Preparation of conductive polyaniline having controlled molecular weight
Assignee: Lockheed Martin Corp
•
Filing: 1990-01-30
•
Granted: 1991-04-16
•
Expires: 2010-01-30
Abstract
Abstract Process for producing conductive polyaniline of controlled molecular weight by providing a mixture of aniline and dianiline in predetermined proportions dependent on the desired molecular weight of polyaniline to be formed. The mixture is reacted in the presence of an oxidant such as ammonium persulfate and a protonic (Bronsted) acid such as tosylic acid, to polymerize the mixture of aniline and dianiline, and forming conductive polyaniline of the desired molecular weight. Soluble conductive polyanilines having an average molecular weight not higher than about 600,000 (by gel permeation chromatography versus polystyrene in N-methyl pyrrolidone) can be obtained. Using about 6 to about 18 mols of aniline per mol of dianiline, according to one mode of procedure, conductive polyaniline having an average molecular weight ranging from about 150,000 to about 600,000 can be obtained. According to another feature of the invention, mild or weak oxidants such as o-chloranil and cupric chloride, as well as strong oxidants such as ammonium persulfate, can be used in the reaction.
Inventors
- 👤 Randy E. Cameron
- 👤 Sandra K. Clement
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 05:37
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/06; H01B1/12; H01B1/124; H01B1/128; C; C08; C08G; C08G73/00; C08G73/02; C08G73/026; C08G73/0266
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
60 words
A process for producing conductive polyaniline which comprises providing a mixture of aniline and dianiline in a molar proportion of aniline to dianiline in said mixture in the range of about 1 to about 100, reacting said mixture in the presence of an oxidant and a protonic acid to polymerize said mixture of aniline and dianiline, and forming conductive polyaniline.
Claim 2
Dependent Claim
60 words
A process for producing conductive polyaniline which comprises providing a mixture of aniline and dianiline in a molar proportion of aniline to dianiline in said mixture in the range of about 1 to about 100, reacting said mixture in the presence of an oxidant and a protonic acid to polymerize said mixture of aniline and dianiline, and forming conductive polyaniline.
Claim 3
Dependent Claim
23 words
The process of claim 1, employing a molar proportion of aniline to dianiline in said range sufficient to form a soluble conductive polyaniline.
Claim 4
Dependent Claim
37 words
The process of claim 1, employing a molar proportion of about 6 to about 18 mols of aniline per mole of dianiline, and obtaining a conductive polyaniline of average molecular weight of about 200 to about 600,000.
Claim 5
Dependent Claim
34 words
The process of claim 1, employing a molar proportion of more than 18 mols of aniline per mol of dianiline, and obtaining a conductive polyaniline having an average molecular weight in excess of 600,000.
Claim 6
Dependent Claim
16 words
The process of claim 1, wherein said oxidant is a strong, mild or a weak oxidant.
Claim 7
Dependent Claim
11 words
The process of claim 1, wherein said oxidant is ammonium persulfate.
Claim 8
Dependent Claim
21 words
The process of claim 1, wherein said oxidant is selected from the group consisting of benzoperoxide o-chloranil, p-chloranil and cupric chloride.
Claim 9
Dependent Claim
28 words
The process of claim 1, wherein said protonic acid is selected from the group consisting of hydrochloric acid, sulfuric acid, formic acid, tosylic acid and benzene disulfonic acid.
Claim 10
Dependent Claim
28 words
The process of claim 6, wherein said protonic acid is selected from the group consisting of hydrochloric acid, sulfuric acid, formic acid, tosylic acid and benzene disulfonic acid.
Claim 11
Dependent Claim
28 words
The process of claim 7, wherein said protonic acid is selected from the group consisting of hydrochloric acid, sulfuric acid, formic acid, tosylic acid and benzene disulfonic acid.
Claim 12
Dependent Claim
53 words
The process of claim 1, including the additional step for increasing the solubility of said conductive polyaniline, which comprises deprotonating said conductive polyaniline to the polyaniline free base, and reacting said polyaniline free base with a compound selected from the group consisting of an anhydride, an alkylating agent and an aromatic multisulfonic acid.
Claim 13
Dependent Claim
93 words
A process for producing conductive polyaniline of controlled molecular weight which comprises providing a reaction mixture of aniline and dianiline in a molar proportion of about 6 to about 18 mols of aniline per mole of dianiline, adding as oxidant ammonium persulfate and a member selected from the group consisting of tosylic acid and benzene disulfonic acid to said mixture, and reacting said mixture to polymerize said mixture of aniline and dianiline, and form a conductive polyaniline soluble in organic solvents and having an average molecular weight of about 2000 to about 600,000.
Claim 14
Dependent Claim
93 words
A process for producing conductive polyaniline of controlled molecular weight which comprises providing a reaction mixture of aniline and dianiline in a molar proportion of about 6 to about 18 mols of aniline per mole of dianiline, adding as oxidant ammonium persulfate and a member selected from the group consisting of tosylic acid and benzene disulfonic acid to said mixture, and reacting said mixture to polymerize said mixture of aniline and dianiline, and form a conductive polyaniline soluble in organic solvents and having an average molecular weight of about 2000 to about 600,000.
Claim 15
Dependent Claim
47 words
The process of claim 12, including adding additional amounts of aniline and ammonium persulfate to the reaction mixture to provide a total predetermined proportion of aniline and dianiline, and obtaining a conductive polyaniline having a molecular weight dependent on the total proportion of aniline and dianiline employed.
Claim 16
Dependent Claim
20 words
The process of claim 13, said conductive polyaniline having an average molecular weight ranging from about 150,000 to about 600,000.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-04-15 | 1994-10-15 | 1995-04-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-04-15 | 1998-10-15 | 1999-04-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-04-15 | 2002-10-15 | 2003-04-16 | $7700.00 | Window Closed / Lapsed |