US4988534A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Titanium carbide coating of bearing components
Assignee: General Electric Co
•
Filing: 1990-01-22
•
Granted: 1991-01-29
•
Expires: 2010-01-22
Abstract
Abstract A bearing retainer for mounting for a bearing in an x-ray tube, the x-ray tube having a rotating anode supported on an anode shaft held within a hollow anode stem, the retainer being slidably fitted into a hollow anode stem to hold one bearing coaxially with the anode shaft and to permit axial motion of the bearing so held, where the sliding surface of the bearing retainer is coated with titanium carbide, and wherein the bearing retainer includes a bearing flange not coated with titanium carbide which may be swaged around the outer race of the bearing to hold the bearing.
Inventors
- 👤 Kamleshwar Upadhya
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 12:05
CPC Classifications
F; F16; F16C; F16C25/00; F16C25/06; F16C25/08; H; H01; H01J; H01J35/00; H01J35/02; H01J35/04; H01J35/08; H01J35/10; H01J35/101; H01J35/1017; H01J35/1024; H01J2235/00; H01J2235/10; H01J2235/1046; H01J2235/1053; H01J2235/1066
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
99 words
A method of producing a lubricated bearing retainer assembly for use in an x-ray tube comprised of a bearing sleeve supporting an outer retainer substrate and a bearing fitted within the bearing sleeve, comprising the steps of: removing contaminants from the bearing substrate surfaces; heating the bearing retainer to substantially 450° C.; depositing a ceramic layer on the outer surfaces of the retainer substrate by plasma assisted physical vapor deposition under a biasing field in a low pressure environment where the biasing voltage is substantially 100 volts and the pressure is maintained between 10 -4 and 10 -2 torr.
Claim 2
Independent Claim
99 words
A method of producing a lubricated bearing retainer assembly for use in an x-ray tube comprised of a bearing sleeve supporting an outer retainer substrate and a bearing fitted within the bearing sleeve, comprising the steps of: removing contaminants from the bearing substrate surfaces; heating the bearing retainer to substantially 450° C.; depositing a ceramic layer on the outer surfaces of the retainer substrate by plasma assisted physical vapor deposition under a biasing field in a low pressure environment where the biasing voltage is substantially 100 volts and the pressure is maintained between 10 -4 and 10 -2 torr.
Claim 3
Dependent Claim
54 words
The method of claim 1 wherein the bearing sleeve includes a flange means and including the steps of: masking the flange means prior to the deposition of the ceramic layer; inserting the bearing in the bearing sleeve; and deforming the masked flange means around the bearing to hold the bearing within the bearing sleeve.
Claim 4
Independent Claim
119 words
A method of producing a lubricated bearing retainer assembly for use in an x-ray tube having a bearing sleeve supporting an outer retainer substrate and a bearing fitted within the bearing sleeve, comprising the steps of: masking the flange means prior to the deposition of the ceramic layer; depositing a ceramic layer on the outer surfaces of the retainer substrate by plasma assisted physical vapor deposition under a biasing field in a low pressure environment where the biasing voltage is substantially 100 volts and the pressure is maintained between 10 -4 and 10 -2 torr; inserting the bearing in the bearing sleeve; and deforming the masked flange means around the bearing to hold the bearing within the bearing sleeve.
Claim 5
Independent Claim
119 words
A method of producing a lubricated bearing retainer assembly for use in an x-ray tube having a bearing sleeve supporting an outer retainer substrate and a bearing fitted within the bearing sleeve, comprising the steps of: masking the flange means prior to the deposition of the ceramic layer; depositing a ceramic layer on the outer surfaces of the retainer substrate by plasma assisted physical vapor deposition under a biasing field in a low pressure environment where the biasing voltage is substantially 100 volts and the pressure is maintained between 10 -4 and 10 -2 torr; inserting the bearing in the bearing sleeve; and deforming the masked flange means around the bearing to hold the bearing within the bearing sleeve.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-01-28 | 1994-07-30 | 1995-01-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-01-28 | 1998-07-30 | 1999-01-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-01-28 | 2002-07-30 | 2003-01-29 | $7700.00 | Window Closed / Lapsed |