Support sheet for photographic printing sheet
Assignee: New Oji Paper Co Ltd
•
Filing: 1989-11-08
•
Granted: 1991-01-29
•
Expires: 2009-11-08
Abstract
Abstract A support sheet for photographic printing paper comprising a substrate sheet, polyolefin resin coating layers formed on the two surfaces of the substrate sheet, and an adhesive layer formed on a surface of the substrate sheet and one of the coating layers and comprising hydroxyethyl cellulose or a mixture of hydroxyethyl cellulose with one or more organic compounds having carboxyl radicals, the adhesive layer enabling the peel strength of the coating layer from the substrate sheet surface to be controlled to an appropriate peelable level of 10 to 200 g/25.4 mm determined in accordance with ASTM D903-49.
Inventors
- 👤 Hiroyuki Nemoto
- 👤 Masahiro Kamiya
- 👤 Tsunehisa Shigetani
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 20:30
CPC Classifications
G; G03; G03C; G03C1/00; G03C1/76; G03C1/805; G03C1/775; G03C1/79; Y; Y10; Y10T; Y10T428/00; Y10T428/27; Y10T428/273; Y10T428/277; Y10T428/31504; Y10T428/31855; Y10T428/3188; Y10T428/31884; Y10T428/31895; Y10T428/31899; Y10T428/31902
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
118 words
A support sheet for photographic printing paper comprising: a substrate sheet comprising a paper sheet; coating layers formed on the two principal surfaces of the substrate sheet comprising a polyolefin resin; and an adhesive layer, disposed between a surface of the substrate sheet and one of the coating layers formed on the surface of the substrate sheet, comprising a member of selected from the group consisting of hydroxyethyl cellulose and mixtures of hydroxyethyl cellulose and at least one organic compound having carboxyl groups, said adhesive layer enabling the peel strength between the substrate sheet surface and the coating layer to be controlled to a peel strength of 10 to 200 g/25.4 mm determined in accordance with ASTM D903-49.
Claim 2
Dependent Claim
118 words
A support sheet for photographic printing paper comprising: a substrate sheet comprising a paper sheet; coating layers formed on the two principal surfaces of the substrate sheet comprising a polyolefin resin; and an adhesive layer, disposed between a surface of the substrate sheet and one of the coating layers formed on the surface of the substrate sheet, comprising a member of selected from the group consisting of hydroxyethyl cellulose and mixtures of hydroxyethyl cellulose and at least one organic compound having carboxyl groups, said adhesive layer enabling the peel strength between the substrate sheet surface and the coating layer to be controlled to a peel strength of 10 to 200 g/25.4 mm determined in accordance with ASTM D903-49.
Claim 3
Dependent Claim
47 words
The support sheet as claimed in claim 1, wherein the hydroxyethyl cellulose in the adhesive layer has a degree of substitution of the hydroxyethyl groups of 1.0 to 1.5 on each glucose unit and an average gram molecule of the substituted hydroxyethyl groups of 1.5 to 2.5.
Claim 4
Dependent Claim
24 words
The support sheet as claimed in claim 1, wherein the hydroxyethyl cellulose in the adhesive layer has a molecular weight of 30,000 to 250,000.
Claim 5
Dependent Claim
36 words
The support sheet as claimed in claim 1, wherein the adhesive layer contains 95% by weight or more of hydroxyethyl cellulose or the mixture of hydroxyethyl cellulose and at least one organic compound having carboxyl groups.
Claim 6
Dependent Claim
34 words
The support sheet as claimed in claim 1, wherein the carboxyl groups-having organic compound is selected from carboxy-modified polyvinyl alcohols, carboxy-modified styrene-butadiene copolymers, carboxy-modified acrylic acid polymers, carboxy-modified acrylic ester polymers and oxidized starch.
Claim 7
Dependent Claim
31 words
The support sheet as claimed in claim 5, wherein the carboxy-modified polyvinyl alcohol contains 1 to 20 molar % of carboxyl groups and has a molecular weight of 40,000 to 130,000.
Claim 8
Dependent Claim
32 words
The support sheet as claimed in claim 1, wherein the mixing ratio in weight of hydroxyethyl cellulose to the carboxyl groups-having organic compound is in the range of from 2:8 to 8:2.
Claim 9
Dependent Claim
23 words
The support sheet as claimed in claim 1, wherein the adhesive layer is in an amount of 0.05 to 5 g/m 2 .
Claim 10
Dependent Claim
27 words
The support sheet as claimed in claim 1, wherein the substrate sheet consists of a paper sheet having a weight of 50 to 250 g/m 2 .
Claim 11
Dependent Claim
34 words
The support sheet as claimed in claim 1, wherein the polyolefin resin in the coating layer is selected from the group consisting of low density polyethylene resins, high density polyethylene resins and mixtures thereof.
Claim 12
Dependent Claim
23 words
The support sheet as claimed in claim 1, wherein the polyolefin in the coating layer has a molecular weight of 20,000 to 200,000.
Claim 13
Dependent Claim
22 words
The support sheet as claimed in claim 1, wherein the coating layer has a weight of 10 to 50 g/m 2 .
Claim 14
Dependent Claim
34 words
The support sheet as claimed in claim 1, wherein the adhesive layer is formed between a surface of the substrate sheet and the coating layer on which a photographic emulsion layer will be formed.
Claim 15
Dependent Claim
84 words
A support sheet for photographic paper comprising a substrate comprising a paper sheet; an adhesive layer disposed on one surface of said substrate and comprising hydroxy ethyl cellulose; and a coating layer comprising a polyolefin resin disposed on both sides of said substrate; wherein said adhesive layer has such a composition and is present in such amount that the peel strength between said substrate and the coating layer separated therefrom by said adhesive is 10 to 200 g/25.4 mm. as determined by ASTM D903-49.
Claim 16
Dependent Claim
84 words
A support sheet for photographic paper comprising a substrate comprising a paper sheet; an adhesive layer disposed on one surface of said substrate and comprising hydroxy ethyl cellulose; and a coating layer comprising a polyolefin resin disposed on both sides of said substrate; wherein said adhesive layer has such a composition and is present in such amount that the peel strength between said substrate and the coating layer separated therefrom by said adhesive is 10 to 200 g/25.4 mm. as determined by ASTM D903-49.
References Cited (Backward Citations)
JPS6134659A
Cited
US4731291A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-01-28 | 1994-07-30 | 1995-01-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-01-28 | 1998-07-30 | 1999-01-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-01-28 | 2002-07-30 | 2003-01-29 | $7700.00 | Window Closed / Lapsed |