US5019552A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Long-laser-pulse method of producing thin films
Assignee: United States Department of Energy
•
Filing: 1990-02-20
•
Granted: 1991-05-28
•
Expires: 2010-02-20
Abstract
Abstract A method of depositing thin films by means of laser vaporization employs a long-pulse laser (Nd-glass of about one millisecond duration) with a peak power density typically in the range 10 5 -10 6 W/cm 2 . The method may be used to produce high T c superconducting films of perovskite material. In one embodiment, a few hundred nanometers thick film of YBa 2 Cu 3 O 7-x is produced on a SrTiO 3 crystal substrate in one or two pulses. In situ-recrystallization and post-annealing, both at elevated temperature and in the presence of an oxidizing agen The invention described herein arose in the course of, or under, Contract No. DE-C03-76SF0098 between the United States Department of Energy and the University of California.
Inventors
- 👤 Mehdi Balooch
- 👤 Donald K. Olander
- 👤 Richard E. Russo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 08:06
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B41/45; C04B41/50; C04B41/5072; C04B41/5074; C04B41/80; C04B41/81; C04B41/85; C23; C23C; C23C14/00; C23C14/06; C23C14/08; C23C14/087; C23C14/22; C23C14/24; C23C14/28; H; H10; H10N; H10N60/00; H10N60/01; H10N60/0268; H10N60/0296; H10N60/0521; Y; Y10; Y10S; Y10S505/00; Y10S505/725; Y10S505/73; Y10S505/732
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
106 words
A method of depositing a thin film of a superconducting ceramic material on a substrate by laser evaporation, comprising the steps of: providing a solid target of the material and the substrate spaced therefrom in an evacuated chamber; maintaining the substrate at a first predetermined elevated temperature; vaporizing a portion of the material from the target by a laser beam having a peak power density in the range between 10 5 -10 6 W/cm 2 and a pulse width in the range between 0.5 to 2.0 milliseconds; and forming the a thin film of the superconducting ceramic material on the substrate from the vaporized target material.
Claim 2
Independent Claim
106 words
A method of depositing a thin film of a superconducting ceramic material on a substrate by laser evaporation, comprising the steps of: providing a solid target of the material and the substrate spaced therefrom in an evacuated chamber; maintaining the substrate at a first predetermined elevated temperature; vaporizing a portion of the material from the target by a laser beam having a peak power density in the range between 10 5 -10 6 W/cm 2 and a pulse width in the range between 0.5 to 2.0 milliseconds; and forming the a thin film of the superconducting ceramic material on the substrate from the vaporized target material.
Claim 3
Dependent Claim
55 words
The method as in claim 1, further comprising: providing a predetermined metered amount of reactive oxidation agent adjacent to the surface of the substrate to be coated, the oxidizing agent being added to replenish depletion in the film; and forming the thin film on the substrate from the vaporized target material and the oxidizing agent.
Claim 4
Dependent Claim
17 words
The method as in claim 2, wherein the reactive oxidizing agent is excited oxygen molecules or atoms.
Claim 5
Dependent Claim
17 words
The method as in claim 2, wherein the reactive oxidizing agent is excited halogen molecules or atoms.
Claim 6
Dependent Claim
32 words
The method as in claim 1, further comprising: maintaining the target at an elevated temperature sufficient to avoid thermal-shock cracking prior to the step of vaporizing the target by a laser beam.
Claim 7
Dependent Claim
37 words
The method as in claim 1, further comprising: exposing the thin film to an additional oxidizing agent; and annealing the thin film at a second predetermined elevated temperature for a time sufficient to yield optimum film quality.
Claim 8
Dependent Claim
21 words
The method as in claim 1, wherein the solid target is a pellet of pressure-sintered or hot isostatically-pressed superconducting ceramic material.
Claim 9
Dependent Claim
26 words
The method as in claim 7, wherein the superconducting ceramic material is chosen from the group consisting of Yttrium-based, Bismuth-based and Thallium-based high-T c superconducting materials.
Claim 10
Dependent Claim
19 words
The method as in claim 8, wherein the superconducting ceramic material is YBa 2 Cu 3 O 7 .
