Skin-surfaced foam glass tile and method for production thereof
Assignee: Inax Corp
•
Filing: 1988-08-23
•
Granted: 1991-02-05
•
Expires: 2008-08-23
Abstract
Abstract A method for producing a foam glass tile having a surface skin comprises the steps of molding a material consisting essentially of a vitrifiable mineral and a foaming agent into a tile-like block; coating the block with a thin layer comprising a vitrifying agent for the mineral material; heating the coated block to a temperature sufficient to fuse the coated layer whereby the molten vitrifying agent permeates into the coated surface of the block; and further heating the coated block to a temperature sufficient to soften the vitrifiable mineral. The method may further include the step of forming a thin layer comprising a vitrifiable mineral and a lesser amount of a foaming agent between the tile-like block and the vitrifying agent layer, followed by firing. The foam glass tile formed by the above method comprises a foam glass tile body and a rigid reinforcing vitrified surface skin, the surface skin being integrally melt-bonded onto at least a top surface of the foam glass body. Such foam glass tiles have a closed cell structure and are thermally insulating.
Inventors
- 👤 Katsuhisa Fukumoto
- 👤 Kiyotaka Kawanishi
- 👤 Ryo Nakada
- 👤 Junpei Yamano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 08:25
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/02; C03C11/00; C03C11/007; E; E04; E04F; E04F13/00; E04F13/07; E04F13/08; E04F13/14; E04F13/145; E04F15/00; E04F15/02; E04F15/08; Y; Y10; Y10T; Y10T428/00; Y10T428/16; Y10T428/163; Y10T428/164; Y10T428/166; Y10T428/249921; Y10T428/249953; Y10T428/249961; Y10T428/249967; Y10T428/249969; Y10T428/24997; Y10T428/249976; Y10T428/249981; Y10T428/249987; Y10T428/249988; Y10T428/24999
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
184 words
A method for producing a thermally insulating foam glass tile having a surface skin comprising the steps of: molding a mixture consisting essentially of a first vitrifiable mineral and an effective amount of a first foaming agent into a tile-like block, forming a coated block by coating at least a top surface of said tile-like block with a layer of a vitrifying agent for said vitrifiable mineral, heating said coated block to a first temperature to melt said vitrifying agent, thereby permeating substantially all of said molten vitrifying agent into at least said top surface of said coated block to form a softened secondary layer consisting of said vitrifying agent and said vitrifiable mineral, heating said coated block to a second temperature to soften said vitrifiable mineral and decompose said foaming agent to form a foamed tile-like block, and cooling said foamed tile-like block, whereby the permeated molten vitrifying agent is integrally melt-bonded to at least said top surface of said coated block to form a rigid reinforcing skin layer consisting essentially of a vitrified mixture of said vitrifying agent and said vitrifiable mineral.
Claim 2
Independent Claim
184 words
A method for producing a thermally insulating foam glass tile having a surface skin comprising the steps of: molding a mixture consisting essentially of a first vitrifiable mineral and an effective amount of a first foaming agent into a tile-like block, forming a coated block by coating at least a top surface of said tile-like block with a layer of a vitrifying agent for said vitrifiable mineral, heating said coated block to a first temperature to melt said vitrifying agent, thereby permeating substantially all of said molten vitrifying agent into at least said top surface of said coated block to form a softened secondary layer consisting of said vitrifying agent and said vitrifiable mineral, heating said coated block to a second temperature to soften said vitrifiable mineral and decompose said foaming agent to form a foamed tile-like block, and cooling said foamed tile-like block, whereby the permeated molten vitrifying agent is integrally melt-bonded to at least said top surface of said coated block to form a rigid reinforcing skin layer consisting essentially of a vitrified mixture of said vitrifying agent and said vitrifiable mineral.
Claim 3
Dependent Claim
45 words
The method as claimed in claim 1, wherein said step of forming a coated block comprises coating between about 3 mg/cm 2 and about 50 mg/cm 2 of said vitrifying agent on a dry basis to at least said top surface of said tile-like block.
Claim 4
Dependent Claim
59 words
The method as claimed in claim 1, further including the step of forming an intermediate layer on at least said top surface of said tile-like block, said intermediate layer having a thickness of up to about 3 mm and consisting essentially of a second vitrifiable mineral and a second foaming agent in a quantity less than said effective amount.
Claim 5
Dependent Claim
41 words
The method as claimed in claim 1 wherein said mixture includes densified particles consisting essentially of said first vitrifiable mineral and said first foaming agent, said densified particles having a mean particle size between about 0.05 mm and about 0.50 mm.
Claim 6
Dependent Claim
41 words
The method as claimed in claim 3, wherein said mixture includes densified particles consisting essentially of said first vitrifiable mineral and said first foaming agent, said densified particles having a mean particle size between about 0.05 mm and about 0.50 mm.
Claim 7
Dependent Claim
57 words
The method as claimed in claim 1, wherein said steps of heating said coated block to said first and second temperatures comprise heating said coated block on a firing stand in a kiln and inserting slidable refractory granules having a diameter between about 0.50 mm and about 5.0 mm between said coated block and said firing stand.
Claim 8
Dependent Claim
56 words
The method as claimed in claim 3, wherein said steps of heating said coated block to said first and second temperatures comprise heating said coated block on a firing stand in a kiln and inserting slidable refractory granules having a diameter between about 0.50 mm and about 5.0 mm between said coated block and firing stand.
Claim 9
Dependent Claim
16 words
The method as claimed in claim 1, wherein said vitrifying agent comprises a borosilicate glass powder.
Claim 10
Dependent Claim
16 words
The method as claimed in claim 3, wherein said vitrifying agent comprises a borosilicate glass powder.
Claim 11
Dependent Claim
20 words
A thermally insulating foam glass tile having a surface skin which is produced according to the method of claim 1.
Claim 12
Dependent Claim
20 words
A thermally insulating foam glass tile having a surface skin which is produced according to the method of claim 3.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-02-04 | 1994-08-06 | 1995-02-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-02-04 | 1998-08-06 | 1999-02-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-02-04 | 2002-08-06 | 2003-02-05 | $7700.00 | Window Closed / Lapsed |