Method of manufacturing surface relief patterns of variable cross-sectional geometry
Assignee: ERIM International Inc
•
Filing: 1989-12-12
•
Granted: 1991-04-02
•
Expires: 2009-12-12
Abstract
Abstract A method of manufacturing surface relief patterns of variable depth in solid materials is disclosed, which patterns, when seen in cross-section, are of variable geometry. After determining the properties of the desired surface relief pattern and of the material to be etched, the steps used in the method include: depositing a layer of measured thickness of photoresist material on the surface of the material to be etched; applying a selected amount of radiation to specific areas on the photoresist, thereby sensitizing the photoresist, so that the amount of radiation on the photoresist is a function of the depth of the desired surface relief pattern in the solid material at that point; chemically developing the photoresist material to remove the sensitized material in proportion to the exposure which it has received; and finally, etching the combined photoresist and substrate through reactive ion etching until portions of the photoresist material have been removed, thereby leaving the desired pattern etched in the substrate. As an additional step, the etched substrate may be coated with a metallic film with protective and optically desirable properties.
Inventors
- 👤 Nickolas P. Vlannes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 20:02
CPC Classifications
G; G02; G02B; G02B5/00; G02B5/18; G02B5/1847; G02B5/1857; G03; G03F; G03F7/00; G03F7/0005; G03F7/001
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
235 words
A method of manufacturing in the surface of a solid substrate a three-dimensional surface relief pattern of desired variable cross-sectional geometry, comprising the steps of: (a) depositing on said surface of said substrate a uniform thickness layer of radiation-sensitive resist material; (b) determining a pattern of transmission density for each point of a mask of variable transmission density said transmission density for each point of said mask of variable transmission density determined based upon the desired variable cross-sectional geometry at a corresponding point of said surface of said substrate to compensate for the non-linear absorption characteristics of transferring said pattern to said resist material; (c) producing a mask of variable transmission density having said determined pattern of variable transmission density; (d) placing said mask between a source of radiation and said resist-covered substrate; (e) exposing said mask and said resist-covered substrate to radiation; (f) chemically developing said resist material, thereby removing a portion of said resist material and leaving remaining resist material corresponding to said pattern of variable transmission density; and (g) etching said surface of said substrate and said remaining resist material by bombarding said substrate and said remaining resist material with a directional beam of reactive ions until said remaining resist material has been removed and a portion of said substrate has been removed, thereby forming a three-dimensional surface relief pattern in said substrate corresponding to the pattern of said remaining resist material.
Claim 2
Independent Claim
235 words
A method of manufacturing in the surface of a solid substrate a three-dimensional surface relief pattern of desired variable cross-sectional geometry, comprising the steps of: (a) depositing on said surface of said substrate a uniform thickness layer of radiation-sensitive resist material; (b) determining a pattern of transmission density for each point of a mask of variable transmission density said transmission density for each point of said mask of variable transmission density determined based upon the desired variable cross-sectional geometry at a corresponding point of said surface of said substrate to compensate for the non-linear absorption characteristics of transferring said pattern to said resist material; (c) producing a mask of variable transmission density having said determined pattern of variable transmission density; (d) placing said mask between a source of radiation and said resist-covered substrate; (e) exposing said mask and said resist-covered substrate to radiation; (f) chemically developing said resist material, thereby removing a portion of said resist material and leaving remaining resist material corresponding to said pattern of variable transmission density; and (g) etching said surface of said substrate and said remaining resist material by bombarding said substrate and said remaining resist material with a directional beam of reactive ions until said remaining resist material has been removed and a portion of said substrate has been removed, thereby forming a three-dimensional surface relief pattern in said substrate corresponding to the pattern of said remaining resist material.
Claim 3
Dependent Claim
60 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 1, wherein: said step of determining said pattern of transmission density further includes compensating for the unequal etch rates of said substrate and said remaining resist material during said step of etching said surface of said substrate and said remaining resist material.
Claim 4
Dependent Claim
99 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 2, wherein: said compensating for the unequal etch rates of said step of determining said pattern of transmission density is based upon the composition of said resist material, the composition of said substrate, the depth of said surface relief pattern, the variable cross-sectional geometry of said surface relief pattern at various points, the wavelength of the radiation used for exposure of said resist material, and the nature of reactive ions to be used in etching substrate and said remaining resist material.
