Abrasive sheet and method for manufacturing the abrasive sheet
Assignee: Nihon Micro Coating Co Ltd
•
Filing: 1988-10-07
•
Granted: 1991-05-14
•
Expires: 2008-10-07
Abstract
Abstract An abrasive sheet is formed by uniformly painting slurry made of mixture of abrasive particles and adhesives on a surface of a base sheet with a pattern of irregularities by embossing. The slurry layer formed on the sheet hardens by drying at adequate temperature to form an abrasive layer. The abrasive layer has high and low abrasive parts formed by the surface tension of slurry, corresponding to the irregularities of the base sheet. The abrasive sheet is characterized by good planar precision of the abrasive layer, hardness to be peeled off the base sheet, and relatively easy producing method in which grooves are formed by the surface tension.
Inventors
- 👤 Motokazu Yamamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 17:28
CPC Classifications
B; B24; B24D; B24D3/00; B24D3/02; B24D3/20; B24D3/28; B24D11/00; B24D11/001; B24D11/005
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
114 words
A method of making an abrasive sheet comprising the steps of: embossing at least one side of a base sheet to form irregularities; painting a slurry, made of a mixture of abrasive particles and resin adhesives, on the embossed side of said base sheet to form an abrasive layer having a substantially planar top surface; and dry hardening said abrasive layer to form high and low abrasive parts corresponding to said irregularities on said side by first passing the slurry painted base sheet through a low temperature dryer to prevent surface drying and then passing the slurry painted base sheet through a high temperature dryer to evaporate organic solvent molecules in the resin adhesives.
Claim 2
Independent Claim
114 words
A method of making an abrasive sheet comprising the steps of: embossing at least one side of a base sheet to form irregularities; painting a slurry, made of a mixture of abrasive particles and resin adhesives, on the embossed side of said base sheet to form an abrasive layer having a substantially planar top surface; and dry hardening said abrasive layer to form high and low abrasive parts corresponding to said irregularities on said side by first passing the slurry painted base sheet through a low temperature dryer to prevent surface drying and then passing the slurry painted base sheet through a high temperature dryer to evaporate organic solvent molecules in the resin adhesives.
Claim 3
Dependent Claim
48 words
The method of claim 1 wherein said embossing side of the base sheet is formed by electric or dielectric heating of the base with high frequency electric waves and then molding the base to form a pattern of irregularities on at least one surface of said base sheet.
Claim 4
Dependent Claim
43 words
A method of making an abrasive sheet according to claim 1, wherein the resin adhesives are formed by dissolving saturated polyester resin in a solvent mixture of toluene, xylene, ethyl acetate and methyl ethyl ketone and then adding isocyanate compound as a hardener.
Claim 5
Dependent Claim
43 words
A method of making an abrasive sheet according to claim 1 wherein the temperature range for the low temperature dryer is from 90° C. to 100° C. and the temperature range for the high temperature dryer is from 105° C. to 125° C.
References Cited (Backward Citations)
US2755607A
Cited
US4078340A
Cited
US4111666A
Cited
US4084941A
Cited
US4142334A
Cited
US4162899A
Cited
US4255164A
Cited
US4317660A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-05-13 | 1994-11-12 | 1995-05-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-05-13 | 1998-11-12 | 1999-05-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-05-13 | 2002-11-12 | 2003-05-14 | $7700.00 | Window Closed / Lapsed |