Lamination coating process using polyesterurethane coating
Assignee: Avery Dennison Corp
•
Filing: 1989-12-21
•
Granted: 1991-03-19
•
Expires: 2009-12-21
Abstract
Abstract A process for forming a composite that is useful as an exterior vehicle part in which a layer of a coating composition is applied to a flexible smooth glossy polymeric carrier sheet and dried and laminated under heat and pressure to a flexible polymeric substrate to form a laminate, the carrier sheet is removed and the laminate is thermoformed into a three dimensional structure and a rigid thermoformable plastic is adhered to the thermoformed laminate to form the composite; the coating compsition used in the process that forms the exterior finish on the composite has a film forming binder which is in an organic liquid carrier is of a polyesterurethane and a multifunctional crosslinking agent of an epoxy compound or an organic polyisocyanate; wherein the polyesterurethane is formed by reacting a hydroxy functional polyester with a hydroxy containing carboxylic acid and an organic polyisocyanate.
Inventors
- 👤 Paul L. Adesko
- 👤 Jeffery W. Johnson
- 👤 Patrick L. Spain
- 👤 Keith L. Truog
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 05:24
CPC Classifications
B; B05; B05D; B05D1/00; B05D1/28; B05D1/286; B29; B29C; B29C51/00; B29C51/14; C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/10; C08G18/12; C08G18/28; C08G18/65; C08G18/66; C08G18/6633; C08G18/6659; C08G18/70; C08G18/72; C08G18/77; C08G18/78; C08G18/79; C08G18/791; C08G18/792; C09; C09D; C09D175/00; C09D175/04; C09D175/06; B05D2701/00
Claims Analysis
Total Claims: 45
Claim 1
Independent Claim
302 words
A process for forming a composite useful as an exterior vehicle body part comprising the following steps: a. applying a layer of a coating composition to a flexible polymeric carrier sheet having a smooth glossy surface and drying said layer; b. laminating with heat and pressure the flexible polymeric carrier sheet with the coating layer to a flexible thermoformable polymeric material with the coating layer of the sheet being adhered to the thermoformable polymeric material to form a laminate; c. removing the polymeric carrier sheet from the laminate whereby the exterior surface of the coating layer retains the glossy surface transferred to it from the polymeric carrier sheet; d. thermoforming the laminate to form a three dimensionally shaped preform; e. adhering the flexible polymeric material of the preform to a rigid synthetic resinous substrate to form a composite useful as an exterior vehicle body part; wherein the coating composition used in the process comprises about 10-70% by weight binder solids and correspondingly about 90-30% by weight organic liquid carrier, wherein the binder consists essentially of (1) a carboxyl functional polyesterurethane having a weight average molecular weight of about 80,000 to 200,000 and is a reaction product of a hydroxy functional polyester, a hydroxy containing carboxylic acid and an organic polyisocyanate, wherein the hydroxy functional polyester is the reaction product of a diol of the formula HOROH and dicarboxylic acid of the formula R 1 (COOH) 2 or an anhydride of such an acid where R is an aliphatic, cycloaliphatic or aromatic hydrocarbon radical having 2-6 carbon and R 1 is an aliphatic, cycloaliphatic or aromatic hydrocarbon radical having 6-12 carbon atoms and (2) multifunctional crosslinking agent selected from the group consisting of a multifunctional aliphatic, cycloaliphatic or aromatic epoxy compound or a multifunctional organic polyisocyanate having at least three reactive isocyanate groups.
