Compositions involving V2 O3 -ZRO2 -TIO2
Assignee: Texaco Inc
•
Filing: 1990-03-21
•
Granted: 1991-06-04
•
Expires: 2010-03-21
Abstract
Abstract The present invention pertains to novel solid solutions involving V 2 O 3 , ZrO 2 and TiO 2 and the method for their preparation. The compositions involving V 2 O 3 , ZrO 2 and TiO 2 fall within the shaded area of a polygon in a ternary composition diagram of V 2 O 3 , ZrO 2 and TiO 2 as shown in the drawing herein e.g., FIG. 1. These materials may be used as an oxidation catalyst or in the manufacture of high temperature refractories.
Inventors
- 👤 Arnulf Muan
- 👤 Mitri S. Najjar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:10
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/48; C04B35/49; B; B01; B01J; B01J23/00; B01J23/16; B01J23/20; B01J23/22; C04B35/495
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
292 words
A method of preparing compositions, from V 2 O 3 , ZrO 2 and TiO 2 that fall within the shaded area circumscribed by ABCDF as shown in the disclosed figure, and wherein said method comprises the steps of (1) heating V 2 O 5 powder having a particle size of less than about 50 microns in an atmosphere in which the partial pressure of oxygen is in the range of 10 -8 to 10 -10 atmospheres while gradually increasing the temperature over a temperature range of about 600° C. to 1300° C. and holding the temperature at about 1300° C. for a period to ensure complete reduction of all vanadium to V 3+ ; (2) heating TiO 2 and ZrO 2 powders each having a particle size of less than about 50 microns for a period of about 10 to 14 hrs. at a temperature in the range of about 600° C. to 800° C. for TiO 2 and about 1000° C. to 1200° C. for ZrO 2 ; (3) thoroughly grinding together about 24 to 98 wt. % of V 2 O 3 from (1), with about 2 to 50 wt. % of ZrO 2 and about 0 to 66 wt. % of TiO 2 from (2) to produce a mixture having a grain size of less than about 50 microns; (4) pelletizing the mixture from (3) at a pressure of about 5,000 psi; and (5) heating and reacting together the pellets from (4) at a temperature in the range of about 1100° C. to 1700° C. for a period in the range of about 12 to 48 hrs. in an atmosphere in which the partial pressure of oxygen is in the range of 10 -10 to 10 -5 atmosphere.
Claim 2
Independent Claim
292 words
A method of preparing compositions, from V 2 O 3 , ZrO 2 and TiO 2 that fall within the shaded area circumscribed by ABCDF as shown in the disclosed figure, and wherein said method comprises the steps of (1) heating V 2 O 5 powder having a particle size of less than about 50 microns in an atmosphere in which the partial pressure of oxygen is in the range of 10 -8 to 10 -10 atmospheres while gradually increasing the temperature over a temperature range of about 600° C. to 1300° C. and holding the temperature at about 1300° C. for a period to ensure complete reduction of all vanadium to V 3+ ; (2) heating TiO 2 and ZrO 2 powders each having a particle size of less than about 50 microns for a period of about 10 to 14 hrs. at a temperature in the range of about 600° C. to 800° C. for TiO 2 and about 1000° C. to 1200° C. for ZrO 2 ; (3) thoroughly grinding together about 24 to 98 wt. % of V 2 O 3 from (1), with about 2 to 50 wt. % of ZrO 2 and about 0 to 66 wt. % of TiO 2 from (2) to produce a mixture having a grain size of less than about 50 microns; (4) pelletizing the mixture from (3) at a pressure of about 5,000 psi; and (5) heating and reacting together the pellets from (4) at a temperature in the range of about 1100° C. to 1700° C. for a period in the range of about 12 to 48 hrs. in an atmosphere in which the partial pressure of oxygen is in the range of 10 -10 to 10 -5 atmosphere.
Claim 3
Dependent Claim
60 words
The method of claim 1 wherein said figure the amounts of V 2 O 3 , ZrO 2 and TiO 2 are characterized as shown in the Table below; ______________________________________
Coordinates (wt %)
Vertices V.sub.2 O.sub.3
ZrO.sub.2
TiO.sub.2
______________________________________
A 50 50 0
B 24 50 26
C 24 10 66
D 32 2 66
F 98 2 0
______________________________________
Claim 4
Dependent Claim
37 words
The method of claim 1 further comprising cooling the pellets from ( 5) to ambient temperature, while at substantially the same partial pressure of oxygen as in (5); and storing the cooled pellets in a sealed container.
Claim 5
Dependent Claim
22 words
The method of claim 1 wherein said compositions involving V 2 O 3 , ZrO 2 and TiO 2 are solid solutions.
Claim 6
Dependent Claim
40 words
The method of claim 1 wherein at the time of reaction in (5) all of the oxide pellets are in the solid state or at least one, two or three of the oxide constituents may be in the molten state.
Claim 7
Dependent Claim
47 words
The method of claim 1 where in step (1) said V 2 O 5 powder is heated in an atmosphere comprising a gas mixture of CO 2 and H 2 with a volume ratio of CO 2 /H 2 in the range of about 10/1 to 1/1.
Claim 8
Dependent Claim
42 words
The method of claim 1 wherein step (5) said pellets are heated in an atmosphere comprising a gas mixture of CO 2 and H 2 with a volume ratio of CO 2 /H 2 in the range of about 10/1 to 1/1.
