion of the compounds I, II, III, IV, V, Vi, VII and VII exposed to the radiation; (e) removing the unpolymerized and uncrosslinked compounds I, II, III, IV, V, VI, VII and VIII, to produce a solid residue on the coated surface, (f) calcining the solid residue of step (e) in sufficient oxygen or air at a temperature of between 700° and 1000° C. for a time effective to obtain a mixed metal oxide; and (g) slowly cooling the solid residue obtained at a temperature of between about 1000° C. and 500° C. at a rate of between about 1° and 5° C. per minute in excess air or oxygen concurrently slowly annealing the mixed metal oxide obtained in flowing oxygen or air by slowly cooling from about 500° C. to 200° C. at a rate of between about 1° and 5° C. per minute.

Claim 12

A process of manufacturing a high T c electrically superconducting article of a specific pattern, which method comprises: (a) preparing a solution comprising an organic solvent and at least three carboxylic acid metal compounds selected from the following structures: ##STR7## R.sup.2 M.sup.2 R.sup.7 (II) R.sup.3 -M.sup.3 -R.sup.8 (III) R.sup.4 -M.sup.4 -R.sup.9 (IV) R.sup.5 -M.sup.5 -R.sup.10 (V) R.sup.19 -M.sup.6 (VI) ##STR8## wherein R.sup.1, R.sup.2, R.sup.3, R.sup.4 and R.sup.5 are each independently selected from organic -C.tbd.C-.tbd.C- containing acids or from: ##STR9## wherein R.sup.11 and R.sup.12 in each of R.sup.1 to R.sup.5 is independently selected from hydrogen, alkyl, aryl, alkenyl or dialkenyl each group independently having from 1 to 10 carbon atoms, or substituted alkyl, aryl, alkenyl or dialkenyl each group independently having from 1 to 10 carbon atoms; R 13 in each of R 1 to R 5 is independently selected from hydrogen or alkyl having from 1 to 6 carbon atoms; and R 14 in each of R 1 to R 5 is independently selected from a direct bond (-), or -(CH 2 ) n - where n is an integer from 1 to 10; R 6 , R 7 , R 8 , R 9 and R 10 are each independently selected from R 1 or -(C=O)R 15 wherein R 15 is alkyl having from 1 to 20 carbon atoms, R 16 , R 17 and R 18 are present and are selected from phenyl, tolyl or xylyl only when M 1 as bismuth is present, R 19 is independently selected from R 1 to R 5 or R 6 to R 10 , R 20 , R<and R 22 are each independently selected from R 1 to R 5 or R 6 to R 10 , R 23 , R 24 , R 25 and R 26 are each independently selected from R 1 to R 5 or R 6 to R 10 , M 1 and M 2 are each independently selected from bismuth, lead, samarium, europium, or mixtures thereof, M 3 and M 4 are each independently selected from barium, strontium, calcium or mixtures thereof, M 5 is copper; M 6 is copper; M 7 is selected from thallium, yttrium, bismuth, aluminum, lanthanum, samarium, dysprosium or holmium, and M 8 is selected from lead, tin or hafnium, with the proviso that compounds (I) to (VIII), are selected to comprise: (i) at least one unsaturated organic acid metal salt of Group IIA element, (ii) at least one unsaturated organic acid metal salt of Group IIIA, IIIB, IVA and VA element, and (iii) an unsaturated organic acid copper, wherein the ratio of metal atoms in Compounds I, II, III, IV, V, VI, VII and VIII is selected to produce a high T c electrically superconducting article upon subsequent oxidation; (b) coating the surface of an article with the solution of step (a), optionally containing a crosslinking agent and initiator; (c) covering selected portions of the coated article with a mask pattern; (d) subjecting the coated surface to electromagnetic radiation effective to polymerize and crosslink the portion of the compounds I, II, III, IV, V, Vi, VII and VII exposed to the radiation; (e) removing the unpolymerized and uncrosslinked compounds I, II, III, IV, V, VI, VII and VIII, to produce a solid residue on the coated surface, (f) calcining the solid residue of step (e) in sufficient oxygen or air at a temperature of between 700° and 1000° C. for a time effective to obtain a mixed metal oxide; and (g) slowly cooling the solid residue obtained at a temperature of between about 1000° C. and 500° C. at a rate of between about 1° and 5° C. per minute in excess air or oxygen concurrently slowly annealing the mixed metal oxide obtained in flowing oxygen or air by slowly cooling from about 500° C. to 200° C. at a rate of between about 1° and 5° C. per minute.

Claim 13

The process of claim 10 wherein in step (b) the surface of the article is precoated with a silanizing agent or a silane coupling agent to improve adhesion of the coating.