Claim 5
Dependent Claim
91 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 1, wherein: said resist material is a negative resist material; said step of determining said pattern of transmission density for each point of a mask of variable transmission density includes determining said pattern as the inverse of said desired variable cross-sectional geometry; and said step of chemically developing said resist material removes the portion of said resist material exposed to said radiation and leaves said remaining resist material not exposed to said radiation.
Claim 6
Dependent Claim
89 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 1, wherein: said resist material is a positive resist material; said step of determining said pattern of transmission density for each point of a mask of variable transmission density includes determining said pattern corresponding to said desired variable cross-sectional geometry; and said step of chemically developing said resist material removes the portion of said resist material not exposed to said radiation and leaves said remaining resist material exposed to said radiation.
Claim 7
Dependent Claim
37 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 1, further comprising the step of: (h) coating said etched substrate with at least one thin film of material.
Claim 8
Dependent Claim
35 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 6, wherein: said at least one thin film of material includes a thin film of a metal.
Claim 9
Dependent Claim
36 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 6, wherein: said at least one thin film of material includes a thin film of a non-metallic dielectric.
Claim 10
Dependent Claim
35 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 6, wherein: said at least one thin film of material includes a thin film of a semiconductor.
Claim 11
Dependent Claim
247 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 1, wherein: said step of determining said pattern of transmission density further includes determining a function of mask transmission density versus depth of etch in said substrate by repeatedly for each mask transmission density (i) depositing on said surface of a test substrate a uniform thickness layer of said radiation-sensitive resist material; (ii) producing a mask of uniform fixed transmission density; (ii) placing said mask between a source of radiation and said resist-covered test substrate; (iv) exposing said mask and said resist-covered test substrate to radiation; (v) chemically developing said resist material, thereby removing a portion of said resist material and leaving remaining resist material corresponding to said pattern of variable transmission density; (vi) etching said surface of said test substrate and said remaining resist material by bombarding said test substrate and said remaining resist material with a directional beam of reactive ions until said remaining resist material has been removed and a portion of said test substrate has been removed; (vii) measuring the depth of etch in said test substrate; and said step of determining said pattern of transmission density further includes determining said transmission density for each point of a mask of variable transmission density corresponding to said transmission density for said test substrate which produced a depth of etch equal to said desired variable cross-sectional geometry at a corresponding point of said surface of said substrate.
Claim 12
Independent Claim
202 words
A method of manufacturing in the surface of a solid substrate a three-dimensional surface relief pattern of desired variable cross--sectional geometry, comprising the steps of: (a) depositing on said surface of said substrate a uniform thickness layer of radiation-sensitive resist material; (b) determining a pattern of exposure intensity for each point of said resist material, said exposure intensity for each point of said resist material determined based upon the desired variable cross-sectional geometry at a corresponding point of said surface of said substrate to compensate for the non-linear absorption characteristics of transferring said pattern to said resist material; (c) exposing said resist-covered substrate to radiation having said pattern of exposure intensity; (d) chemically developing said resist material, thereby removing a portion of said resist material and leaving remaining resist material corresponding to said pattern of exposure intensity; and (g) etching said surface of said substrate and said remaining resist material by bombarding said substrate and said remaining resist material with a directional beam of reactive ions until said remaining resist material has been removed and a portion of said substrate has been removed, thereby forming a three-dimensional surface relief pattern in said substrate corresponding to the pattern of said remaining resist material.
Claim 13
Independent Claim
202 words
A method of manufacturing in the surface of a solid substrate a three-dimensional surface relief pattern of desired variable cross--sectional geometry, comprising the steps of: (a) depositing on said surface of said substrate a uniform thickness layer of radiation-sensitive resist material; (b) determining a pattern of exposure intensity for each point of said resist material, said exposure intensity for each point of said resist material determined based upon the desired variable cross-sectional geometry at a corresponding point of said surface of said substrate to compensate for the non-linear absorption characteristics of transferring said pattern to said resist material; (c) exposing said resist-covered substrate to radiation having said pattern of exposure intensity; (d) chemically developing said resist material, thereby removing a portion of said resist material and leaving remaining resist material corresponding to said pattern of exposure intensity; and (g) etching said surface of said substrate and said remaining resist material by bombarding said substrate and said remaining resist material with a directional beam of reactive ions until said remaining resist material has been removed and a portion of said substrate has been removed, thereby forming a three-dimensional surface relief pattern in said substrate corresponding to the pattern of said remaining resist material.