Claim 9
Dependent Claim
52 words
The method of claim 1 wherein steps (1) and (5) said materials are heated in an atmosphere comprising a gas mixture of CO 2 and CO or H 2 O and H 2 in volumetric ratios CO 2 /CO or H 2 O/H 2 in the range of about 10/1 to 1/1.
Claim 10
Dependent Claim
51 words
The method of claim 1 wherein said composition has the formula Zr 0 .11 V 1 .89 Ti 0 .83 O 5 .00 as illustrated by point G in said figure, and having the following coordinates in wt. %: V 2 O 3 64, ZrO 2 6 and TiO 2 30.
Claim 11
Dependent Claim
13 words
The method of claim 1 wherein said composition has a structure of pseudobrookite.
Claim 12
Dependent Claim
129 words
Thermal refractory compositions comprising, (1) a solid solution in the amount of about 1-25 wt. %, and (2) at least one oxide having a cationic portion selected from the group consisting of Cr, Mg, Al, Mn, Si, and mixtures thereof, wherein said solid solution is produced from V 2 O 3 , ZrO 2 and TiO 2 and has a composition that falls within the shaded area circumscribed by ABCDF as shown in the disclosed Figure wherein the amounts of V 2 O 3 , ZrO 2 and TiO 2 are characterized as shown in the table below: ______________________________________
Coordinates (Wt %)
Vertices V.sub.2 O.sub.3
ZrO.sub.2
TiO.sub.2
______________________________________
A 50 50 0
B 24 50 26
C 24 10 66
D 32 2 66
F 98 2 0
______________________________________
Claim 13
Dependent Claim
129 words
Thermal refractory compositions comprising, (1) a solid solution in the amount of about 1-25 wt. %, and (2) at least one oxide having a cationic portion selected from the group consisting of Cr, Mg, Al, Mn, Si, and mixtures thereof, wherein said solid solution is produced from V 2 O 3 , ZrO 2 and TiO 2 and has a composition that falls within the shaded area circumscribed by ABCDF as shown in the disclosed Figure wherein the amounts of V 2 O 3 , ZrO 2 and TiO 2 are characterized as shown in the table below: ______________________________________
Coordinates (Wt %)
Vertices V.sub.2 O.sub.3
ZrO.sub.2
TiO.sub.2
______________________________________
A 50 50 0
B 24 50 26
C 24 10 66
D 32 2 66
F 98 2 0
______________________________________
Claim 14
Dependent Claim
88 words
Compositions produced from V 2 O 3 , ZrO 2 and TiO 2 , wherein said compositions are solid solutions and fall within the shaded area circumscribed by ABCDF as shown in the disclosed Figure wherein the amounts of V 2 O 3 , ZrO 2 and TiO 2 are characterized as shown in the table below: ______________________________________
Coordinates (Wt %)
Vertices V.sub.2 O.sub.3
ZrO.sub.2
TiO.sub.2
______________________________________
A 50 50 0
B 24 50 26
C 24 10 66
D 32 2 66
F 98 2 0
______________________________________
Claim 15
Dependent Claim
88 words
Compositions produced from V 2 O 3 , ZrO 2 and TiO 2 , wherein said compositions are solid solutions and fall within the shaded area circumscribed by ABCDF as shown in the disclosed Figure wherein the amounts of V 2 O 3 , ZrO 2 and TiO 2 are characterized as shown in the table below: ______________________________________
Coordinates (Wt %)
Vertices V.sub.2 O.sub.3
ZrO.sub.2
TiO.sub.2
______________________________________
A 50 50 0
B 24 50 26
C 24 10 66
D 32 2 66
F 98 2 0
______________________________________
Claim 16
Dependent Claim
51 words
A composition as provided in claim 12 having the formula Zr 0 .11 V 1 .89 Ti 0 .83 O 5 .00 as illustrated by point G in said disclosed Figure and having the following coordinates in wt. % V 2 O 3 64, ZrO 2 6 and TiO 2 30.
Claim 17
Dependent Claim
112 words
Compositions produced from V 2 O 3 , ZrO 2 and TiO 2 and in which the vanadium is present in the trivalent and tetravalent states, and the structure comprises pseudobrookite; wherein said compositions are characterized by their ability to catalyze oxidation reactions and which fall within the shaded area circumscribed by ABCDF as shown in the disclosed Figure wherein the amounts of V 2 O 3 , ZrO 2 and TiO 2 are characterized as shown in the table below: ______________________________________
Coordinates (Wt %)
Vertices V.sub.2 O.sub.3
ZrO.sub.2
TiO.sub.2
______________________________________
A 50 50 0
B 24 50 26
C 24 10 66
D 32 2 66
F 98 2 0
______________________________________
Claim 18
Dependent Claim
112 words
Compositions produced from V 2 O 3 , ZrO 2 and TiO 2 and in which the vanadium is present in the trivalent and tetravalent states, and the structure comprises pseudobrookite; wherein said compositions are characterized by their ability to catalyze oxidation reactions and which fall within the shaded area circumscribed by ABCDF as shown in the disclosed Figure wherein the amounts of V 2 O 3 , ZrO 2 and TiO 2 are characterized as shown in the table below: ______________________________________
Coordinates (Wt %)
Vertices V.sub.2 O.sub.3
ZrO.sub.2
TiO.sub.2
______________________________________
A 50 50 0
B 24 50 26
C 24 10 66
D 32 2 66
F 98 2 0
______________________________________
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-06-03 | 1994-12-03 | 1995-06-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-06-03 | 1998-12-03 | 1999-06-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-06-03 | 2002-12-03 | 2003-06-04 | $7700.00 | Window Closed / Lapsed |