Claim 14

The process of claim 10 wherein in step (a) the organic solvent is pyridine.

Claim 15

The process of claim 10 wherein the surface of the substrate to be coated is first treated with a non-metallic surfactant.

Claim 16

The process of claim 11 wherein the composition of step (a) further includes a nonmetallic surfactant.

Claim 17

The process of claim 14 wherein the surfactant is independently selected from SURFYNOL® 104E, TRITON® or TWEEN® surfactants.

Claim 18

The process of claim 1 wherein the super-conducting oxide formed is independently selected from: YBa 2 Cu 3 O 7 ; Bi 2 Sr 2 CaCu 2 O 8 ; Tl 2 Ba 2 Ca p-1 Cu p O 4+2p (where p=2,3), (La 1-q M q ) 2 CuO 4-r (where M=Ba, Sr and Ca; and O≦q<0.2) and r≦0.1; AB a 2Cu 3 O 7-s (where A=rare earth element, s<0.45); BiAl 1-t CaSrCuO 7-2 ; Bi 2 Al 1-t (Ca 1-u Sr u )Cu 2 O 7-s ; Bi 2 Al 1-t (Ca 1-u Sr u ) 2 Cu 2 O 7-s ; Bi 2 Al 1-t (Ca 1-u Sr u ) 2 Cu 2 O 8-s (where O≦t≦0.3 and 0.4≦u≦0.95; Pb 2 Sr 2 ACu 3 O 8 where A=lanthanide; Tl 1 Ca n-1 Ba 2 Cu n O 2 (n+3) (n=1,2,3); Bi 2 Sr 2 Cu 2 O 7-s ; Ba 2 YCu 3 O q ; Bi 2 Sr 2 CaCu 2 Oq; Tl 2 Ba 2 Ca w-1 Cu w O 5+2w-1+x (where w=1,2,3 and x is between 0 and 20); Bi 2 Sr 2 Ca w-1 Cu w O 5+2w-1-q ; or Tl 2 Ca 2 Ba 2 Cu 3 O 10 .

Claim 19

The process of claim 1 wherein in step A, the metal organic salts have at least one metal compound having different unsaturated organic groups attached, at least one group having from 3 to 9 carbon atoms and at least one having from 10 to 20,carbon atoms.

Claim 20

The process of claim 17 wherein at least one group is CH2=C-(CH )(C=O)-O-, and one group on the oleic acid group.

Claim 21

The process of claim 10 wherein the superconducting oxide formed is independently selected from: YB a 2Cu 3 O 7 ; Bi 2 Sr 2 CaCu 2 O 8 ; Tl 2 Ba 2 Ca p-1 Cu p O 4+2p (where p=2,3); (La 1-q M q ) 2 CuO 4-r (where M=Ba, Sr and Ca; and O<q<0.2) and r<0.1; ABa 2 Cu 3 O 7-s (where A=rare earth element, s<0.45); BiAl 1-t CaSrCuO 7-s ; Bi 2 Al 1-t (Ca 1-u Sr u )Cu 2 O 7-s ; Bi 2 Al 1-t (Ca 1-u Sr u ) 2 Cu 2 O 7-s ; Bi 2 Al 1-t (Ca 1-u Sr u ) 2 Cu 2 O 8-s (where O<t<0.3 and 0.4<u<0.95; Pb 2 Sr 2 ACu 3 O 8 where A=lanthanide; Tl 1 Ca n-1 Ba 2 Cu n O 2 (n+3) (n=1,2,3); Bi 2 Sr 2 Cu 2 O 7-s ; Ba 2 YCu 3 O q ; Bi 2 Sr 2 CaCu 2 O q ; Tl 2 Ba 2 Ca w-1 Cu w O 5+2w-1+x (where w=1,2,3 and x is between 0 and 20); Bi 2 Sr 2 Ca w-1 Cu w O 5+2w-1-q ; or Tl 2 Ca 2 Ba 2 Cu 3 O 10 .

Claim 22

The process of claim 10 wherein in step (a) the organic metal groups have at least one metal compound having different unsaturated groups attached at least one group having from 3 to 9 carbon atoms, and at least one group having from 10 to 20 carbon atoms.

Claim 23

The process of claim 20 wherein at least one group is CH 2 =C(CH 3 )(C=O)-O- and one group is the oleic group.

Claim 24

The process of claim 1 wherein in step (A) the metal atoms comprise Bi-Sr-Ca-Cu-O in a ratio of about 2212.

Claim 25

The process of claim 22 wherein in step (A) the organic metal compounds comprise triphenyl bismuth (V) dimethacrylate, strontium (II) dimethyacrylate, calcium (II) (oleate) methyacrylate, and copper (II) dimethacryalte.