Claim 2
Dependent Claim
302 words
A process for forming a composite useful as an exterior vehicle body part comprising the following steps: a. applying a layer of a coating composition to a flexible polymeric carrier sheet having a smooth glossy surface and drying said layer; b. laminating with heat and pressure the flexible polymeric carrier sheet with the coating layer to a flexible thermoformable polymeric material with the coating layer of the sheet being adhered to the thermoformable polymeric material to form a laminate; c. removing the polymeric carrier sheet from the laminate whereby the exterior surface of the coating layer retains the glossy surface transferred to it from the polymeric carrier sheet; d. thermoforming the laminate to form a three dimensionally shaped preform; e. adhering the flexible polymeric material of the preform to a rigid synthetic resinous substrate to form a composite useful as an exterior vehicle body part; wherein the coating composition used in the process comprises about 10-70% by weight binder solids and correspondingly about 90-30% by weight organic liquid carrier, wherein the binder consists essentially of (1) a carboxyl functional polyesterurethane having a weight average molecular weight of about 80,000 to 200,000 and is a reaction product of a hydroxy functional polyester, a hydroxy containing carboxylic acid and an organic polyisocyanate, wherein the hydroxy functional polyester is the reaction product of a diol of the formula HOROH and dicarboxylic acid of the formula R 1 (COOH) 2 or an anhydride of such an acid where R is an aliphatic, cycloaliphatic or aromatic hydrocarbon radical having 2-6 carbon and R 1 is an aliphatic, cycloaliphatic or aromatic hydrocarbon radical having 6-12 carbon atoms and (2) multifunctional crosslinking agent selected from the group consisting of a multifunctional aliphatic, cycloaliphatic or aromatic epoxy compound or a multifunctional organic polyisocyanate having at least three reactive isocyanate groups.
Claim 3
Dependent Claim
30 words
The process of claim 1 in which the laminating step b. is carried out at a temperature of about 150°-250° C. and at a pressure of about 10-75 kg/linear cm.
Claim 4
Dependent Claim
35 words
The process of claim 1 in which the binder of the coating composition comprises about 80-99 percent by weight of the carboxyl functions polyesterurethane and about 1-20 percent by weight of the multifunctional crosslinking agent.
Claim 5
Dependent Claim
30 words
The process of claim 2 in which the hydroxy functional polyester of the coating is the reaction product of about 1.2-1.4 equivalents of diol for 1 equivalent of dicarboxylic acid.
Claim 6
Dependent Claim
57 words
The process of claim 3 in which the polyesterurethane of the coating composition is the reaction product of about 60-90 percent by weight of the hydroxy functional polyester, about 1-5 percent by weight of the hydroxy containing carboxylic acid containing one carboxyl group and two hydroxyl groups, and about 5-30 percent by weight of the organic polyisocyanate.
Claim 7
Dependent Claim
43 words
The process of claim 5 in which the diol used to form the hydroxy functional polyester that is used to form the polyesterurethane is from the group of butane diol, hexane diol, cyclohexane dimethanol, ethylene glycol or mixtures of any of the above.
Claim 8
Dependent Claim
50 words
The process of claim 5 in which the dicarboxylic acid used to form the hydroxy functional polyester that is used to form the polyesterurethane is from the group of adipic acid, azelaic acid, sebasic acid, dodecane dicarboxylic acid, hexahydrophthalic acid or its anhydride or mixtures of any of the above.
Claim 9
Dependent Claim
38 words
The process of claim 5 in which the hydroxy containing carboxylic acid used to form the polyesterurethane is from the group of dihydroxy succinic acid, dihydroxy benzoic acid, dimethylol propionic acid, dihydroxy propionic acid and any mixtures thereof.
Claim 10
Dependent Claim
49 words
The process of claim 5 in which the organic polyisocyanate used to form the hydroxy functional polyester that is used to form the polyesterurethane comprises an aliphatic, cycloaliphatic or aromatic diisocyanate and up to 10 percent by weight, based on the weight of the polyesterurethane, of an organic triisocyanate.
Claim 11
Dependent Claim
47 words
The process of claim 9 in which the organic polyisocyanate is from the group of hexamethylene diisocyanate, isophorone diisocyanate, biphenylene diisocyanate, toluene diisocyanate, bis cyclohexyl diisocyanate, tetramethyl xylene diisocyanate, ethylethylene diisocyanate, dimethylethylene diisocyanate, methyltrimethylene diisocyanate, cyclopentylene diisocyanate, cyclohexylene diisocyanate, phenylene diisocyanate, naphthalene diisocyanate, bis-(isocyanatocyclohexyl)-methane and diisocyanatodiphenyl ether.