Claim 14
Dependent Claim
60 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 11, wherein: said step of determining said pattern of exposure intensity further includes compensating for the unequal etch rates of said substrate and said remaining resist material during said step of etching said surface of said substrate and said remaining resist material.
Claim 15
Dependent Claim
99 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 12, wherein: said compensating for the unequal etch rates of sad step of determining said pattern of exposure intensity is based upon the composition of said resist material, the composition of said substrate, the depth of said surface relief pattern, the variable cross--sectional geometry of said surface relief pattern at various points, the wavelength of the radiation used for exposure of said resist material, and the nature of reactive ions to be used in etching substrate and said remaining resist material.
Claim 16
Dependent Claim
88 words
The method of manufacturing at three-dimensional surface relief pattern of desired variable cross--sectional geometry as claimed inn claim 11, wherein: said resist material is a negative resist material; said step of determining said pattern of exposure intensity for each point of said resist material includes determining said pattern as the inverse of said desired variable cross-sectional geometry; and said step of chemically developing said resist material removes the portion of said resist material exposed to said radiation and leaves said remaining resist material not exposed to said radiation.
Claim 17
Dependent Claim
86 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 11, wherein: said resist material is a positive rest material; said step of determining said pattern of exposure intensity for each point of said resist material includes determining said pattern corresponding to said desired variable cross-sectional geometry; and said step of chemically developing said resist material removes the portion of said resist material not exposed to said radiation and leaves said remaining resist material exposed to said radiation.
Claim 18
Dependent Claim
37 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 11, further comprising the step of: (h) coating said etched substrate with at least one thin film of material.
Claim 19
Dependent Claim
35 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 16, wherein: said at least one thin film of material includes a thin film of a metal.
Claim 20
Dependent Claim
36 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed in claim 16, wherein: said at least one thin film of material includes a thin film of a non-metallic dielectric.
Claim 21
Dependent Claim
35 words
The method of manufacturing a three-dimensional surface relief pattern of desired variable cross-sectional geometry as claimed inn claim 16, wherein: said at least one thin film of material includes a thin film of a semiconductor.
Claim 22
Dependent Claim
141 words
In a method of manufacturing in the surface of a solid substrate a three-dimensional surface relief pattern of desired variable cross--sectional geometry including the steps of depositing a uniform thickness layer of radiation-sensitive resist material on the substrate, exposing the resist-covered substrate to a pattern of radiation, chemically developing the exposed resist material, and etching the surface of the substrate and the remaining resist material with a directional beam of reactive ions, the improvement comprising the step of: determining the pattern of radiation exposure intensity for each point of said resist material based upon the desired variable cross-sectional geometry at a corresponding point of said surface of said substrate to compensate for the non-linear absorption characteristics of transferring the pattern to the resist material and to compensate for the unequal etch rates of the substrate and the resist material during etching.
Claim 23
Dependent Claim
141 words
In a method of manufacturing in the surface of a solid substrate a three-dimensional surface relief pattern of desired variable cross--sectional geometry including the steps of depositing a uniform thickness layer of radiation-sensitive resist material on the substrate, exposing the resist-covered substrate to a pattern of radiation, chemically developing the exposed resist material, and etching the surface of the substrate and the remaining resist material with a directional beam of reactive ions, the improvement comprising the step of: determining the pattern of radiation exposure intensity for each point of said resist material based upon the desired variable cross-sectional geometry at a corresponding point of said surface of said substrate to compensate for the non-linear absorption characteristics of transferring the pattern to the resist material and to compensate for the unequal etch rates of the substrate and the resist material during etching.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-04-01 | 1994-10-01 | 1995-04-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-04-01 | 1998-10-01 | 1999-04-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-04-01 | 2002-10-01 | 2003-04-02 | $7700.00 | Window Closed / Lapsed |