Method for making fiber reinforced plastic tubing
Assignee: Plas/Steel Products Inc
•
Filing: 1986-10-22
•
Granted: 1991-04-09
•
Expires: 2006-10-22
Abstract
Abstract Fiber reinforced plastic tubing is formed by an innermost layer of braided strands that include longitudinal stud fill strands within the braid, a second layer of longitudinal strands, and a third layer of braided strands, all thoroughly encased in a monolithic mass of plastic matrix material that is not, itself, divided into layers. The tube is fabricated on a continuous basis by winding two sets of strands in opposite directions on a mandrel and braiding the two sets with each other and with stud fill strands that prevent that first layer of braid from stretching longitudinally and thereby tightening immovably on the mandrel. The strands are braided dry but are wetted with liquid plastic matrix material as the braid is compacted on the mandrel. A fourth set of strands is wetted by liquid plastic matrix material and guided to lie longitudinally along and evenly spaced about the wetted first braid, and fifth and sixth set of strands are braided dry around the fourth set and compacted and wetted to press against the fourth set and to press the fourth set against the first setted braid. No curing is done until after the latter compacting and wetting. The multi-layer tubing is pulled along the mandrel by alternately-operating gripping devices in which a soft tube sealed into a rigid shell is expanded inwardly by fluid pressure between the shell and the soft tube, thereby forcing the soft tube to grip the tubing around the entire circumference of the tubing.
Inventors
- 👤 Elson B. Fish
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 23:23
CPC Classifications
D; D04; D04C; D04C3/00; D04C3/48; B; B29; B29C; B29C53/00; B29C53/56; B29C53/58; B29C53/60; B29C53/68; B29C53/80; B29C53/8008; B29C53/805; B29C53/8058; B29C53/8066; B29C53/8075; B29C70/00; B29C70/04; B29C70/28; B29C70/40; B29C70/50; B29C70/52; B29C70/521; D04C1/00; D04C1/06; B29K; B29K2105/00; B29K2105/06; B29K2105/08; B29K2105/0809; B29K2105/0827; D10; D10B; D10B2403/00; D10B2403/02; D10B2403/024; D10B2403/0241; D10B2403/02411; D10B2505/00; D10B2505/02
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
283 words
A method of fabricating multi-layer fiber reinforced plastic tubing on a continuous basis comprising the steps of: braiding a first layer of strands about a stationary mandrel by weaving together first, second, and third sets of strands, said second and third sets being wound oppositely about said mandrel while said first set is pulled longitudinally and interwoven therewith, whereby said first set inhibits said braided first layer from gripping said mandrel to an extend as will prevent movement of the resulting tubular layer with respect to said mandrel; simultaneously radially gripping and axially pulling said first layer relative to said stationary mandrel; prewetting said first layer by applying a liquid plastic matrix material to said second and third strands prior to engagement about said mandrel; drawing said braided layer through a die orifice that defines with said mandrel a decreasing annular clearance through which said layer moves to gradually fully compact said strands onto said mandrel; applying a liquid plastic matrix material under pressure to said first braided layer of stands while said layer is being gradually compacted and confined between said die orifice and said mandrel and before said braided layer is fully compacted; applying a liquid plastic matrix material to said first braided layer of strands at the exit end of said orifice by surrounding said mandrel and said braided layer with said liquid plastic to inhibit air from being drawn into said layer as it expands following compaction; and curing the liquid plastic matrix material while said tubular braid is moved along and is supported by said mandrel and while the liquid plastic matrix material is radially confined between the mandrel and a surrounding outer die to form self-supporting tubing.
Claim 2
Independent Claim
283 words
A method of fabricating multi-layer fiber reinforced plastic tubing on a continuous basis comprising the steps of: braiding a first layer of strands about a stationary mandrel by weaving together first, second, and third sets of strands, said second and third sets being wound oppositely about said mandrel while said first set is pulled longitudinally and interwoven therewith, whereby said first set inhibits said braided first layer from gripping said mandrel to an extend as will prevent movement of the resulting tubular layer with respect to said mandrel; simultaneously radially gripping and axially pulling said first layer relative to said stationary mandrel; prewetting said first layer by applying a liquid plastic matrix material to said second and third strands prior to engagement about said mandrel; drawing said braided layer through a die orifice that defines with said mandrel a decreasing annular clearance through which said layer moves to gradually fully compact said strands onto said mandrel; applying a liquid plastic matrix material under pressure to said first braided layer of stands while said layer is being gradually compacted and confined between said die orifice and said mandrel and before said braided layer is fully compacted; applying a liquid plastic matrix material to said first braided layer of strands at the exit end of said orifice by surrounding said mandrel and said braided layer with said liquid plastic to inhibit air from being drawn into said layer as it expands following compaction; and curing the liquid plastic matrix material while said tubular braid is moved along and is supported by said mandrel and while the liquid plastic matrix material is radially confined between the mandrel and a surrounding outer die to form self-supporting tubing.
Claim 3
Dependent Claim
16 words
The method of claim 1, wherein said gripping is accomplished by a uniformly applied circumferential force.
Claim 4
Dependent Claim
28 words
The method of claim 1 comprising the additional step of cooling the structure comprising the first, second and third sets of stands before curing the plastic matrix material.
Claim 5
Dependent Claim
49 words
The method of claim 1 in which, after being interbraided, the first, second, and third sets of strands are moved along generally converging paths to a region of maximum compaction and are wetted while being moved along said generally converging paths and before reaching the region of maximum compaction.
Claim 6
Dependent Claim
41 words
The method of claim 1 wherein said prewetting is performed by wetting an annular surface which surrounds said mandrel with liquid plastic, and rubbing said second and third strands against said wetted surface while they are being wound around said mandrel.
References Cited (Backward Citations)
US2602766A
Cited
US3007497A
Cited
US3033729A
Cited
US3470051A
Cited
US3457962A
Cited
US3529050A
Cited
US3769127A
Cited
US3694131A
Cited
US4202718A
Cited
US4515737A
Cited
US4494436A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-04-08 | 1994-10-08 | 1995-04-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-04-08 | 1998-10-08 | 1999-04-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-04-08 | 2002-10-08 | 2003-04-09 | $7700.00 | Window Closed / Lapsed |