Claim 12
Dependent Claim
30 words
The process of claim 9 in which the organic polyisocyanate comprises a blend of about 9-15% by weight of an organic diisocyanate and 5-10% by weight of an organic triisocyanate.
Claim 13
Dependent Claim
38 words
The process of claim 11 in which the organic triisocyanate is from the group of triphenylmethane triisocyanate, benzene triisocyanate, toluene triisocyanate, an adduct of trimethylol propane and tetramethyl xylene diisocyanate, the trimer of hexamethylene diisocyanate and mixtures thereof.
Claim 14
Dependent Claim
23 words
The process of claim 11 in which the organic diisocyanate is isophorone diisocyanate and the organic triisocyanate is the trimer of hexamethylene diisocyanate.
Claim 15
Dependent Claim
38 words
The process of claim 5 in which the hydroxy functional carboxylic acid used to form the polyesterurethane is from the group of dihydroxy succinic acid, dihydroxy benzoic acid, dimethylol propionic acid, dihydroxy benzoic acid and any mixtures thereof.
Claim 16
Dependent Claim
25 words
The process of claim 3 in which the multifunctional crosslinking agent is an epoxy compound which comprises a multifunctional aliphatic, cycloaliphatic or aromatic epoxy compound.
Claim 17
Dependent Claim
44 words
The process of claim 14 in which the epoxy compound is from the group of sorbitol based diepoxide, cyclohexyl based diepoxide, sebasic acid diglycidyl ester, adipic acid diglycidyl ester, ethylene glycol diglycidyl ether, hexanediol diglycidyl ether, hexahydrophthalic anhydride diglycidyl ester and any mixtures thereof.
Claim 18
Dependent Claim
31 words
The process of claim 15 in which the epoxy compound comprises a blend of 0.5-3% by weight of a difunctional epoxy compound and 4-10% by weight of a trifunctional epoxy compound.
Claim 19
Dependent Claim
29 words
The process of claim 17 in which the trifunctional epoxy compound is from the group of trishydroxyethyl isocyanurate triglycidylether, pentaerythritol glycidyl ether, triglycidyl tris (2-hydroxyethyl)isocyanurate and any mixtures thereof.
Claim 20
Dependent Claim
48 words
The process of claim 5 in which the polyesterurethane is the reaction product of a hydroxy functional polyester of cyclohexane dimethanol, hexahydrophthalic anhydride, dodecanedioic acid and adipic acid and dimethylol propionic acid and isophorone diisocyanate and trimer of hexamethylene diisocyanate and the epoxy compound is cyclohexyl based diepoxide.
Claim 21
Dependent Claim
58 words
The process of claim 5 in which the polyesterurethane is the reaction product of a hydroxy functional polyester of cyclohexane dimethanol, hexahydrophthalic anhydride, dodecanedioic acid and adipic acid and dimethylol propionic acid and isophorone diisocyanate and trimer of hexamethylene diisocyanate and the epoxy compound is a trifunctional epoxide of an adduct of trimer of hexamethylene diisocyanate and glycidol.
Claim 22
Dependent Claim
25 words
The process of claim 3 in which the multifunctional crosslinking agent is a multifunctional organic polyisocyanate which comprises a multifunctional aliphatic, cycloaliphatic or aromatic polyisocyanate.
Claim 23
Dependent Claim
32 words
The process of claim 21 in which the multifunctional polyisocyanate is from the group of trimer of hexamethylene diisocyanate, triphenylmethane triisocyanate, benzene triisocyanate, toluene triisocyanate, adduct of trimethylol propane and tetramethylxylene diisocyanate.
Claim 24
Dependent Claim
16 words
The process of claim 21 in which the polyisocyanate is blocked with an organic blocking agent.
