Abstract
Abstract There are described solvent-free, low monomer or monomer-free polymerizable melt compositions suitable for the corrosion and abrasion resistant coatings of substrates and formed bodies of metal, plastic, cellulose materials and/or inorganic materials and/or the creation of a protective film with barrier properties and methods of making them. The melt compositions are particularly useful especially for use in packaging, and comprise: (a) at least one polymerizable, hydroxyl-containing polymer having an average molecular weight (Mw) of between 1,000 and 500,000 and a glass transition temperature (Tg) of ≧+20° C., and/or (b) at least one polymerizable, linear unbranched and/or branched polyester and/or its copolymer having an average molecular weight (Mw) of between 800 and 50,000 and a glass transition temperature (Tg) of ≧-50° C., and/or (c) a polymerizable oligomer carrying an ethylenically unsaturated group, of the following group consisting of acrylic, methacrylic, ether, ester, urethane, amide, imide, epoxide, siloxane, phenol, novolak and/or mercapto compounds having an average molecular weight (Mw) of between 400 and 10,000, and (d) if required, conventional additives. Further described are processes for preparing these melt compositions and methods of further processing these melt compositions and finishing planar substrates and/or shaped bodies with these melt compositions. Moreover, the present invention relates to a process for polymerization or curing of the melt composition.
Inventors
- 👤 Georg Bolte
- 👤 Rudolf Hinterwaldner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 19:02
CPC Classifications
C; C09; C09D; C09D157/00; C09D157/06; C09D157/10; C08; C08F; C08F290/00; C08F290/08; C08F299/00; C08F299/02; C08F299/04; C09D167/00
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
215 words
A method of coating a substrate to provide a protective coating or film thereon, said method comprising the steps of: (a) providing a solvent-free, low monomer or monomer-free, polymerizable hot melt comprised of a polymerizable component selected from the group consisting of (1) at least one polymerizable, hydroxyl-containing polymer containing <0.01 wt. % residual free monomers and having a mean molecular weight (M w ) of between about 1,000 and about 500,000 and a glass transition temperature (T g )≧-20° C. to +181° C.; (2) at least one polymerizable, linear straight chain and/or branched polyester and/or copolymer thereof containing ≦0.1 wt. % residual free monomers and having a mean molecular weight (M w ) between about 800 and about 50,000 and a glass transition temperature (T g )≧-50° C. to +50° C.; (3) components (1) and (2) in admixture; and (4) components (1) and/or (2) in admixture with a polymerizable, ethylenically-unsaturated group carrying oligomer consisting of acrylic, methacrylic, ether, ester, urethane, amide, imide, epoxy, siloxane, phenol, novolak and/or mercapto compounds containing ≦0.5 wt. % residual free monomers and having a mean molecular weight (M w ) of about 400 to about 10,000; (b) applying said hot melt to a substrate in the form of a coating or thin film, and (c) polymerizing said hot melt.
Claim 2
Independent Claim
215 words
A method of coating a substrate to provide a protective coating or film thereon, said method comprising the steps of: (a) providing a solvent-free, low monomer or monomer-free, polymerizable hot melt comprised of a polymerizable component selected from the group consisting of (1) at least one polymerizable, hydroxyl-containing polymer containing <0.01 wt. % residual free monomers and having a mean molecular weight (M w ) of between about 1,000 and about 500,000 and a glass transition temperature (T g )≧-20° C. to +181° C.; (2) at least one polymerizable, linear straight chain and/or branched polyester and/or copolymer thereof containing ≦0.1 wt. % residual free monomers and having a mean molecular weight (M w ) between about 800 and about 50,000 and a glass transition temperature (T g )≧-50° C. to +50° C.; (3) components (1) and (2) in admixture; and (4) components (1) and/or (2) in admixture with a polymerizable, ethylenically-unsaturated group carrying oligomer consisting of acrylic, methacrylic, ether, ester, urethane, amide, imide, epoxy, siloxane, phenol, novolak and/or mercapto compounds containing ≦0.5 wt. % residual free monomers and having a mean molecular weight (M w ) of about 400 to about 10,000; (b) applying said hot melt to a substrate in the form of a coating or thin film, and (c) polymerizing said hot melt.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein said substrate is preheated to at least +50° C. prior to application of said hot melt thereto.
Claim 4
Dependent Claim
28 words
The method of claim 2 wherein said substrate is a plastic material and said material is preheated to a temperature 10° C. below the softening point of same.