Claim 11
Dependent Claim
57 words
The method as in claim 9, further comprising: providing a predetermined metered amount of reactive oxidizing agent adjacent to the surface of the substrate to be coated, the oxidizing agent being added to replenish depletion of oxygen in the film; and forming the thin film on the substrate from the vaporized target material and the oxidizing agent.
Claim 12
Dependent Claim
17 words
The method as in claim 10, wherein the reactive oxidizing agent is excited oxygen molecules or atoms.
Claim 13
Dependent Claim
17 words
The method as in claim 10, wherein the reactive oxidizing agent is excited halogen molecules or atoms.
Claim 14
Dependent Claim
32 words
The method as in claim 10, further comprising: maintaining the target at an elevated temperature sufficient to avoid thermal-shock cracking prior to the step of vaporizing the target by a laser beam.
Claim 15
Dependent Claim
37 words
The method as in claim 10, further comprising: exposing the thin film to an additional oxidizing agent; and annealing the thin film at a second predetermined elevated temperature for a time sufficient to yield optimum film quality.
Claim 16
Dependent Claim
25 words
The method as in claim 14, wherein the second predetermined elevated temperature of the substrate is in the range between 700° C and 900° C.
Claim 17
Dependent Claim
25 words
The method as in claim 14, wherein the first predetermined elevated temperature of the substrate is in the range between 500° C and 800° C.
Claim 18
Independent Claim
111 words
The method of coating a thin film of a superconducting material on a substrate by laser evaporation, comprising the steps of: providing a solid target of the material and the substrate spaced therefrom in an evacuated chamber; maintaining the substrate at a first predetermined elevated temperature; vaporizing a portion of the material from the target by a laser beam having a long width and a low peak power density less than 5×10 6 W/cm 2 such that vaporization is substantially close to thermal equilibrium, thereby maintaining the vaporized target material at substantially the stoichiometry of the solid target; and forming the thin film on the substrate from the vaporized target material.
Claim 19
Independent Claim
111 words
The method of coating a thin film of a superconducting material on a substrate by laser evaporation, comprising the steps of: providing a solid target of the material and the substrate spaced therefrom in an evacuated chamber; maintaining the substrate at a first predetermined elevated temperature; vaporizing a portion of the material from the target by a laser beam having a long width and a low peak power density less than 5×10 6 W/cm 2 such that vaporization is substantially close to thermal equilibrium, thereby maintaining the vaporized target material at substantially the stoichiometry of the solid target; and forming the thin film on the substrate from the vaporized target material.
Claim 20
Dependent Claim
57 words
The method as in claim 17, further comprising: providing a predetermined metered amount of reactive oxidation agent adjacent to the surface of the substrate to be coated, the oxidizing agent being added to replenish depletion of oxygen in the film; and forming the thin film on the substrate from the vaporized target material and the oxidizing agent.
Claim 21
Dependent Claim
17 words
The method as in claim 18, wherein the reactive oxidizing agent is excited oxygen molecules or atoms.
Claim 22
Dependent Claim
17 words
The method as in claim 18, wherein the reactive oxidizing agent is excited halogen molecules or atoms.
Claim 23
Dependent Claim
32 words
The method as in claim 17, further comprising: maintaining the target at an elevated temperature sufficient to avoid thermal-shock cracking prior to the step of vaporizing the target by a laser beam.
Claim 24
Dependent Claim
37 words
The method as in claim 17, further comprising: exposing the thin film to an additional oxidizing agent; and annealing the thin film at a second predetermined elevated temperature for a time sufficient to yield optimum film quality.
Claim 25
Dependent Claim
20 words
The method as in claim 17, wherein the solid target is a pellet of pressure-sintered or hot isostatic-pressed superconducting material.
Claim 26
Dependent Claim
25 words
The method as in claim 23, wherein the superconducting material is chosen from the group consisting of Yttrium-based, Bismuth-based and Thallium-based high-T c superconducting materials.
Claim 27
Dependent Claim
18 words
The method as in claim 24, wherein the superconducting material is YBa 2 Cu 3 O 7 .
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-05-27 | 1994-11-26 | 1995-05-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-05-27 | 1998-11-26 | 1999-05-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-05-27 | 2002-11-26 | 2003-05-28 | $7700.00 | Window Closed / Lapsed |