Claim 25
Dependent Claim
52 words
The process of claim 5 in which the polyesterurethane is the reaction product of a hydroxy functional polyester of cyclohexane dimethanol, hexahydrophthalic anhydride, dodecanedioic acid and adipic acid and dimethylol propionic acid and isophorone diisocyanate and trimer of hexamethylene diisocyanate and the organic polyisocyanate crosslinking agent is a trimer of hexamethylene diisocyanate.
Claim 26
Dependent Claim
16 words
The process of claim 1 in which the flexible polymeric sheet is a thin polyester film.
Claim 27
Dependent Claim
45 words
The process of claim 1 in which a clear layer of the coating composition of claim 1 is applied to the flexible carrier and at least partially dried and then a pigmented layer of a coating composition is applied to the clear layer and dried.
Claim 28
Dependent Claim
24 words
The process of claim 26 in which the coating composition of the pigmented layer comprises binder of a fluorocarbon polymer and an acrylic polymer.
Claim 29
Dependent Claim
19 words
The process of claim 27 in which the binder of the pigmented layer comprises polyvinylidene fluoride and polyalkyl methacrylate.
Claim 30
Dependent Claim
39 words
The process of claim 26 in which the clear layer and pigmented layer form the exterior surface of the composite and have gloss of at least 80 measured at 20° and a distinctness of image of at least 80.
Claim 31
Dependent Claim
43 words
The process of claim 26 in which the coating composition of the clear layer contains additives of components selected from the group consisting of ultraviolet light screeners, ultraviolet light stabilizers, microgel, flow control agent and mixtures of any or all of the above.
Claim 32
Dependent Claim
66 words
The process of claim 26 in which the coating composition of the pigmented layer contains components selected from the group consisting of ultraviolet light screeners, ultraviolet light stabilizers, microgel, flow control agent and mixtures of any or all of the above and contains pigment in pigment to binder ratio of about 1:100 to 200:100 wherein the binder comprises the film forming constituents of the coating composition.
Claim 33
Dependent Claim
51 words
The process of claim 26 in which at least one thin size layer is applied to the pigmented layer and is dried; wherein the size layer is selected from the group consisting of polyalkyl acrylates, polyalkyl methacrylates, iminated polyalkyl acrylates or methacrylates, vinyl chloride polymers, polyurethanes, polyimides, and any mixtures thereof.
Claim 34
Dependent Claim
31 words
The process of claim 1 in which the flexible thermoformable polymeric material comprises a polymer selected from the group consisting of thermoplastic polyolefins, acrylonitrile-butadiene-styrene terpolymers, polystyrene and styrene-acrylonitrile copolymers mixtures thereof.
Claim 35
Dependent Claim
28 words
The process of claim 33 in which the flexible thermoformable polymeric material comprises of polyolefin of polypropylene or polyethylene having a melt flow of about 0.5-2.0 g/10 min.
Claim 36
Dependent Claim
30 words
The process of claim 33 in which the flexible layer of thermoformable polyolefin comprises an extruded sheet of a compounded mixture of polypropylene, a synthetic elastomeric resin, pigments and additives.
Claim 37
Dependent Claim
18 words
The process of claim 33 in which the flexible thermoformable polymer material comprises a sheet of acrylonitrile-butadiene-styrene polymer.
Claim 38
Dependent Claim
54 words
The process of claim 1 in which the rigid synthetic resinous substrate comprises a thermoformable polymeric material having a flexural modulus of about 175-2100 MPa and a melt flow rate of about 0.5-8.0 g/10 min. and is selected from the group consisting of thermoplastic polyolefin, acrylonitrile-butadiene-styrene polymer, polystyrene and styrene-acrylonitrile copolymers and mixtures thereof.
Claim 39
Dependent Claim
29 words
The process of claim 37 in which the thermoformable polymeric material of the rigid synthetic resinous substrate is injection molded in contact with the laminate to form the composite.
Claim 40
Dependent Claim
19 words
The process of claim 38 in which the rigid synthetic resinous substrate comprises thermoformable polyolefin of polyethylene or polypropylene.
Claim 41
Dependent Claim
14 words
The process of claim 38 in which the rigid synthetic substrate comprises acrylonitrile-butadiene-styrene polymer.