Claim 5
Dependent Claim
27 words
The method of claim 2 wherein said substrate is a cellulosic or inorganic material and said material is preheated to a temperature of at least +100° C.
Claim 6
Dependent Claim
31 words
The method of claim 1 wherein any free radicals present are cured by means of a peroxide or hydroperoxide initiator in the presence of heat or with ultraviolet or electron beams.
Claim 7
Dependent Claim
15 words
The method of claim 1 wherein said polymerization occurs by means of an electron beam.
Claim 8
Dependent Claim
20 words
The method of claim 1, wherein at least one of said polymerizable compounds is at least a partially crystalline compound.
Claim 9
Dependent Claim
14 words
The method of claim 1, wherein said hydroxyl-containing polymer (1) is a cellulose derivative.
Claim 10
Dependent Claim
51 words
The method of claim 8, wherein said hydroxyl-containing polymer (1) is cellulose ester, cellulose ether or a mixture thereof containing at least about 0.1% by weight of reactive acrylic groups, methacrylic groups or a mixture thereof and having a mean molecular weight (M w ) between about 10,000 and about 250,000.
Claim 11
Dependent Claim
55 words
The method of claim 1, wherein said hydroxyl-containing polymer (1) is a polyvinyl alcohol derivative containing ≧0.1% by weight of reactive acrylic groups, methacrylic groups or a mixture thereof and having a mean molecular weight (M w ) between about 10 and about 100,000 and a glass transition temperature (T g ) of ≧-20° C.
Claim 12
Dependent Claim
55 words
The method of claim 1, wherein said hydroxyl-containing polymer (1) is a phenol or novolak derivative containing ≧0.1% by weight of reactive acrylic groups, methacrylic groups, or mixture thereof and having a mean molecular weight (M w ) between about 1,000 and about 50,000 and a glass transition temperature (T g ) of ≧-20° C.
Claim 13
Dependent Claim
86 words
The method of claim 1, wherein the polymer (2) is a linear, straight-chain polyester or copolyester, or a mixture thereof, or a branched polyester or copolyester or a mixture thereof, or a mixture of (a) said straight chain polyester or copolyester or mixtures thereof and (b) said branched polyester or copolyester or mixture thereof, said polymer (2) containing ≧0.1% by weight of reactive acrylic groups, methacrylic groups, or a mixture thereof and having a mean molecular weight (M w ) between about 1,000 and about 20,000.
Claim 14
Dependent Claim
16 words
The method of claim 12, wherein the mean molecular weight is between about 1,000 and 10,000.
Claim 15
Dependent Claim
87 words
The method of claim 1, wherein said polymer (2) is a hydroxyl containing basic polyester selected from (a) a hydroxyl polyester having branched chains of polyester units with branches at three or more polyester forming functions, (b) a hydroxyl polyester with alkyl side chains linked through ester or ether groups of three or more polyester forming functions, and containing ≧0.1% by weight of reactive acrylic groups, methacrylic groups, or a mixture thereof and having a mean molecular weight (M w ) of about 1,000 to about 20,000.
Claim 16
Dependent Claim
36 words
The method of claim 1, further including the step of prepolymerizing the hot melt after application to said substrate to a degree sufficient for further processing, forming the substrate and subsequently completely curing the hot melt.
Claim 17
Dependent Claim
15 words
The method of claim 15, wherein the method is carried out in an inert medium.
Claim 18
Dependent Claim
17 words
The method of claim 16, wherein the inert medium is nitrogen, carbon dioxide or a noble gas.
Claim 19
Dependent Claim
11 words
The method of claim 17, wherein the inert medium is preheated.
Claim 20
Dependent Claim
66 words
The method of claim 1, wherein said polymerizable hot melt is polymerized or cured by spraying water on said coating of said hot melt, cooling said coated substrate by providing an atmosphere of high humidity about said substrate to result in the condensation of water on the surface of said substrate, and removing said condensed water from said surface upon polymerization or curing of said coating.
References Cited (Backward Citations)
DE1917788A1
Cited
US3928265A
Cited
DE2436186A1
Cited
US4175977A
Cited
DE2914982A1
Cited
EP0154924A2
Cited
EP0184349A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-02-04 | 1994-08-06 | 1995-02-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-02-04 | 1998-08-06 | 1999-02-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-02-04 | 2002-08-06 | 2003-02-05 | $7700.00 | Window Closed / Lapsed |