US4998709A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making graphite electrode nipple
Assignee: ConocoPhillips Co
•
Filing: 1990-04-19
•
Granted: 1991-03-12
•
Expires: 2010-04-19
Abstract
Abstract The present invention resides in improved graphite nipples which are suitable for connecting graphite electrodes. The graphite nipples are prepared by adding mesophase pitch-based carbon fibers into a typical nipple extrusion blend.
Inventors
- 👤 Robert R. Griffin
- 👤 Keith M. Roussel
- 👤 Ta-Wei Fu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 07:12
CPC Classifications
H; H05; H05B; H05B3/00; H05B3/10; H05B3/12; H05B3/14; C; C04; C04B; C04B35/00; C04B35/515; C04B35/52; C04B35/71; C04B35/78; C04B35/80; C04B35/83; H05B7/00; H05B7/02; H05B7/06; H05B7/08; H05B7/085; Y; Y10; Y10S; Y10S403/00; Y10S403/05; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T428/00; Y10T428/30
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
139 words
A process for producing graphite nipples suitable for connecting graphite electrodes which comprises the steps of: (a) adding from about 8 weight percent to about 20 weight percent of carbon fibers produced from spun mesophase pitch to from about 45 weight percent to about 65 weight percent of premium coke and from about 22 weight percent to about 28 weight percent of a binder to form an extrusion blend, (b) extruding the extrusion blend to form an elongated carbon nipple, (c) subjecting the carbon nipple to a temperature of from about 760° C. to about 982° C. for from about 2 weeks to about 5 weeks to produce a baked carbon nipple; and (d) subjecting the baked carbon nipple to a temperature above about 2,704° C. from about 5 days to about 14 days to produce a graphite nipple.
Claim 2
Dependent Claim
139 words
A process for producing graphite nipples suitable for connecting graphite electrodes which comprises the steps of: (a) adding from about 8 weight percent to about 20 weight percent of carbon fibers produced from spun mesophase pitch to from about 45 weight percent to about 65 weight percent of premium coke and from about 22 weight percent to about 28 weight percent of a binder to form an extrusion blend, (b) extruding the extrusion blend to form an elongated carbon nipple, (c) subjecting the carbon nipple to a temperature of from about 760° C. to about 982° C. for from about 2 weeks to about 5 weeks to produce a baked carbon nipple; and (d) subjecting the baked carbon nipple to a temperature above about 2,704° C. from about 5 days to about 14 days to produce a graphite nipple.
Claim 3
Dependent Claim
22 words
The process according to claim 1 wherein the mesophase pitch used to produce carbon fibers has a melting point below 350° C.
Claim 4
Dependent Claim
25 words
The process according to claim 1 including adding from about 0.01 weight percent to about 2.5 weight percent of iron oxide to the extrusion blend.
Claim 5
Dependent Claim
22 words
The process of claim 1, including adding from about 0.01 to about 4 weight percent of a lubricant to the extrusion blend.
Claim 6
Dependent Claim
30 words
The process according to claim 1, wherein the graphitized carbon fibers of the graphite nipples have a tensile strength of from about 200×10 3 psi to about 300×10 3 psi.
Claim 7
Dependent Claim
32 words
The process according to claim 1, wherein the graphitized carbon fibers of the graphite nipple have a Youngs modulus of elasticity of from about 55×10 6 psi to about 120×10 6 psi.
References Cited (Backward Citations)
US3550270A
Cited
US3790393A
Cited
US3671385A
Cited
US3936535A
Cited
US3914395A
Cited
GB1548046A
Cited
SU874619A1
Cited
DE3124364A1
Cited
JPS60191057A
Cited
US4594722A
Cited
USH420H
Cited
US4814307A
Cited
US4777093A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-03-11 | 1994-09-10 | 1995-03-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-03-11 | 1998-09-10 | 1999-03-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-03-11 | 2002-09-10 | 2003-03-12 | $7700.00 | Window Closed / Lapsed |