Claim 42
Dependent Claim
84 words
The process of claim 26 that forms a composite useful as an exterior vehicle part comprising the following layers of components: a. 10-125 micron thick layer of a glossy clear thermoplastic finish of a coating composition bonded firmly to b. 5-75 micron thick layer of a thermoplastic pigment containing layer of the coating composition of claim 1 bonded to c. 125-1250 micron thick layer of a flexible thermoformable material that is bonded to d. 500-25,000 micron thick layer of a rigid synthetic resinous material.
Claim 43
Dependent Claim
236 words
A process for forming a laminate useful for making an exterior vehicle body part comprising the following steps: a. applying a layer of a coating composition to a flexible polymeric carrier sheet having a smooth glossy surface and drying said layer; b. laminating with heat and pressure the flexible polymeric carrier sheet with the coating layer to a flexible thermoformable polymeric material with the coating layer of the sheet being adhered to the thermoformable polymeric material to form a laminate; wherein the coating composition used in the process comprises about 10-70% by weight binder solids and correspondingly about 90-30% by weight organic liquid carrier, wherein the binder consists essentially of (1) a carboxyl functional polyesterurethane having a weight average molecular weight of about 80,000 to 200,000 and is reaction product of a hydroxy functional polyester, a hydroxy containing carboxylic acid and an organic polyisocyanate, wherein the hydroxy functional polyester is the reaction product of a diol of the formula HOROH and dicarboxylic acid of the formula R 1 (COOH) 2 or an anhydride of such an acid where R is an aliphatic, cycloaliphatic or aromatic hydrocarbon radical having 2-6 carbon and R 1 is an aliphatic, cycloaliphatic or aromatic hydrocarbon radical having 6-12 carbon atoms and (2) multifunctional crosslinking agent selected from the group consisting of a multifunctional aliphatic, cycloaliphatic or aromatic epoxy compound or a multifunctional organic polyisocyanate having at least three reactive isocyanate groups.
Claim 44
Dependent Claim
236 words
A process for forming a laminate useful for making an exterior vehicle body part comprising the following steps: a. applying a layer of a coating composition to a flexible polymeric carrier sheet having a smooth glossy surface and drying said layer; b. laminating with heat and pressure the flexible polymeric carrier sheet with the coating layer to a flexible thermoformable polymeric material with the coating layer of the sheet being adhered to the thermoformable polymeric material to form a laminate; wherein the coating composition used in the process comprises about 10-70% by weight binder solids and correspondingly about 90-30% by weight organic liquid carrier, wherein the binder consists essentially of (1) a carboxyl functional polyesterurethane having a weight average molecular weight of about 80,000 to 200,000 and is reaction product of a hydroxy functional polyester, a hydroxy containing carboxylic acid and an organic polyisocyanate, wherein the hydroxy functional polyester is the reaction product of a diol of the formula HOROH and dicarboxylic acid of the formula R 1 (COOH) 2 or an anhydride of such an acid where R is an aliphatic, cycloaliphatic or aromatic hydrocarbon radical having 2-6 carbon and R 1 is an aliphatic, cycloaliphatic or aromatic hydrocarbon radical having 6-12 carbon atoms and (2) multifunctional crosslinking agent selected from the group consisting of a multifunctional aliphatic, cycloaliphatic or aromatic epoxy compound or a multifunctional organic polyisocyanate having at least three reactive isocyanate groups.
Claim 45
Dependent Claim
56 words
The process of claim 42 in which the laminate comprising the following layers of components: a. 10-125 micron thick layer of a glossy clear thermoplastic finish bonded firmly to b. 5-75 micron thick layer of a thermoplastic pigment containing layer of the coating composition bonded to c. 125-1250 micron thick layer of a flexible thermoformable material.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-03-18 | 1994-09-17 | 1995-03-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-03-18 | 1998-09-17 | 1999-03-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-03-18 | 2002-09-17 | 2003-03-19 | $7700.00 | Window Closed / Lapsed |