Polyester composition which is particularly suitable for use in thermoforming thin walled articles
Assignee: Corpus Christi Polymers LLC
•
Filing: 1987-03-13
•
Granted: 1991-02-26
•
Expires: 2007-03-13
Abstract
Abstract This invention relates to a thermoplastic resin composition which is particularly suitable for use in thermoforming thin walled articles. The thermoplastic resin compositions are comprised of (1) from about 94 to about 99 weight percent polyethylene naphthalate and (2) from about 1 to 6 weight percent of at least one polyester elastomer. The subject invention also deals with thermoforming such thermoplastic resin compositions into articles, such as food trays, having a crystallinity within the range of about 10% to about 40%.
Inventors
- 👤 Donald E. Richeson
- 👤 Judith A. Tweedie
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 17:28
CPC Classifications
C; C08; C08L; C08L33/00; C08L33/04; C08L67/00; C08L67/02
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
45 words
A thermoformed, non-oriented, heat-set, thin walled article which consists of (1) from about 94 to about 99 weight percent polyethylene naphthalate, (2) from about 1 to about 6 weight percent of at least one polyester elastomer, and (3) an effective amount of a heat stabilizer.
Claim 2
Dependent Claim
45 words
A thermoformed, non-oriented, heat-set, thin walled article which consists of (1) from about 94 to about 99 weight percent polyethylene naphthalate, (2) from about 1 to about 6 weight percent of at least one polyester elastomer, and (3) an effective amount of a heat stabilizer.
Claim 3
Dependent Claim
89 words
A process for making a heat set, partially crystalline, thin walled article which comprises: thermoforming a substantially amorphous sheet which consists of the thermoplastic resin composition specified in claim 1, wherein said thermoforming is carried out in a heated mold for a time sufficient to achieve a crystallinity in said article which is within the range of about 10% to about 40%, wherein said polyester elastomer is comprised of polyester segments and polyether segments and wherein said thermoplastic resin composition has an intrinsic viscosity of at least 0.8 dl/g.
Claim 4
Dependent Claim
70 words
A process as specified in claim 2 wherein said amorphous sheet is preheated to a temperature which is within the range of 140° C., to 220° C., wherein a mold temperature within the range of about 160° C. to about 225° C. is utilized and wherein said thermoplastic resin composition is comprised of from 96 to 98 weight percent polyethylene naphthalate and from 2 to 4 weight percent polyester elastomer.
Claim 5
Dependent Claim
37 words
A process as specified in claim 3 wherein said thermoforming is carried out for a time sufficient to achieve a crystallinity in said article which is within the range of about 20 percent to about 30 percent.
Claim 6
Dependent Claim
52 words
A thermoformed, non-oriented, heat-set, thin walled article which consists of (1) from about 94 to about 99 weight percent polyethylene naphthalate, (2) from about 1 to about 6 weight percent of at least one polyester elastomer, (3) an effective amount of a heat stabilizer, and (4) at least one non-nucleating organic colorant.
Claim 7
Dependent Claim
52 words
A thermoformed, non-oriented, heat-set, thin walled article which consists of (1) from about 94 to about 99 weight percent polyethylene naphthalate, (2) from about 1 to about 6 weight percent of at least one polyester elastomer, (3) an effective amount of a heat stabilizer, and (4) at least one non-nucleating organic colorant.
Claim 8
Dependent Claim
62 words
A process for making a heat set, partially crystalline, thin walled article which comprises: thermoforming a substantially amorphous sheet which consists of the thermoplastic resin composition specified in claim 5, wherein said thermoforming is carried out in a heated mold for a time sufficient to achieve a crystallinity in said article which is within the range of about 10% to about 40%.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-02-25 | 1994-08-27 | 1995-02-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-02-25 | 1998-08-27 | 1999-02-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-02-25 | 2002-08-27 | 2003-02-26 | $7700.00 | Window Closed / Lapsed |